Hasil Pencarian  ::  Simpan CSV :: Kembali

"In manufacturing of component of automotive with use aluminum material, fluidity factor of aluminum liquid play a part important at moulding process with gravity and or die casting. Low fluidity liquid aluminum represent one of the factor causing to be formed affect / reject for example gas of porosity, shrinkage, misrun / shut cold and spot hard This research aim to know aluminum liquid _fluidity with parameter charging material l00% ingot ( 0% scrap) and 50% ingot (50% scrap), addition of AlTiB refiner grain ( 0,05 - o.6%) and addition ofAlSr modifier ( 0,001% - 0, 02%) by using temperature variation (630°C) 700?C1 720°C, 73 C, and 750°C) from 2 local ingot of aluminum ACZB. From result of this research indicate that the quality of ingot play a part important to fluidity value. ingot with little inclusion have high fluidity value. At addition of AlTtB grain refiner 0, 05 - 0,8 %, from both ingot assess reached by optimum fluidity of addition moment 0,6%. While addition of AlSr modifier of rate 0,001 - 0,02 % for reached by optimum fluidity value of addition moment 0, 01 %."

"Komposit Aluminium 6061 berpenguat nanopartikel SiC dibuat menggunakan metode pengecoran aduk, dimana ditambahkan unsur Mg 10% untuk mengoptimalkan pembasahan antara matriks dan penguat serta penambahan grain refiner Al-TiB untuk meningkatkan sifat mekanik dari material. Penambahan fraksi volume nanopartikel sebesar 0,05%, 0,10%, 0,15%, 0,20%, dan 0,30% dilakukan untuk mengetahui fraksi volume optimal.Data hasil penelitian menunjukkan nilai kekuatan tarik maksimum sebesar 217,2 Mpa pada penambahan 0,15%vf dengan elongasi optimal 6% pada penambahan 0,20%vf. Nilai kekerasan terus meningkat seiring dengan penambahan fraksi volume, akan tetapi harga impak terus menurun seiring dengan penambahan fraksi volume. Porositas yang terbentuk semakin meningkat seiring dengan penambahan fraksi volume nanopartikel SiC. Penambahan unsur Al-TiB menghasilkan ukuran butir yang lebih kecil dan persebaran partikel serta porositas yang lebih merata.

---

Aluminium 6061 composite reinforced with nanoparticles SiC produced by stir casting with the addition of Magnesium 10% as wetting agent to optimize wettability between matrix and reinforcement and addition of Titanium Boron as grain refiner to increase mechanical properties. In this study, addition of nano-particles volume fraction in the amount of SiC 0.05 %, 0.10 %, 0.15 %, 0.20 %, and 0.30 % were used in order to known the optimum volume fraction.As the result, the maximum of ultimate tensile strength is 271,2 Mpa in addition of 0,15%vf, with maximum elongation up to 6% in additon of 0,20%vf. Hardness value continues to rise with the addition of volume fraction, but the impact properties declines steadily with the addition of volume fraction. Porosity percentage increase with the addition of nanoparticles SiC."

