Hasil Pencarian  ::  Simpan CSV :: Kembali

"ABSTRAKTahap awal penelitian dimulai dari pembuatan Katalis Na-ACE dari cangkang telur ayam yang diaktivasi dengan cara kalsinasi dalam suhu 950oC dan menghasilkan bubuk putih yang merupakan ACE (Activated Chicken Eggshell). ACE diimpregnasi logam Na dengan menggunakan prekursor NaOH 3% sehingga menghasilkan Na-ACE yang memiliki kebasaan lebih besar dibandingkan dengan ACE. ACE dan Na-ACE dikarakterisasi menggunakan FTIR, EDAX dan XRD serta uji kebasaan dengan metode titrasi. Na-ACE yang telah berhasil disintesis digunakan untuk sintesis chalcone yang merupakan intermediet senyawa pirazolin. Senyawa chalcone disintesis melalui mekanisme reaksi kondensasi aldol silang dengan menggunakan starting material 2-Hidroksi Asetofenon dan 2-Hidroksi Benzaldehid yang menghasilkan rendemen terbesar yaitu 84.03% pada kondisi optimum pada Suhu 60oC, selama 3 Jam dengan katalis 15%. Senyawa chalcone hasil sintesis dikarakterisasi menggunakan FTIR, UV-VIS dan LCMS. Sintesis senyawa pirazolin menggunakan senyawa chalcone hasil sintesis sebelumnya dengan hidrazin hidrat dengan perbandingan 1 : 4 yang akan menghasilkan rendemen terbesar pada kondisi optimum 4 jam reaksi, suhu 80oC dan 20% katalis dengan rendemen sebesar 62,98%. Senyawa pirazolin hasil sintesis dikarakterisasi menggunakan FTIR, UV-VIS, dan LCMS. Senyawa chalcone dan pirazolin diuji antioksidan menggunakan DPPH dan didapatkan % inhibisi chalcone sekitar 41% pada konsentrasi chalcone sebesar 1000 ppm sedangkan % inhibisi pada pirazolin sebesar 84% pada konsentrasi pirazolin sebesar 125 ppm.

---

ABSTRACTThis Research was generated with the synthesis of catalyst Na-ACE from chicken egg shells, activated calcination in temperature of 950oC and will produced a white powder of ACE (Activated Chicken Eggshell). ACE was impregnated by Na metal using NaOH 3% solution as a precursor to produce Na-ACE which has a higher basicity than ACE. ACE and Na-ACE catalyst were characterized by FTIR, XRD and EDAX and for the bacisity test, titration method was used. The catalys of Na-ACE were used for synthesizing chalcone compound as intermediet material of pirazoline synthesis.Chalcone compound was synthesized through cross aldol condensation by reacting two starting materials, 2-hidroksi asetofenon, 2-hidroksi benzaldehid yield of 84,03% at the optimum condition 60oC, 3 hours and 15% catalys weight.this synthesized chalcone compound were characterized using FTIR, UV-VIS, and LCMS. The next step was synthesis pirazoline compound using chalcone and hidrazin hidrat with ratio of 1:4 and produced the greatest yield (62,98%) in the optimum conditionwhich are 4 hours reaction time, temperature of 80oC and 20% catalys weight. Pirazoline compound were characterized using FTIR, UV-VIS, and LCMS. Finally, both of chalcone and pirazoline compound were antioxidant tested using DPPH and resulted around 41% of inhibition of 1000 ppm for chalcone, and 84% inhibition of 125 ppm for pirazoline."

