"The use of waste cooking oil (WCO) as feedstock and in microwave heating technology helps to reduce the cost of biodiesel. In this study, a continuous flow transesterification of waste cooking oil (WCO) by microwave irradiation for biodiesel production using calcium oxide (CaO) as aheterogeneous catalyst, calcined from cockle shells, is used. The catalyst was packed inside a plastic perforated container mounted on a stirrer shaft and inserted inside the reactor. The thermocouple inside the reactor was connected to a temperature controller and microwave power input to maintain the temperature. Response surface methodology (RSM) was employed to study the relationships between power input, stirrer speed and liquid hourly space velocity (LHSV) on the WCO methyl ester (WCOME) conversion at a fixed molar ratio of methanol to oil of 9 and a reaction temperature set at 65oC. The experiments were developed using the Box-Behnken design (BBD) for optimum conditions. The transesterification of the WCO was produced at 72.5% maximum WCOME conversion at an optimum power input of 445 W, stirrer speed of 380 rpm and LHSV of 71.5 h-1 . The energy consumption in a steady state condition was 0.594 kWh for the production of 1 litre WCOME, for this heterogeneous catalyst is much faster than conventional heating."

"Thermal decomposition of fish bones to obtain calcium oxide (CaO) was conducted at various temperatures of 400, 500, 800, 900, 1000, and 1100 °C. The calcium oxide was then characterized using X-ray diffractometer, FTIR spectrophotometer, and SEM analysis. The calcium oxide obtained from the decomposition at 1000 °C was then used as a catalyst in the production of biodiesel from waste cooking oil. Diffraction pattern of the calcium oxide produced from decomposition at 1000 °C showed a pattern similar to that of the calcium oxide produced by the Joint Committee on Powder Diffraction Standard (JCDPS). The diffractions of 2q values at 1000 °C were 32.2, 37.3, 53.8, 64.1, and 67.3 deg.

The FTIR spectrum of calcium oxide decomposed at 1000 °C has a specific vibration at wave-length 362 cm-1, which is similar to the specific vibration of Ca-O. SEM analysis of the calcium oxide indicated that the calcium oxide's morphology shows a smaller size and a more homogeneous structure, compared to those of fish bones. The use of calcium oxide as a catalyst in the production of biodiesel from waste cooking oil resulted in iod number of 15.23 g/100 g KOH, density of 0.88 g/cm3, viscosity of 6.00 cSt, and fatty acid value of 0.56 mg/KOH. These characteristic values meet the National Standard of Indonesia (SNI) for biodiesel."