"Banyak industri komponen otomotif yang menggunakan paduan AC4B dalam proses pengecoran cylinder head karena kelebihannya di antara paduan aluminium lainnya. Kelebihan paduan AC4B antara lain ringan, kuat, tahan korosi dan mampu dilakukan proses perlakuan panas. Cylinder head memiliki dimensi yang cukup rumit sehingga adanya perbedaan kecepatan pembekuan antara bagian tebal dan tipis menyebabkan terjadinya penyusutan dan kebocoran pada cylinder head. Dengan penambahan grain refiner (Ti) diharapkan terciptanya nukleat (partikel AlTi3) secara merata pada bagian tebal dan tipis sehingga menghasilkan pembekuan yang seragam (mengurangi terjadinya penyusutan dan bocor) serta menghasilkan ukuran butir yang lebih kecil. Masalah lain yang sering muncul adalah efek fading karena durasi LPDC yang cukup lama.Penelitian ini bertujuan mempelajari pengaruh penambahan grain refiner 0,05 wt.% Ti dalam bentuk serbuk (fluks) terhadap karakteristik paduan AC4B serta mempelajari waktu fading selama 1 sampai 4 jam dengan metode pengecoran LPDC. Sampel pengujian dibedakan menjadi sampel bagian tipis (stud bolt) dan bagian tebal (daging). Hal ini untuk mengetahui pengaruh penambahan titanium terhadap laju pembekuan cepat dan lambat. Kedua sampel tersebut dietsa untuk menghitung jarak DASnya dan dilakukan pengamatan mikrosruktur setelah itu menguji kekerasan. Sampel uji tarik dan uji komposisi diambil pada awal dan akhir pengecoran. Sampel pengamatan SEM dan EDS diambil pada bagian tebal dan dilakukan untuk mengetahui fasa intermetaliknya.Hasil penelitian menunjukkan bahwa penambahan 0,05 wt.% Ti menghasilkan kekerasan yang melebihi standar JIS untuk paduan AC4B (80 BHN) yaitu berkisar antara 87,2 sampai 92,9 BHN. Efek fading tidak terjadi baik pada bagian tebal maupun pada bagian tipis. Hal ini terlihat pada perubahan kekerasan yang terjadi selama 4 jam tidak terlalu signifikan. Adanya sedikit pengadukan pada mesin LPDC dicurigai yang menyebabkan tidak terlihatnya efek fading.Hasil uji tarik mengalami penurunan dari 165,8 MPa menjadi 162,9 MPa serta hasil perpatahanya getas. Fasa yang terbentuk adalah fasa intermetalik Al2Cu yang berwarna putih, fasa intermetalik β-Al15(Fe,Mn)3Si2 yang berwarna abu abu, fasa AlSi yang berwarna gelap dan matriks aluminium. Tingkat kegagalan cylinder head cukup tinggi yaitu 8,3 %. Hal ini diperkirakan karena kurang banyaknya jumlah grain refiner (Ti) yang digunakan pada proses pengecoran cylinder head dalam menanggulangi cacat bocor.

---

Many of automotive manufacturing used AC4B alloy for producing cylinder head because their benefical characteristics such as light, strong, good corrosion resistance and heat treateable. Cylinder head has complex dimension enough therefore the difference of cooling rate may lead to shrinkage and leakage of cylinder head. By adding grain refiner (Ti), nucleat AlTi3 are expected to uniformly distribute to thin and thick parts of cylinder head. The uniform cooling can reduce shrinkage, leakage and grain size.

This research aims for studying the addition of grain refiner 0.05 wt.% Ti (flux) of AC4B characteristics and studying fading efect in 1 to 4 h with Low Pressure Die Casting method. Testing sample is taken from thin (stud bolt) and thick parts to study effect of titanium on solidification rate on each part. Both of samples were etching for calculating the DAS and microstructure examination then evaluate hardness testing. Tensile and compotition samples were taken at start and ending of casting process. SEM and EDS samples were used to examine the intermetallic phases.

The research show that addition of grain refiner with 0.05 wt.% Ti was increasing hardness number about 87.2 to 92.9 BHN beyond JIS standard of AC4B (80 BHN). Fading efect did not occur at thick and thin sample. This is confirmed by the hardness?s changing in four hours was not significant. Agitation of LPDC mechine suspected the hardness of thick and thin sample were not significant.

Tensile test was decreasing from 165.8 MPa to 162.9 MPa and has a brittle fracture. Phases that occurred are white Al2Cu, grey β-Al15(Fe,Mn)3Si2, dark AlSi, and aluminium matrix. Reject level of cylinder head is 8.3 %. This predicted cause by insufficient of using grain refiner (Ti) for producing cylinder head to overcome leakage reject level."

