"Sintesis ZSM-5 mikropori dan hirarki telah dilakukan dengan menggunakan zeolit ??alam Bayat sebagai sumber silika dan alumina. Pada zeolit ??alam dilakukan proses aktivasi, purifikasi, dealuminasi, dan fragmentasi terlebih dahulu untuk menghilangkan pengotor yang terdapat dalam zeolit alam. Sintesis ZSM-5 dilakukan dengan menggunakan metode single template dengan menambahkan TPAOH tetrapropilamonium hidroksida merupakan substrat organik sebagai pengarah struktur mikropori. Selanjutnya, sintesis ZSM-5 hirarki menggunakan metode double templated dengan penambahan TPAOH dan PDDAM poli akrilamida-co-diallyldimethylammonium chloride sebagai pengarah struktur mesopori. Zeolit ??yang disintesis kemudian dikarakterisasi dengan berbagai metode seperti FTIR, XRD, SEM-EDX dan BET. Hasil karakterisasi XRD menunjukan bahwa ZSM-5 hasil sintesis memiliki puncak khas 2? 7-10? dan 22-25?. Hasil analisa SEM menunjukan ZSM-5 hasil sintesis berbentuk heksagonal yang merupakan ciri khas kristal ZSM-5. Rasio mol Si/Al hasil sintesis ZSM-5 mikropori dan ZSM-5 hirarki berturut-turut adalah 32,34 dan 43,53. Hasil analisa BET menunjukan ZSM-5 mikropori memiliki rerata diameter pori sebesar 2,0213 nm dan ZSM-5 hirarki memilki rerata diameter pori sebesar 2,3837. Kemudian, hasil sintesis ZSM-5 dimodifikasi menjadi H/ZSM-5 untuk menghasilkan zeolit yang lebih stabil dalam lingkungan termal atau hidrotermal. H/ZSM-5 mikropori dan hirarki diuji aktivitasnya sebagai katalis dalam reaksi perengkahan senyawa n-heksadekana sebagai senyawa model. H/ZSM-5 hirarki memiliki konversi yang paling tinggi yaitu sebesar 84,73 serta memiliki persentase yield dan selektivitas produk gasolin paling tinggi berturut-turut yaitu sebesar 83,13 dan 98,11.

---

Synthesis of miroporous and hierarhical ZSM 5 has been carried out using Bayat natural zeolite as silica and alumina source. Prior being used as material for synthesis, natural zeolite was subjected to the process of activation, purification, dealumination, and fragmentation to remove impurities contained in natural zeolite. The synthesis of microporous ZSM 5 was performed using a single template method by adding TPAOH tetrapropylammonium hydroxide as an organic substrate as micropore structure directing agent. Furthermore, the synthesis of hierarchical ZSM 5 uses a double template method with the addition of TPAOH and PDDAM poly acrylamide co diallyldimethylammonium chloride as mesoporous structure directing agent. The synthesized zeolite were then characterized by various methods such as FTIR, XRD, SEM EDX and BET. The XRD characterization results show that the synthesized ZSM 5 had typical peaks of 2 7 10 and 22 25 . SEM analysis results showed ZSM 5 synthesized had hexagonal shaped which is characteristic of ZSM 5 crystals. The molar ratio of Si Al of synthesized ZSM 5 micropore and ZSM 5 hierarchies were 32.34 and 43.53, respectively. The result of BET analysis showed that ZSM 5 micropore has pore diameter mean was 2.0213 nm and ZSM 5 hierarchy has pore diameter mean was 2,3837. Then, the ZSM 5 synthesis results were modified to H ZSM 5 to increase the stability zeolite in thermal or hydrothermal environments. Microporous and hierarchical H ZSM 5 were then used as a catalytic cracking reaction catalyst using n hexadecane as a model compound. Hierarchical H ZSM 5 had the highest conversion that is equal to 84.73 and has the highest percentage of yield and selectivity of gasoline product which is 83.13 and 98.11 , respectively."

