Arnia Putri Pratama
Konversi selulosa dari limbah sekam padi terdelignifikasi menjadi asam levulinat menggunakan katalis MnOx/ZSM-5 berpori hirarki, Mn3O4, dan MN2 = Cellulose conversion of delignified rice husk waste to levulinic acid using catalysts hierarchical MnOx/ZSM-5, Mn3O4, and Mn2
" Delignified rice husk waste has been converted to levulinic acid. There are using three types of manganese compounds as catalyst, hierarchical MnOx ZSM 5 zeolite, MnOx in this case Mn3O4, and Mn II ion. Hierarchical ZSM 5 zeolite was prepared through double template metode, then modified with Mn3O4 using impregnation metode follow by calcination at 550oC. In addition, the preparation of MnOx as Mn3O4 was carried out. Prior used, rice husk was being dewaxed and ... "
Depok: Universitas Indonesia, 2017
S68805
UI - Skripsi Membership  Universitas Indonesia Library
cover
Sitti Fachramiya Fhaza
Sintesis Mn3O4/ZSM-5 dari mineral aluminasilika alam sebagai katalis reaksi konversi α-selulosa menjadi asam levulinat = Synthesis of Mn3O4/ZSM-5 zeolite from natural aluminosilicate minerals and its application as heterogeneous catalyst for α-cellulose to levulinic acid
" Material ZSM-5 berhasil disintesis dari zeolit alam Bayat ndash; Klaten dan Kaolin Belitung sebagai sumber mineralnya dengan melakukan 2 tahap, yaitu pre-treatment terhadap zeolit alam dan kaolin terlebih dahulu dan kemudian sintesis material zeolit ZSM-5. Zeolit alam bayat sebagai sumber mineral Si/Al untuk sintesis terlebih dahulu diberi perlakuan sebagai berikut : aktivasi, purifikasi, fragmentasi dan dealuminasi, sedangkan kaolin sebagai sumber silika yang menutupi kekurangan silika pada saat sintesis diberi perlakuan : aktivasi, purifikasi dan ekstraksi ... "
Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2018