"Paduan AC4B (standar JIS) atau paduan 333.0 as-cast (standar AA) secara komersial banyak digunakan sebagai bahan baku pembuatan komponen pada industri manufaktur otomotif. Diketahui sering terjadi reject karena kegagalan yang terjadi pada pembuatan komponen otomotif, diantaranya adalah shrinkage dan porosity. Pendinginan yang tidak stabil atau tidak merata dapat menyebabkan shrinkage yang berimplikasi pada menurunnya kekuatan dari produk cor. Dengan penambahan grain refiner sebagai nuklean, maka pendinginan dapat lebih terkontrol sehingga butir-butir logam menjadi lebih halus dan dihasilkan kekuatan mekanis yang lebih baik. Efek fading perlu dikontrol saat penambahan grain refiner. Keefektifan grain refiner semakin turun seiring dengan meningkatnya waktu.Pada penelitian ini dilakukan penambahan grain refiner 0.019 wt.% Ti dalam bentuk serbuk fluks setelah proses degassing. Proses pengecoran dilakukan pada Low Pressure Die Casting (LPDC) dalam rentang 120 menit dengan 4 variabel waktu fading setiap 30 menit : 30 menit, 60 menit, 90 menit, dan 120 menit. Sampel pengujian diambil pada bagian yang tebal dan bagian tipis dari cylinder head hasil proses LPDC untuk mengetahui pengaruh penambahan titanium terhadap laju pembekuan pada setiap variabel waktu fading. Dilakukan pengujian tarik dan kekerasan untuk mengetahui perubahan sifat mekanis berupa perubahan nilai kekuatan tarik, elongasi serta kekerasan. Pengamatan mikrostruktur untuk mengamati perubahan mikrostruktur yang terjadi akibat penambahan titanium. Pengamatan struktur dengan SEM dan EDAX dilakukan untuk mengetahui fasa yang terbentuk.Hasil penelitian menunjukkan bahwa penambahan grain refiner dengan kadar 0.019 wt.% Ti meningkatkan kekuatan tarik, kekerasan serta menurunkan nilai Dendrite Arm Spacing (DAS). Terjadi kecenderungan peningkatan kembali nilai DAS sehingga berdampak pada penurunan sifat mekanis setelah 30 menit karena berkurangnya keefektifan grain refiner. Menurunnya keefektifan grain refiner ini menunjukkan terjadinya efek fading. Fenomena ini diasumsikan karena pengendapan partikel AlTi3 pada dasar furnace seiring bertambahnya waktu karena perbedaan densitas partikel grain refiner (~3,35 gr/cm3) dan aluminium cair (~2.3 gr/cm3).

---

AC4B alloys (JIS standard) or 333.0 as cast alloys (AA standard) are widely used commercially as raw materials for parts manufacturing on automotive industries. Reject is often occurred and caused by shrinkage and porosity. Uncontrolled solidification could cause shrinkage which leads to lowering the strength of cast product. With the addition of grain refiner as nucleant, solidification rate can be controlled resulting in finer grain and better mechanical properties. Fading effect must be controlled at grain refiner addition. Grain refiner effectivity is lower as time increases.

On this research grain refiner addition in flux powder was added at 0.019 wt. % Ti after degassing process. Casting was done in Low Pressure Die Casting (LPDC) in 120 minutes with 4 variables fading time every 30 minutes : 30 minutes, 60 minutes, 90 minutes, and 120 minutes. Samples was taken from thick and thin parts from cylinder head to observe titanium addition on solidification rate on every fading time variables. Tensile test and hardness test was conducted to observe changes in mechanical properties in tensile strength, elongation and hardness value. Microstructure examination was performed to observe changes in microstructure after titanium addition, while SEM and EDAX observation was conducted to read phases that occur.

The experiment results shows that 0.019 wt. % grain refiner addition increased tensile strength, hardness,and decreased DAS value. After 30 minutes, there are increase in DAS value and decrease in mechanical properties because decrease of grain refiner effectivity. The decrease of grain refiner effectivity shows the fading effect. This phenomenon was assumed by the settling of Al3Ti on the bottom of the furnace as time increases because of the difference in grain refiner particle density (~3,35 gr/cm3) and molten aluminium (~2.3 gr/cm3)."