"ABSTRAKSintesis Zeolit NaY menggunakan sumber alam alumina dan silika memiliki banyaktantangan. Berfokus pada pengurangan bahan sintetis, dalam penelitian ini, sintesis telahdilakukan menggunakan kaolin alam Bangka Belitung sebagai sumber silika danalumina. Pre-treatment pada kaolin diperlukan melalui proses aktivasi, pemurnian, dankalsinasi. Selanjutnya, zeolit NaY juga disintesis menggunakan kaolin alami sebagaisumber silika dan alumina dengan beberapa jenis benih yang dibuat dari sumber silikayang berbeda, yaitu Ludox HS40, Na-silikat, dan NaY komersil dari Wako. Semuamaterial kemudian dikarakterisasi menggunakan XRD, FTIR, dan SEM-EDX. Dapatdilihat bahwa seed dari Ludox HS40 memberikan NaY terbaik. Tapi, zeolite NaPmenjadi pengotor utama. Rasio Si/Al NaY zeolit adalah ~1.78 dengan bentuk poladifraksi mirip dengan yang ada dalam literatur. Sehingga disimpulkan, sintesis NaYmenggunakan aluminasilika alam sebagai sumber silika dan alumina cukup berhasil.Hasil uji perengkahan memperlihatkan jika katalis dengan material sintetik (HYsintetik) memiliki persen konversi, yield dan selektivitas yang lebih tinggi dibandingkandengan katalis dengan campuran bahan alam (HY MKSE dan HY SE). Namun, setiapkatalis memiliki persen yield dan selektivitas lebih tinggi terhadap produk C5dibandingkan dengan produk lainnya.

---

ABSTRACT Synthesis of sodium Y zeolite (NaY Zeolite) using natural sources of alumina and silicais interesting yet challenging. Focused on reducing synthetic material, in this research,synthesis has been carried out using Bangka natural Kaolin as silica and aluminasources. Pretreatment on kaolin was needed through the process of activation,purification, and calcination. The purpose of activation process is to remove the polarimpurities, free oxides in the surface that cover up the pores, and release the water thattrapped in the pores of the materials. The purification was conducted using Na-acetatebuffer solution with ratio 1:3 (w/v). The calcination process was required because Si-Oand Al-O structures in Kaolin are inactive and inert. Synthesis of NaY zeolite wasconducted with the addition seed gel using hydrothermal method with 24 hours at thetemperature 100 oC for crystallization. Furthermore, NaY zeolites were also synthesizedusing natural kaolin as silica and alumina sources with several types of seeds made fromdifferent silica sources, i.e Ludox HS40, Na-silicate, and NaY zeolite from Wako . Allmaterials then were characterized using XRD, FTIR, and SEM-EDX. It can be seen thatseed from Ludox HS40 gives the best NaY. But, NaP zeolite becomes the mainimpurities. The Si/Al ratio of NaY zeolite is ~1.78 but the shape of the crystals issimilar to that in literature. To conclude, synthesis of NaY using naturalaluminasilicates as source is considerably successful. The cracking test results show ifthe catalyst with synthetic material (HY synthetic) has a higher percent conversion,yield and selectivity compared to a catalyst with a mixture of natural materials (HYMKSE and HY SE). However, each catalyst has a higher percent yield and selectivityfor C5 products compared to other products."