"Di antara beragamnya heterosiklik, 1,4-dihidropiridin (1,4-DHP) adalah salah satu cincin heterosiklik terpenting yang menunjukkan efek terapis serbaguna dan memainkan peran penting dalam proses sintesis. Senyawa N-heterosiklik lainnya yaitu, senyawa 1,2,3-triazol adalah heterosiklik nitrogen tak jenuh, aromatik, berbentuk cincin lima, terdiri dari tiga atom nitrogen beraturan dan dua atom karbon dengan dua ikatan rangkap. 1,2,3-triazol disukai dalam material pembuatan obat karena mudah berikatan dengan berbagai jenis enzim dan reseptor. Kalkon merupakan salah satu  metabolit sekunder golongan flavonoid pada beberapa spesies tumbuhan. Struktur senyawa kalkon mudah dimodifikasi untuk meningkatkan aktivitas biologisnya dengan menambahkan gugus fungsi seperti aril, halogen, hidroksil, karboksil dan fenil yang memungkinkan kalkon antibakteri, antimalaria, antikanker, antioksidan, antihiperglikemik, imunomodulator, dan efek antiinflamasi. Senyawa 1,4-dihidropiridin terbentuk melalui reaksi kondensasi Hantzsch. Reaksi ini sering menghasilkan produk dengan hasil yang baik dan metode eksperimen ini adalah protokol yang paling banyak digunakan untuk menyiapkan 1,4-dihidropiridin dengan berbagai substituen pada posisi C4. Senyawa1,2,3-triazol dapat disintesis melalui reaksi sikloadisi azida-alkuna yang dikatalisis oleh Cu(I). Ini adalah interaksi antara azida organik dan alkuna yang hanya melibatkan bentuk 1,4-disubstitusi 1,2,3-triazol. Dalam memebentuk senyawa hibrida dihidropiridin triazol menggunakan preskusor berupa variasi azida aromatik, sedangkan senyawa hibrida dihidropiridin triazol kalkon menggunakan prekusor dari variasi aldehida aromatik dan katalis basa dari NaOH. Produk akhir dari yang didapatkan diantaranya Dihidropiridin Triazol (4-Azido Benzoat) dengan yield sebesar 88,19%; Dihidropiridin Triazol (4-Azido Asetofenon) dengan yield sebesar 94,33%; Dihidropiridin Triazol Kalkon (4-Metoksibenzaldehida) dengan yield sebesar 30,02%; Dihidropiridin Triazol Kalkon (4-Fluorobenzaldehida) dengan yield sebesar 51,0%; dan Dihidropiridin Triazol Kalkon (2-Piridinkarboksaldehida) dengan yield sebesar 67,47%.

---

Among the diverse heterocycles, 1,4-dihydropyridine (1,4-DHP) is one of the most important heterocyclic rings that exhibits versatile therapeutic effects and plays an important role in the synthesis process. Another N-heterocyclic compound, namely, the 1,2,3-triazole compound, is an unsaturated, aromatic, five-ring nitrogen heterocycle, consisting of three regular nitrogen atoms and two carbon atoms with two double bonds. 1,2,3-triazole is preferred as a drug manufacturing material because it easily binds to various types of enzymes and receptors. Chalcone is one of the secondary metabolites of the flavonoid group in several plant species. The structure of chalcone compounds is easily modified to increase its biological activity by adding functional groups such as aryl, halogen, hydroxyl, carboxyl and phenyl which enable chalcone to have antibacterial, antimalarial, anticancer, antioxidant, antihyperglycemic, immunomodulatory and anti-inflammatory effects. The 1,4-dihydropyridine compound is formed via the Hantzsch condensation reaction. This reaction often produces products in good yields and this experimental method is the most widely used protocol for preparing 1,4-dihydropyridines with various substituents at the C4 position. The 1,2,3-triazole compound can be synthesized via the azide-alkyne cycloaddition reaction catalyzed by Cu(I). This is an interaction between an organic azide and an alkyne involving only the 1,4-disubstituted 1,2,3-triazole form. In forming the dihydropyridine triazole hybrid compound, a precursor is used in the form of a variety of aromatic azides, while the dihydropyridine triazole chalcone hybrid compound uses a precursor from a variety of aromatic aldehydes and a base catalyst from NaOH. The final products obtained include Dihydropyridine Triazol (4-Azido Benzoate) with a yield of 88.19%; Dihydropyridine Triazole (4-Azido Acetophenone) with a yield of 94.33%; Dihydropyridine Triazole Chalcone (4-Methoxybenzaldehyde) with a yield of 30.02%; Dihydropyridine Triazole Chalcone (4-Fluorobenzaldehyde) with a yield of 51.0%; and Dihydropyridine Triazole Chalcone (2-Pyridincarboxaldehyde) with a yield of 67.47%."