"Komposit merupakan material yang sedang dikembangkan, yang terdiri dari dua jenis material atau lebih untuk meningkatkan sifat mekanis. Salah satu aplikasinya yaitu pada tabung roket, yang menggunakan komposit berbahan dasar logam Metal Matrix Composite . Material yang digunakan yaitu Al 6061 dengan penambahan partikel nano SiC 0.15 Vf sebagai penguat, Mg 10 wt. sebagai agen pembasah, dan variabel TiB sebesar 0.02, 0.03, 0.04, 0.05, dan 0.06 wt. sebagai pemodifikasi butir agar lebih halus dan meningkatkan sifat mekanis. Hasil dari penelitian ini menunjukan dengan adanya penambahan partikel nano SiC dan TiB sebagai pemodifikasi ukuran butir, dapat meningkatkan sifat mekanis. Penambahan TiB yang paling baik yaitu pada pada penambahan 0.06 wt. dengan kandungan aktual pada komposit sebesar 0.0535 wt. , yang menghasilkan nilai kekuatan tarik sebesar 204.9 MPa, nilai kekerasan 53.58 HRB, dan laju keausan sebesar 0.0012 mm3/m. Peningkatan sifat mekanis disebabkan karena terdapat fasa Mg2Si sebagai penguat, lalu TiB2 sebagai agen nuklean yang memperhalus butir, dan fasa MgAl2O4 yang berada pada antarmuka partikel nano SiC dengan matriks sehingga memiliki pembasahan yang baik.

---

Composite is advance material that being developed, that contains of two materials or more to improve the mechanical properties. One of the application is rocket tube, that using metal matrix composite MMC . The base material is Al 6061 with addition of nanoparticles SiC 0.15 Vf as reinforcment, Mg 10 wt. as wetting agent, and variables of TiB 0.02, 0.03, 0.04, 0.05, and 0.06 wt. as grain refiner so it can improve the mechanical properties too. The result of this research, that with addition of nanoparticles SiC and TiB as grain refiner, it make the improvement of mechanical properties. The best addition of TiB is with the addition of 0.06 wt. TiB, which is the actual content in composite is 0.0535 wt. . The result shows that the Ultimate Tensile Strength reached 204.9 MPa, the hardness is 53.58 HRB, and the wear rate is 0.0012 mm3 m. The improvement of mechanical properties are because of there are Mg2Si phase as second phase that increase the strength of material, TiB2 as the nuclean to refine the grain, and MgAl2O4 phase that exist in the interface of nanoparticles SiC and the matrix, so it have good wettability between nanoparticles SiC and the matrix."

"ABSTRAKPenambahan partikel penghalus butir Ti-B dalam matriks ADC12 berpenguat nano SiC mampu meningkatkan sifat mekanis komposit dengan mekanisme penghalusan butir. Ti-B ditambahkan dengan tujuan menghasilkan Al3Ti sebagai nuklean dan memodifikasi struktur dendritik menjadi globular. Penambahan magnesium sebesar 10 bertujuan sebagai agen pembasah agar didapatkan ikatan antarfasa antara matriks dan penguat partikel nano SiC. Pada penelitian ini ditambahkan 0.15 Vf nano SiC dan variasi penambahan Ti-B 0.0 , 0.02 , 0.04 , 0.06 , dan 0.08 wt . Hasil penelitian dikarakterisasi secara komposisi dengan OES dan XRD, mikrostruktur dengan OM dan SEM, kemudian diuji mekanis tarik, keras, aus, dan impak. Komposisi paling optimal yaitu pada penambahan 0.04 wt TiB, yang menghasilkan nilai kekuatan tarik 135.9 MPa, kekerasan 45.6 HRB, laju aus 1.47x10-5 mm3/s, dan harga impak 0.0225 J/mm2. Peningkatan penambahan Ti-B linear dengan reduksi ukuran butir, namun penambahan lebih dari 0,04 wt tidak menunjukkan perubahan ukuran butir secara signifikan. Selain karena penghalusan butir akibat Al3Ti, peningkatan kekuatan mekanis terjadi akibat terbentuknya fasa MgAl2O4 pada antarmuka partikel nano SiC dan matriks ADC12.