"Sintesis ZSM-5 berpori hirarki telah dilakukan dengan metode double template untuk meningkatkan aktivitas dan selektivitas katalitik material tersebut. Dalam proses sintesis ini, dilakukan variasi template pertama yang digunakan, yaitu TPAOH (ZSM-5h), etilendiamin (ZSM-5h_en) dan trietilen tetramin (ZSM-5h_teta). Semua sampel hasil sintesis dikarakterisasi menggunakan instrumen XRD, BET SAA, SEM, EDS dan XRF. Hasil karakterisasi XRD menunjukkan bahwa pola difraksi sinar X ZSM-5 menunjukkan puncak yang kuat pada 2 theta 7-9 dan 22-25 yang merupakan puncak khas zeolit ZSM-5. Sedangkan pada ZSM-5h_en dan ZSM-5h_teta intensitas puncak-puncak tersebut sangat lemah yang menunjukkan bahwa zeolit ZSM-5 tidak terbentuk dengan baik. Hasil karakterisasi dengan BET Surface Area Analyzer menunjukkan bahwa ZSM-5 hasil sintesis memiliki ukuran pori > 2 nm dan terlihat adanya hysterical loop pada pola isoterm adsorpsi desorpsi yang dihasilkan. Hal ini menunjukkan bahwa telah terbentuk mesoporositas pada material hasil sintesis. Zeolit ZSM-5 selanjutnya dimodifikasi menjadi H/ZSM-5 dengan metode tukar ion kemudian dipanaskan pada suhu 550?C. H/ZSM-5 yang dihasilkan dikarakterisasi dengan FTIR dan EDS untuk mengetahui karakter keasaman yang dihasilkan kemudian diuji coba pada reaksi perengkahan katalitik senyawa n-heksadekana. Sebagai pembanding, dilakukan pula sintesis ZSM-5 mikropori (ZSM-5m) dan diuji aktivitas katalitiknya agar diketahui pengaruh ukuran pori terhadap hasil reaksi perengkahan katalitik. Hasil yang diperoleh menunjukkan bahwa katalis H/ZSM-5h menghasilkan persen konversi yang tinggi, yaitu sebesar 37,25% dengan persen massa yield gasolin dan selektivitas gasolin berturut-turut sebesar 17,28% dan 46,38%.

---

Attempt to synthesize hierarchical ZSM 5 zeolites (ZSM-5h) through double template method has been hydrothermally carried out. In order to develop the structure of microporous ZSM 5, three different templates was used TPAOH, ethylene diamine (en), or triethylene tetramine teta, followed by dimethyl dialyl ammonium chloride acrylamide copolymer as mesopore directing agent. All samples were characterized using XRD, BET Surface Area Analyzer, SEM, EDS and XRF.

XRD pattern of ZSM 5h zeolite showed specific peaks at position 2 theta of 7-9 and 22-25 that were characteristic of ZSM-5 zeolite. Otherwise, in the XRD pattern of ZSM-5h en and ZSM-5h teta zeolites the peaks were very weak, indicating that ZSM 5 zeolites were not well formed. Nitrogen adsorption of ZSM-5h exhibited hysterical loop at P Po 0.7 ndash 0.9 indicating the presence of hierarchical mesoporous in this sample.

SEM images of ZSM-5h zeolite showed hexagonal shape that was characteristic of ZSM-5 zeolite. Afterward, H/ZSM-5h zeolite was prepared through ion exchange treatment using 1 M ammonium nitrate solution, followed by calcination at 550 oC to remove all ammonia and produce H/ZSM-5h. This sample was characterized using FTIR and EDS to observe its acidity. Then, preliminary test on H/ZSM-5h zeolite as catalyst in cracking of n hexadecane will be discussed.

As comparison, microporous ZSM-5 zeolite ZSM 5m was synthesized and tested under the same conditions to study the effect of different pore size on its activity in catalytic cracking of n-hexadecane. The result show that conversion percent of catalytic reaction using H/ZSM-5h was 37,25 (%wt), which was higher than H/ZSM-5m. Percent of yield and selectivity of gasoline product using this material were 17,28 and 46,38 (%wt) respectively"

