Bondan Tiara Sofyan
WC-Co coatings for high temperature rocket nozzle applications : an applications note
" High velocity oxy-fuel (HVOF) sprayed tungsten carbide ? cobalt (WC-Co) coatings exhibit attributes that allow them to be a candidate material for high temperature applications; such as temperature insulators for rocket nozzles. This application note investigates the effect of surface preparation, in this case the grit blasting process, on the characteristics of the so-formed coating. The WC-Co coatings exhibited high hardness and low porosity. The composition of WC-Co coating varied in different regions, but on ... "
Fakultas Teknik Universitas Indonesia, 2010
J-Pdf
Artikel Jurnal  Universitas Indonesia Library
cover
Muhammad Faris Naufal Aulia
Studi pengaruh kekasaran permukaan substrat terhadap sifat mekanik lapisan coating paduan berbasis kobalt dengan metode pelapisan high velocity oxygen fuel (HVOF) kondisi operasi yang agresif dalam berbagai bidang industri yang mengharuskan komponen-kompon = Study on effects of substrate surface roughness on mechanical properties of cobalt based alloy coating with high velocity oxygen fuel (HVOF) method / Muhammad Faris Naufal Aulia
" ABSTRAK
Kondisi operasi yang agresif dalam berbagai bidang industri yang mengharuskan komponen-komponen didalamnya seperti pipa dan tube bekerja secara terus menerus dan sering kali menuntun kepada kegagalan. Kegagalan suatu komponen dalam suatu industri tentunya dapat membuat proses produksi terhenti untuk sementara waktu dan tentunya menimbulkan kerugian. Untuk dapat memperpanjang umur pakai komponen, high velocity oxygen fuel (HVOF) dianggap sebagai metode pelapisan yang sesuai. Sebelum melakukan pelapisan maka diperlukan proses persiapan permukaan terlebih dahulu, metode yang dipilih ... "
2016
S62969
UI - Skripsi Membership  Universitas Indonesia Library
cover
Pengaruh kekasaran permukaan terhadap kekuatan lekat dan struktur mikro lapisan WC-Co hasil HVOF Thermal Spray
" Pada makalah ini dibahas karakteristik lapisan WC-Co hasil proses thermal spray dengan teknik HVOF (High Velocity Oxy-Fuel) yang akan diaplikasikan pada pada nosel roket RX-10Q guna menggantikan pelapis grafit masif yang berat. Untuk itu, dilakukan studi pengaruh kekasaran permukaan terhadap kekuatan lekat dan struktur mikro lapisan. Hasil yang diperoleh menunjukkan bahwa variasi tekanan proses penyemprotan (grit blasting) menyebabkan variasi kekasaran permukaan, dimana semakin besar tekanan yang diberikan, semakin kasar permukaan yang diperoleh. Namun, kekuatan kohesi lapisan ... "
Depok: Fakultas Teknik Universitas Indonesia, 2004
JUTE-XVIII-4-Des2004-291
Artikel Jurnal  Universitas Indonesia Library
cover
Pelapisan Permukaan dalam Nosel Roket RKX100 dengan Cr2C3-NiCr HVOF: Optimasi Kekuatan lekat melalui Variasi Kekasaran Permukaan
" Nozzle of RKX l00 rocket contributes 30 % to the total weight of the structure, so that allowing further research on weight reduction. An alternatiye for this is by substitution of massive graphite, which is currently used' as thermal protector in the nozzle, with thin layer of HVOF (High Velocity Oxy-Fuel) thermal spray layer. A series of study on the characteristics of various type of HVOF coating material have been conducted This paper presents the investigation on the HVOF ... "
Jurnal Teknologi, Vol. 20 (3) Maret 2006 : 203-208, 2006
JUTE-20-3-Sep2006-203
Artikel Jurnal  Universitas Indonesia Library
cover
Albi Erlangga Aryatama
Studi pengaruh kekasaran permukaan material jis g 3132 spht-2 dan astm a213 t91 terhadap sifat mekanik hasil pelapisan cr2c3-nicr dengan metode high velocity oxygen fuel = Study of substrate roughness on jis g 3132 spht 2 and astm a213 t91 towards mechanical properties as a result of cr2c3 nicr coating with high velocity oxygen fuel method
" Dengan semakin meningkatnya perkembangan teknologi, tentunya dibutuhkan pula komponen alat produksi pada industri yang mampu menahan kondisi operasi agresif yang mengakibatkan kegagalan material seperti keausan, korosi dan oksidasi temperatur tinggi. Salah satu metode pelapisan material untuk menangani dan mencegah kegagalan tersebut adalah Thermal Spray. Pada penelitian ini, material JIS G 3132 SPHT-2 dan ASTM A213 - T91 diberi perlakuan grit blasting dengan variasi tekanan 2 bar, 3 bar, 4 bar dan 5 bar untuk mendapatkan ... "
Depok: Fakultas Teknik Universitas Indonesia, 2016
S63671
UI - Skripsi Membership  Universitas Indonesia Library