---

ABSTRACTAddition of Ti B grain refiner in ADC12 nano SiC composite results in improvement of mechanical properties through grain refinement mechanism. Ti B was added to form Al3Ti as nucleant and modify the dendritic structure into globular. 10 of Mg added as a wetting agent to improve wettability between nano SiC as reinforce and ADC12 as matrix to maintain a good interphase. In this study, used 0.15 vf of nano SiC and few variations of TiB respectively 0.0 , 0.02 , 0.04 , 0.06 , dan 0.08 wt . Several test were conducted to characterize the material OES, XRD, OM, SEM, and destructive test tensile, hardness, wear, and impact . Obtained the best composition is 0.04 wt TiB which results 135,9 MPa in Ultimate Tensile Strength UTS , 45.6 HRB in hardness, 1.47x10 5 mm3 s as wear rate, impact strength 0.0225 J mm2. The increase of Ti B addition results in grain refinement but the addition more than 0,04 wt gives no significant results. The increase in mechanical properties of composites mainly because of Al3Ti acts as nucleant which initiates the grain refinement and the existence of MgAl2O4 phase which indicates a good interphase between nano SiC and ADC12 matrix."

"Al2O3 reinforced aluminum A356 has been successfully fabricated using the stir casting method. The development of current technology requires a material that is light, strong, tough, and corrosion and wear resistant, in addition to various other advanced properties. A composite material was therefore developed. Composite materials can be used in a wide range of strategic sectors such as the automotive, military, aerospace, and electrical industries. This study aims to develop a composite material that consists of aluminum A356 as the matrix and micro Al2O3 as the reinforcement, with 8 wt% magnesium as the wetting agent with the addition of grain refiner TiB at 0; 0.01; 0.0347; 0.0362; 0.0622; and 0.0689 wt% using the stir casting method. The material characterization comprises tensile testing, hardness testing, wear testing, chemical composition testing (OES and XRD), and microstructure testing (OM, SEM, and EDX). The test results revealed that the addition of 0.0347 wt% TiB was capable of reducing the size and changing the shape of a long and coarse grain to become round and fine, thereby significantly increasing its tensile strength, hardness, and wear resistance, but decreasing the elongation and ductility."

"Aluminium adalah material yang banyak digunakan dalam industri otomotif karena sifatnya yang ringan, kuat dan tahan korosif. Salah satu penggunaanya untuk komponen cylinder head, komponen ini menggunakan jenis paduan aluminium AC4B dengan proses low pressure die casting. Namun produk yang dihasilkan dalam proses pengecoran ini banyak ditemukan kegagalan seperti porositas, penyusutan (shrinkage) yang menyebabkan kebocoran.Dari permasalahan tersebut maka dilakukan penelitian yaitu dengan penambahan titanium kedalam aluminium AC4B yang bertujuan untuk menigkatkan sifat mekanis dan meminimalisasi kegagalan pada komponen cylinder head yang dihasilkan. Penelitian ini secara khusus ditujukan untuk mempelajari pengaruh variasi persentase titanium (0.019 wt % dan 0.029 wt %) terhadap penghalusan butir aluminium AC4B dengan proses low pressure die casting. Kemudian menguji sampel cylinder head dengan uji tarik, uji kekerasan, pengukuran besar dendrite arms spacing dan menganalisa mikrostuktur dengan mikroskop optik dan dengan SEM dan EDS, serta pengujian bocor.\Penambahan penghalus butir sebesar 0.019 wt % Ti dan 0.029 wt % Ti pada aluminium AC4B meningkatkan kekuatan tarik sebesar 13.4 % dan 20.1 % dengan bentuk perpatahan getas. Sementara, nilai kekerasan juga mengalami peningkatan dengan panambahan titanium. Pada bagian tipis, penambahan 0.019 wt % Ti dan 0.029 wt % Ti meningkatkan nilai kekerasan sebesar 3.06 % dan 5.65 %. Pada bagian tebal, penambahan 0.019 wt % Ti dan 0.029 wt % Ti meningkatkan nilai kekerasan sebesar 2.14 % dan 5.19 %. Untuk besar dendrite arms spacing terjadi penurunan dengan penambahan titanium. Pada bagian tipis, panambahan 0.019 wt % Ti dan 0.029 wt % Ti menurunkan besar DAS sebesar 29.3 % dan 48.5 %. Pada bagian tebal, dengan penambahan 0.019 wt % Ti dan 0.029 wt % Ti menurunkan besar DAS sebesar 6.67 % dan 28.6 %. Pada pengamatan mikrostruktur menggunkan SEM tidak ditemukannya fasa Al3Ti. Untuk hasil uji bocor terdapat cylinder head yang mengalami bocor. Penambahan 0.019 wt % Ti dan 0.029 wt % Ti tidak terlalu efektif untuk mengurangi kegagalan shrinkage dan bocor pada komponen cylinder head tapi dapat mengurangi kegagalan karena blow hole.