"Senyawa turunan β-merkapto karbonil adalah senyawa yang mengandung ikatan C-S yang menunjukkan berbagai aktivitas biologis, seperti anti-bakteri, anti-mikroba, anti-jamur, anti-kanker, anti-trombotik, anti-oksidan, efek anti-diabetes dan agen potensial sitotoksik. Sintesis senyawa turunan β-merkapto karbonil dapat ditingkatkan efisiensi waktunya dengan menggunakan katalis heterogen berbasis air berupa Bis[Prolinate-N,O]Zn atau Zn[Prolin]2. Dalam penelitian ini, modifikasi sinamaldehid telah dilakukan dengan sintesis kalkon dan turunannya dan mereaksikannya dengan reagen merkaptan seperti 2-merkaptoetanol. Berdasarkan hasil optimasi reaksi, diperoleh kondisi optimum dengan menggunakan pelarut etanol. Yield yang didapatkan dalam kondisi optimum pada senyawa 2 sebesar 59,44%, senyawa 3 sebesar 66,22%, senyawa 4 sebesar 66,22%, dan senyawa 5 sebesar 59,88%. Produk hasil sintesis dan katalis Bis[Prolinate-N,O]Zn dikarakterisasi menggunakan Kromatografi Lapis Tipis (KLT), Spektrofotometer FT-IR, Spektrofotometer UV-Vis, dan GC-MS. Kalkon dan turunannya, serta produk hasil sintesis diuji aktivitas antioksidan dengan metode DPPH. Aktivitas antioksidan yang ditandai dengan nilai IC50 untuk kalkon sebesar 9614,32 ppm, senyawa 2 sebesar 1378,25 ppm, 2-hidroksi kalkon sebesar 2569,74 ppm, senyawa 3 sebesar 581,47 ppm, 4-hidroksi-3-metoksi kalkon sebesar 1094,37 ppm, dan senyawa 5 sebesarThe β-mercapto carbonyl derivative is a compound containing C-S bonds which shows a variety of biological activities, such as anti-bacterial, anti-microbial, anti-fungal, anti-cancer, anti-thrombotic, anti-oxidant, anti-diabetic effects and potential cytotoxic agents. Synthesis of β-mercapto carbonyl derivative compounds can be increased in time efficiency using a water-based heterogeneous catalyst in the form of Bis [Prolinate-N, O] Zn or Zn[Proline]2. In this study, chalcone and cinnamaldehyde were modified with mercaptan reagents such as 2-mercaptoethanol. Based on the results of the optimization of the reaction, the optimum conditions are obtained by using ethanol as a solvent. Yield obtained in optimum conditions at compound 2 was 59.44%, compound 3 was 66.22%, compound 4 was 66.22%, and compound 5 was 59.88%. The Zn[Proline]2 catalysts and the product were characterized using Thin Layer Chromatography (TLC), FT-IR spectrophotometer, UV-Vis spectrophotometer, and GC-MS. Chalcone and derivatives, as well as synthesized products were tested for antioxidant activity by the DPPH method. Antioxidant activity is characterized by IC50 values for chalcone of 9614.32 ppm, compound 2 of 1378.25 ppm, 2-hydroxy chalcone of 2569.74 ppm, compound 3 of 581.47 ppm, 4-hydroxy-3-methoxy chalcone of 1094.37 ppm, and compound"

