Hasil Pencarian  ::  Simpan CSV :: Kembali

"The title of this research is "Mix Design of Pervious Concrete". The research will criticizes on how to make pervious concrete as an alternative in concrete construction. Pervious Concrete can be made by concrete, asphalt, open-celled stones and gravels. These materials have to be mixed with a certain dosage in order to produce open celled structures which can be ran through by water and air. The research which was held at laboratorium, is done by doing some testing to sampels that already designed based on planned compositions. The testing covers; pressure test, bending test and porosity test to make sure that the samples can be ran through by water and air. From the compositons that already planned, this research is hoping to get shape or form variations of pervious with the information of strength from each compotitions.

---

Skripsi ini berjudul "Rancang Campur Pembuatan Pervious Concrete" membahas mengenai cara pembuatan pervious concrete sebagai salah satu alternatif konstruksi beton. Pervious concrete dapat dibuat dari beton, aspal, open-celled stones, dan kerikil dimana bahan-bahan tersebut dapat dicampur sedemikian rupa sehingga menghasilkan struktur berlubang yang dapat dilewati air dan udara. Penelitian ini dilakukan di laboratorium dengan cara melakukan pengujian terhadap benda uji yang telah didesain dengan komposisi yang direncanakan. Pengujian benda uji tersebut berupa pengujian kuat tekan, kuat lentur dan pengecekan porositas untuk memastikan keadaan benda uji dapat dilewati air dan udara. Dari variasi komposisi yang telah direncanakan diharapkan didapat bentuk pervious yang bermacam-macam dan dapat diketahui kekuatan masing-masing komposisi."

"Skripsi ini membahas mengenai perilaku pelat papan partikel cacah kotak aseptik. Tujuan penelitian ini untuk mendapatkan desain campuran papan partikel yang terbaik sesuai peraturan JIS A 5908:2003 dan SNI 03?2105?2006. Papan partikel terbuat dari bahan aseptik yang merupakan bahan yang digunakan untuk kemasan minuman kotak. Untuk perekat papan partikel digunakan phenol formaldehida. Phenol formaldehida berbentuk cair dan proses perekatannya dengan hot press sebesar 10 kg/cm2 atau 15 kg/cm2. Pada penelitian yang ditinjau adalah uji kimia, fisik, mekanik, dan beban garis. Didapat hasil campuran terbaik pada ukuran cacah kotak aseptik 50 mm x 5 mm, 10% phenol formaldehida, tebal papan 1 cm, non glassir, dan tekanan 15 kg/cm2 sedangkan dari uji beban garis didapat hasil bahwa papan partikel tidak getas dan kuat menahan tekan. Dari hasil study memperlihatkan bahwa papan partikel cacah kotak aseptik yang dibuat cocok digunakan untuk papan partisi, plafond, dan furniture.

---

This final assignment discusses about the behavior of particleboard plate made of shredded aseptic boxes. The purpose of this study is to obtain a mixture of particleboard which best fits the regulations JIS A 5908:2003 and SNI 03-2105-2006. Adhesive used for particleboard was phenol formaldehyde. The phenol formaldehyde is liquid and with hot press at 10 kg/cm2 or 15 kg/cm2 it becomes solid glue material. In the research chemical test, physical test, mechanical test, and knife edge load test are conducted.

The best results obtained were for the size of the shredded mixture aseptic boxes 50 mm x 5 mm, 10% phenol formaldehyde, 1 cm thick board, non glassir, and pressure of 15 kg/cm2 while from plate test results particleboard showed a not brittle state and can withstand the press. From the study results showed that the particle board shredded aseptic boxes suitable is used to partition board, plafond, and furniture. "

"Portland Composite Cement (PCC) merupakan campuran clinker dan bahan mineral tambahan seperti fly ash, pozzolan, dll. Produksi semen PCC yang lebih sedikit mengandung clinker ini dapat mengurangi ketergantungan terhadap clinker yang produksinya semakin berkurang. Seiring beredarnya semen PCC di pasaran, beton dengan semen PCC perlu diuji kekuatannya. Penelitian ini bertujuan untuk mendapatkan nilai-nilai kuat tekan, kuat tarik belah, dan kuat lentur beton menggunakan semen PCC. Beton didesain dengan menggunakan faktor air semen 0,3; 0,35; 0,45; 0,55; 0,65; 0,75; dan 0,8. Pengujian dilakukan pada umur 7, 14 dan 28 hari. Hasil pengujian diolah dengan metode rata-rata dan metode chisquare. Hasil pengolahan data menunjukkan metode chi-square menghasilkan data yang lebih akurat dengan jumlah error yang lebih sedikit. Grafik yang dihasilkan menunjukkan hubungan antara kuat tekan, kuat tarik belah dan kuat lentur dengan umur adalah berbanding lurus. Sedangkan hubungan antara kuat tekan, kuat tarik belah dan kuat lentur dengan FAS adalah berbanding terbalik. Dengan membandingkan kuat tekan, kuat tarik belah dan kuat lentur didapatkan hubungan kuat tekan dan kuat lentur adalah fr = 0,623 _ fc?, hubungan kuat tekan dan kuat tarik belah adalah ft = 0,656 _ fc?, dan hubungan kuat tarik belah dan kuat lentur adalah fr = 0,948 _ ft.

---

Portland Composite Cement (PCC) is a mixture of clinker and mineral additions such as fly ash, pozzolan, etc.. PCC's production which contain fewer clinker, can reduce the dependence on clinker, whose the production has decreased. Along the spread of PCC in the market, concrete using PCC need to be tested. This study aimed to obtain the values of compressive strength, splitting tensile, and flexural strength of concrete using PCC. Concrete is designed with water cement ratio 0,3; 0,35; 0,45; 0,55; 0,65; 0,75; dan 0,8. Tests are performed at the age of 7, 14 and 28 days.

The test results are processed by average method and chi-square method. Data processing results show chi-square method produces more accurate data with a smaller number of errors. The resulting graphs show the relationship between compressive strength, splitting tensile and flexural strength is directly proportional to the age. While the relationship between compressive strength, splitting tensile and flexural strength is inversely proportional to the water cement ratio. By comparing the compressive strength, splitting tensile and flexural strength, we can also obtain the relationship between compressive and flexural strength is fr = 0,623 _ fc?, the relationship between compressive and splitting tensile strength is ft = 0,656 _ fc?, and the relationship between splitting tensile and flexural strength is fr = 0,948 _ ft."