---

Aluminum is the material most used in automotive industry because of light, good strength and corrosion resistant. One of the application of aluminum is used for cylinder head component, this component use aluminum alloy AC4B with low pressure die casting process. But the product in casting process much have failure such as porosity and shrinkage which cause leakage.This experiment was conducted to counter these problems with addition of titanium to increase mechanical properties and minimize reject from cylinder head manufacturing. The subject of this research was to study the effect of 0.019 wt. % and 0.029 wt. % titanium addition on grain refinement of AC4B alloy produced with low pressure die casting. Cylinder head samples were tested with tensile test, hardness test, dendrite arms spacing observation. Microstructure analysis was performed with optical microstructure and SEM/EDS, and also leakage test.Grain refiner addition of 0.019 wt. % Ti and 0.029 wt. % Ti increased tensile strength 13.4 % and 20.1 % with brittle fracture. Meanwhile, hardness value also increased with the addition of titanium. On thin parts, addition of 0.019 wt % Ti and 0.029 wt % Ti increased hardness value for 3.06 % and 5.65 %. On thick parts, the addition of 0.019 wt % Ti and 0.029 wt % Ti increased hardness value for 2.14 % and 5.19 %. The addition of titanium decreased dendrite arms spacing value. On thin parts, the addition of 0.019 wt % Ti and 0.029 wt % Ti decreased DAS value for 29.3 % and 48.5 %. On thick parts, the addition of 0.019 wt % Ti and 0.029 wt % Ti decreased DAS value for 6.67 % and 28.6 %. Al3Ti was not found with microstructure analysis using SEM. On leakage test, there were some cylinder head that exhibit leakage. On 0.019 wt % Ti there were 5 cylinder head that experience leakage, or 6.25 % and on 0.029 wt % Ti addition there were 8 cylinder head that experience leakage, or 10 %.On leakage test, there are several cylinder head that exhibit shrinkage. The addition of 0.019 wt % Ti and 0.029 wt % Ti were not very effective in decreasing shrinkage failure and leakage on cylinder head component, but effective in decreasing failure caused by blow hole."