"Penyebab kematian paling signifikan di dunia (lebih dari 50%) diakibatkan dari stres oksidatif yang berkontribusi terhadap perkembangan banyak penyakit. Oleh karena itu, untuk melawan efek tersebut, dapat digunakan zat antioksidan. Zat antioksidan merupakan salah satu bioaktivitas yang dimiliki oleh senyawa heterosiklik (berbasis tiazolidindion). Pada penelitian ini, telah berhasil disintesis senyawa 4H-tiopiran melalui reaksi thia-Diels-Alder antara 1,4-naftokuinon dengan tiokalkon. Senyawa tiokalkon disintesis dari Lawesson’s Reagent (LR) dengan kalkon melalui reaksi thionation. Senyawa kalkon disintesis melalui reaksi kondensasi Claisen-Schmidt dari senyawa berbasis tiazolidindion dengan aldehida aromatik (tereftalaldehida), yang divariasikan dengan keton (asetofenon dan 2-asetil piridin) dengan bantuan katalis hijau nanopartikel magnetik CoFe2O4. Senyawa kalkon pada kondisi optimal menghasilkan rendemen sebesar 62,26%, dengan menggunakan sejumlah 5 mol% katalis dalam etanol pada kondisi refluks selama 2 jam. Aktivitas katalitik pada katalis nanopartikel magnetik ini dapat digunakan secara berulang hingga 5 siklus, tanpa kehilangan hasil yang signifikan. Senyawa akhir 4H-tiopiran menghasilkan rendemen sebesar 50,24% (variasi asetofenon) dan 48,96% (variasi 2-asetil piridin). Nanopartikel magnetik CoFe2O4 disintesis melalui metode green synthesis menggunakan ekstrak kulit petai sebagai agen penghidrolisis dan penstabil. Nanopartikel ini dikarakterisasi dengan FTIR, XRD, VSM, UV-DRS, FESEM, EDX, TEM, SAED, dan HR-TEM. Hasil karakterisasi menunjukkan bahwa CoFe2O4 yang disintesis memiliki ukuran nanopartikel serta sifat magnetik, optik, dan elektrikal. Hasil analisis karakterisasi XRD mengonfirmasi struktur kristalnya berbentuk kubik, dengan rata-rata ukuran kristalit 8,94 nm. Hasil analisis VSM dengan nilai Ms (41 emu/g), Mr (8 emu/g), dan Hc (693 Oe) mengonfirmasi sifat magnetiknya. Hasil analisis UV-DRS menunjukkan sifat optik dan elektrikal, dengan nilai celah pita sekitar 1,4 eV. Hasil pencitraan TEM menunjukkan bahwa morfologi nanopartikel magnetik CoFe2O4 berbentuk kubik, dengan rata-rata ukuran distribusi partikel 37,67 nm. Senyawa organik hasil sintesis juga diuji aktivitas antioksidannya dengan menggunakan metode DPPH dan parameter BDE. Senyawa 4H-tiopiran (variasi 2-asetil piridin) menunjukkan aktivitas antioksidan terkuat dengan nilai IC50 sebesar 90,80 μg/mL (kategori kuat). Hal ini juga didukung oleh nilai parameter BDE yang rendah pada gugus C-H dari benzo[g]tiokromena (74,0 kkal/mol) dan piridin (105,1 kkal/mol).

---

The most significant cause of death in the world (more than 50%) results from oxidative stress which contributes to the development of many diseases. Therefore, to counter these effects, antioxidant substances can be used. Antioxidant substances are one of the bioactivities possessed by heterocyclic compounds (thiazolidinedione-based). In this study, the compound 4H-thiopyran has been successfully synthesized through the thia-Diels-Alder reaction between 1,4-naphthoquinone and thiochalcone. A thiochalcone compound was synthesized from Lawesson's reagent (LR) with chalcone through a thionation reaction. Chalcone compounds were synthesized via Claisen-Schmidt condensation reactions of thiazolidinedione-based compounds with aromatic aldehydes (terephthalaldehyde), which were varied with ketones (acetophenone and 2-acetyl pyridine) with the help of CoFe2O4 magnetic nanoparticle green catalysts. The chalcone compound at optimal conditions produced a yield of 62.26% using of 5 mol% catalyst amount in ethanol under reflux conditions for 2 h. The catalytic activity of this magnetic nanoparticle catalyst can be used repeatedly, up to 5 cycles, without significant yield loss. The final compound 4H-thiopyran produced yields of 50.24% (acetophenone variation) and 48.96% (2-acetyl pyridine variation). CoFe2O4 magnetic nanoparticles were synthesized via the green synthesis method using petai peel extract as a hydrolyzing and capping agent. These nanoparticles were characterized by FTIR, XRD, VSM, UV-DRS, FESEM, EDX, TEM, SAED, and HR-TEM. The characterization results show that the synthesized CoFe2O4 has nanoparticle size as well as magnetic, optical, and electrical properties. The XRD characterization analysis results confirmed the cubic crystal structure, with an average crystallite size of 8.94 nm. Magnetic properties were confirmed through VSM analysis results with Ms (41 emu/g), Mr (8 emu/g), and Hc (693 Oe) values. UV-DRS analysis results showed optical and electrical properties, with a band gap value of about 1.4 eV. The TEM imaging results reveal that the morphology of the CoFe2O4 magnetic nanoparticles is cubic, with an average particle distribution size of 37.67 nm. The synthesized organic compounds were also tested for antioxidant activity using the DPPH method and BDE parameters. The 4H-thiopyran compound (2-acetyl pyridine variation) showed the strongest antioxidant activity with an IC50 value of 90.80 μg/mL (strong category). This is also supported by the low value of BDE parameters on the C-H group of benzo[g]thiochromene (74.0 kcal/mol) and pyridine (105.1 kcal/mol)."