"ABSTRAKTelah dilakukan studi sintesis dan karakteristik zeolit HY dengan pori hirarki menggunakan metode template dan non template sebagai katalis untuk reaksi perengkahan n-heksadekana. Hasil karakterisasi XRD menunjukkan zeolit NaY hirarki dengan metode template dan non template memiliki puncak khas pada 2 teta 6?, 10? dan 11? yang merupakan puncak karakteristik untuk zeolit NaY, walaupun untuk NaY hirarki dengan template memiliki sedikit pengotor yaitu zeolit NaP. Adsorpsi dengan nitrogen menunjukkan bahwa NaY hirarki dengan template dan non template memilki hysterical loop pada P/Po 0,7 ndash; 0,9 yang mengindikasikan adanya pori hirarki pada kedua zeolit tersebut dan hasil pengukuran BET menghasilkan luas permukaan 393,496 m2/g dan 528,82 m2/g untuk NaY hirarki dengan template dan NaY hirarki tanpa template secara berturut-turut. Zeolit NaY hirarki kemudian dimodifikasi dengan metode tukar kation sehingga menghasilkan HY berpori hirarki dan hasil karakterisasi dengan IR-DRS menunjukkan adanya penambahan keasaman pada kedua zeolit HY berpori hirarki. Uji keasaman dengan adsorpsi menggunakan ammonia yang menunjukkan adanya puncak pada bilangan gelombang 1458 cm-1 dan 1443 cm-1 untuk HY hirarki template dan HY hirarki non template dimana bilangan gelombang tersebut merupakan vibrasi NH3 bebas yang teradsorpsi. Zeolit HY berpori hirarki kemudian digunakan sebagai katalis reaksi perengkahan katalitik menggunakan n-heksadekana sebagai senyawa model dan hasil reaksi perengkahan menunjukkan zeolit HY berpori hirarki memiliki selektivitas yang tinggi untuk menghasilkan fraksi gasolin dengan selektivitas sebesar 30 dan 23 dibandingkan dengan zeolit HY mikropori yang memiliki selektivitas sebesar 25 .

---

ABSTRACTThe synthesis and characteristic of HY zeolit with pore hierarchy using template and non template method had been done as cracking catalyst on n hexadecane. The XRD pattern showed both the hierarchical NaY zeolit with the template and non template methods had a characteristic peak at 2 teta 6 , 10 and 11 which are the characteristic peaks for NaY zeolits although for the hierarchical NaY the template has slightly impurities NaP zeolit. Adsorption with nitrogen showed that the hierarchical NaY with templates and non templates exhibited hysterical loop on P Po 0.7 0.9 which indicated a hierarchical pore on both zeolits and BET measurements results for NaY hierarchy with template and NaY hierarchy non template has surface area 393.496 m2 g and 528.82 m2 g for NaY hierarchy with template and NaY hierarchy non template, respectively. Zeolit NaY hierarchy was then modified by cation exchange method to form hierarchical HY and characterization results with IR DRS showed the addition of acidity in both zeolit after adsorption using ammonia, which are indicated peak at 1458 cm 1 and 1443 cm 1 for hierarchical HY with template and a non template which the wave numbers for NH3 vibrations. Hierarchical HY zeolits were then used as a catalytic cracking reaction catalyst using n hexadecane as a model compound and the cracking reaction result shows a porous HY porous zeolit having high selectivity to produce a gasolin fraction with selectivity of 30 and 23 compared to a micropore HY zeolit that having selectivity by 25 ."