"Paduan AC4B merupakan paduan Al - Si - Cu yang banyak digunakan dalam proses pengecoran komponen otomotif, khususnya cylinder head. Karakteristik dari paduan ini adalah sifatnya yang kuat, ringan, tahan korosi, dan dapat dilakukan proses perlakuan panas. Salah satu masalah yang sering ditemui pada proses pengecoran Low Pressure Die Casting paduan ini adalah kebocoran yang diakibatkan oleh porositas dan penyusutan. Penelitian ini ditujukan untuk mempelajari penambahan penghalus butir titanium sebagai salah satu solusi dari masalah untuk mengatasi masalah penyusutan yang diakibatkan oleh tidak terkontrolnya laju pembekuan.Pada penelitian ini dilakukan penambahan penghalus butir 0.0505 wt. % Ti dan 0.072 wt. % Ti dalam bentuk serbuk fluks setelah proses degassing. Proses pengecoran dilakukan pada Low Pressure Die Casting dalam rentang waktu empat jam. Sampel pengujian diambil pada bagian yang tebal dan bagian tipis untuk mengetahui pengaruh penambahan titanium terhadap laju pembekuan pada tiap bagian. Dilakukan pengujian kekerasan dan pengamatan mikrostruktur untuk mengamati perubahan kekerasan yang terjadi dan perubahan mikrostruktur akibat penambahan titanium. Pengujian tarik juga dilakukan untuk mengetahui perubahan nilai kekuatan tarik. Pengamatan struktur dengan SEM dan EDAX dilakukan untuk mengetahui fasa yang terbentuk.Hasil penelitian menunjukkan bahwa penambahan penghalus butir dengan kadar 0.0505 wt. % Ti dan 0.072 wt. % Ti meningkatkan kekerasan dan kekuatan tarik, serta mengecilkan nilai DAS. Penambahan 0.0505 wt. % Ti meningkatkan kekerasan sebesar 2.8% pada bagian tebal dan 4.4 % pada bagian tipis. Penambahan 0.072 wt. % Ti meningkatkan kekerasan sebesar 7.17 % pada bagian tebal dan 5.1 % pada bagian tipis. Peningkatan kekuatan tarik pada penambahan 0.0505 wt. % Ti adalah sebesar 28.7 %, dan pada penambahan 0.072 wt. % Ti peningkatan yang terjadi sebesar 33.4 %. Nilai DAS pada penambahan 0.0505 wt. % Ti berkurang sebesar 20.2 % pada bagian tebal, 46.3 % pada bagian tipis. Penambahan 0.072 wt. % Ti mengurangi nilai DAS sebesar 26.5 % pada bagian tebal dan 50.3 % pada bagian tipis. Fasa yang terbentuk adalah fasa intermetalik Al2Cu yang berwarna putih, fasa intermetalik β - Al15(Fe,Mn)3Si2 yang berwarna abu abu muda, fasa AlSi yang berwarna abu abu gelap, dan matriks aluminium.

---

AC4B alloy is one of Al - Si - Cu alloys widely used in automotive parts casting, especially cylinder head. This alloys have characteristics such as strong, light, good corrosion resistance, and heat treatable. One of the problems commonly faced in low pressure die casting of this alloy is caused by porosity and shrinkage which leads to leakage. The subject of this research was to study addition of titanium grain refiner for an alternative solution to reducing shrinkage problems caused by uncontrolled solidification.

The addition of 0.0505 wt. % Ti and 0.072 wt. % Ti grain refiner in flux was added after degassing. Casting processes was done in Low Pressure Die Casting for four hours. Testing samples was taken from thick and thin parts to study the effect of titanium grain refiner addition on solidification rate on each parts. Hardness testing and microstructure examination was conducted to observe changes in both hardness and microstructure after titanium addition. Tensile test was also performed to study changes in tensile strength of material, while SEM and EDAX observation is done to read phases that occur.

The experiment results shows that addition of grain refiner of 0.0505 wt. % Ti and 0.072 wt. % Ti increased hardness and tensile strength, and also decreased DAS value. The increase of hardness on the addition of 0.0505 wt. % Ti is 2.8 % on thick parts and 4.4 % on thin parts. The addition of 0.072 wt. % Ti increased hardness for 7.17 % on thick parts and 5.1 % on thin parts. Tensile strength increased at the addition of 0.0505 wt. % Ti for 28.7 % , while the addition of 0.072 wt. % Ti increased tensile strength for 33.4 %.DAS value decreased from the addition of 0.0505 wt. % Ti for 20.2 % on thick parts, and 46.3 % on thin parts. The addition of 0.072 wt. % Ti decreased DAS value for 26.5 % on thick parts and 50.3 % on thin parts. Phases that occurred are white Al2Cu, light grey β - Al15(Fe,Mn)3Si2, dark grey AlSi, and aluminium matrix."