"Pada penelitian ini digunakan variasi prekursor senyawa azida aromatik untuk menyintesis turunan 1,4-dihidropiridin dan variasi prekursor senyawa aldehida aromatik untuk menyintesis 1,4-dihidropiridin triazol hibrida kalkon. Pada sintesis 1,4- dihidropiridin bermotif 1,2,3-triazol melalui reaksi propargilasi, kondensasi Hantzsch, dan sikloadisi azida-alkuna, sedangkan pada sintesis hibrida 1,4-dihidropiridin kalkon bermotif 1,2,3-triazol melalui reaksi kondensasi Claisen-Schmidt. Sintesis menggunakan variasi prekursor dengan tujuan membandingkan hasil yield produk dan keberhasilan sintesis dengan mengubah struktur senyawa induknya. Produk-produk pada penelitian ini diharapkan bisa menjadi referensi dalam menyintesis suatu senyawa kalkon baru dengan gugus dihidropiridin dan triazol sebagai cincin penghubung. Didapatkan massa dan yield produk : dihidropiridin-triazol etil 4-benzoat (0,258 g; yield 94,37%), dihidropiridin- triazol-4-asetil (0,539 g; yield 93,90%), dihidropiridin-triazol-kalkon(tiofena) (0,054 g; yield 32,33%), dihidropiridin-triazol-ka lkon(t rans-s inam aldeh ida) (0,096 g; yield 57,48%). Produk-produk senyawa tersebut dikarakterisasi dengan instrumen titik leleh, FTIR, LC-MS/MS, dan NMR. Dengan demikian maka variasi dari azido aromatik tidak terlalu berpengaruh terhadap yield produk dihidropiridin-triazol, sedangkan variasi aldehida aromatik berpengaruh terhadap yield produk dihidropiridin-triazol-kalkon.

---

In this study, a variety of aromatic azide compound precursors were used to synthesise 1,4-dihydropyridine derivatives and a variety of aromatic aldehyde compound precursors to synthesise 1,4-dihydropyridine triazole hybrid chalcones. In the synthesis of 1,4-dihydropyridine patterned 1,2,3-triazole through propargylation reaction, Hantzsch condensation, and azide-alkyne cycloaddition, while in the synthesis of 1,4- dihydropyridine chalcone hybrid patterned 1,2,3-triazole through Claisen-Schmid t condensation reaction. The synthesis used a variety of precursors with the aim of comparing product yields and the success of synthesis by changing the structure of the parent compound. The products in this study are expected to be a reference in synthesising a new chalcone compound with dihydropyridine and triazole groups as connecting rings. The mass and yield of the products: dihydropyridine-triazole ethyl 4-benzoate (0.258 g; yield 94.37%), dihydropyridine-triazole-4-a cety l (0.539 g; yield 93.90%), dihydropyridine-triazole-chalcone(thiophene) (0.054 g; yield 32.33%), dihydropyridine- triazole-chalcone(trans-cinnamaldehyde) (0.096 g; yield 57.48%). The products were characterised by melting point, FTIR, LC-MS/MS, and NMR instruments. Thus, the variation of aromatic azido does not affect the yield of dihydropyridine-triazole product, while the variation of aromatic aldehyde affects the yield of dihydropyridine-triazole- chalcone product."