"Sintesis zeolit NaY dari zeolit alam Bayat dilakukan melalui proses aktivasi, purifikasi, dealuminasi dan fragmentasi. Aktivasi dan purifikasi bertujuan untuk menghilangkan pengotor-pengotor pada zeolit. Proses dealuminasi dilakukan untuk mengurangi alumina yang terdapat di dalam struktur zeolit. Fragmentasi dilakukan berdasarkan metode Submolten Salt System dengan perbandingan zeolit alam Bayat dan NaOH adalah 2:1. Zeolit alam Bayat digunakan sebagai sumber silika dan alumina dengan NaAlO2 sebagai sumber alumina tambahan. Penelitian ini menggunakan zeolit alam Bayat karena harganya yang lebih terjangkau dan lebih ramah lingkungan dibandingkan dengan bahan sintetik. Sintesis zeolit NaY dilakukan dengan metode hidrotermal dan teknik seeding dengan komposisi seed gel 5 of Al : 6,25 Na2O: Al2O3 : 10 SiO2 : 180 H2O rasio molar dengan variasi pH 11, 12 dan 13. Didapatkan luas permukaan masing-masing zeolit sebesar 100,1744 m2/g, 142,8409 m2/g dan 22,4591 m2/g dengan ukuran pori masing ndash;masing sebesar 5,2 nm; 5,2 nm dan 35,5 nm. Hal ini didukung dengan data pola difraksi pada XRD yang menunjukan adanya kemiripan dengan pola XRD zeolit NaY sintetis dan juga data FTIR yang menunjukan adanya puncak penyusun unit pembangun sekunder puncak double 4 dan 6 ring khas faujasit pada bilangan gelombang 600-500 cm-1. Tahap selanjutnya adalah memodifikasi zeolit NaY yang telah disintesis menjadi zeolit HY dengan metode tukar kation untuk meningkatkan kadar keasaman dan kestabilannya sehingga dapat digunakan sebagai katalis perengkahan n-heksadekana. Hasil reaksi perengkahan menunjukan bahwa zeolit HY pH 12 memiliki nilai konversi dan yield gasolin paling tinggi dibandingkan dengan zeolit HY pH 11 dan HY pH 13 yaitu sebesar 25,945 . Bila ditinjau berdasarkan bahan baku pembuatannya, HY yang dimodifikasi dari zeolit alam Bayat memiliki kemampuan konversi, yield dan selektivitas terhadap gasolin yang lebih rendah jika dibandingkan dengan HY kaolin dan HY dari bahan sintetis.

---

Synthesis of NaY zeolite from Bayat Natural Zeolite was prepared through activation, purification, dealumination and fragmentation process. The activation and purification process are to remove some impurities. Dealumination process is done to leach some alumina from zeolite structures. Fragmentation process refers to Submolten Salt System methods with the ratio of Bayat natural zeolite and NaOH is 2 1. Bayat natural zeolite is used as silica and alumina sources with NaAlO2 as an additional source of alumina. This research uses Bayat natural zeolite because the price is more affordable and more environmentally friendly compared with synthetic materials. The NaY zeolite was synthesized with hydrothermal methods and seeding technique with the composition of seed gel 5 of Al 6.25 Na2O Al2O3 10 SiO2 180 H2O molar ratio with pH variation of 11, 12 and 13. The respective surface area of NaY zeolite pH 11, 12 and 13 as synthesized was 100,1744 m2 g, 142,8409 m2 g dan 22,4591 m2 g with the pore size of 5,25 nm 5,25 nm and 35,5 nm. This is supported by XRD diffraction pattern data which shows similarity with XRD pattern of synthetic NaY zeolite as well as FTIR data showing the peak of the construction of the secondary peak builder unit of 4 and 6 distinct faujasite rings in the wave number 600 500 cm 1. The next step is to modify the NaY zeolite that has been synthesized into HY zeolite by cation exchange method to increase the acidity level so that it can be used as a n hexadecane cracking catalyst. The next step is to modify the NaY zolite as synthesized into HY zeolite by cation exchange method to increase the acidity level so it can be used as cracking catalyst of n hexadecane. The result of the cracking reaction indicates that the HY zeolite pH 12 has the highest conversion value and highest yield of gasoline compared with the HY zeolite pH 11 and HY pH 13 which is 25,945 . Then reviewed on the basis of the raw material of manufacture, modified HY of the Bayat natural zeolite has a lower conversion ability, yield and selectivity to gasoline compared with HY kaolin and HY of synthetic materials."