Subandrio Soemali
Pengaruh basisitas pada pengolahan bijih kromit yang telah di benefisiasi pada sub-merged arc furnace untuk pembuatan ferrochrome = Effect of basicity in chromite processing which has been in benefitiation on sub-merged arc furnace for ferrochrome making
" Ferokrom 45-75 Cr dan 35-50 Fe paduan penting pembuatan baja tahan karat karena sifat kekuatan dan ketahanan korosi yang tinggi. Ferokrom berasal dari endapan kromit di wilayah Indonesia adanya berkadar rendah dengan ratio Cr/Fe < 1.5 sehingga diperlukan benefisiasi. Tahapan benefisiasinya pemisahan magnetik lemah dilanyutkan pemanggangan temperatur, waktu, jenis reduktor dan berat CaCO3 , hasil pemanggangan dilakukan pemisahan magnetik kuat dan diuji xrf dan xrd. Parameter optimal benefisiasi untuk pembuatan briket input peleburan tanur SAF. ... "
2017
T48407
UI - Tesis Membership  Universitas Indonesia Library
cover
Adi Cipto Dimas Perkasa
Studi proses thermal reactive deposition dengan variasi temperatur menggunakan campuran serbuk ferrovanadium dan ferrochromium = Study of thermal reactive deposition process with temperature variations using ferrovanadium and ferrochromium powder
" ABSTRAK
Telah dilakukan proses surface treatment Thermal Reactive Deposition (TRD) dalam pembentukan lapisan tipis karbida pada substrat baja SUJ2 . Pada proses ini menggunakan metode pack cementation menggunakan campuran serbuk Ferrovanadium dan Ferrochromium sebagai carbide former . Serbuk carbide former dan susbtrat dicampur bersama NH4Cl dan Al2O3 untuk diproses selama 6 jam dalam furnace. Dilakukan 3 variasi temperatur yaitu 900, 950 dan 1000 C untuk mengetahui pengaruh temperatur terhadap ketebalan, kehomogenan, kekerasan dan laju keausan lapisan ... "
2017
S67498
UI - Skripsi Membership  Universitas Indonesia Library
cover
Mohammad Dani
A new precipitation-hardened austenitic stainless steel investigated by electron microscopy
" The 56Fe16.6Cr25Ni0.9Si0.5Mn austenitic superalloy has been produced in an induction furnace; it was made from granular ferro-scrap, ferrochrome, ferrosilicon, and ferromanganese materials. Originally, this alloy had been proposed for use in high mechanical loads and high temperature conditions (such as in nuclear and fossil fuel power plant facilities). Tensile strength tests showed that the alloy has an average yield strength of about 430.56 MPa, which is higher than Incoloy A-286 (a commercially available alloy). A ... "
Depok: Faculty of Engineering, Universitas Indonesia, 2018
UI-IJTECH 9:1 (2018)
Artikel Jurnal  Universitas Indonesia Library
cover
Laurensia
Peningkatan kadar dan rasio pasir kromit kadar rendah melalui proses benefisiasi dengan variabel jumlah reduktor batubara dan aditif caso4 pada reduction roasting = The enhancement of chromium grade and its ratio from local low grade chromite sand through beneficiation process with the variation of reductant and caso4 as additive dosage on reduction roasting process
" ABSTRAK
Sekitar 95 dari seluruh bijih kromit yang ditambang di dunia digunakan sebagai bahan baku pembuatan ferrochromium FeCr . Pada penelitian sebelumnya, peleburan pasir kromit kadar rendah tidak dapat menghasilkan ferrochromium dengan kadar Cr ge; 60 sehingga pasir kromit kadar rendah harus dilakukan proses benefisiasi untuk meningkatkan kadar Cr dan rasio Cr/Fe sebelum proses peleburan menjadi ferrochromium. Penelitian ini menggunakan pasir kromit kadar rendah asal Kabupaten Konawe, Sulawesi Selatan. Proses benefisiasi yang dilakukan adalah magnetic separation ... "
2017
S66515
UI - Skripsi Membership  Universitas Indonesia Library