"A research was being done for analyzing strength and stiffness characteristic of two types of laminated fiber glass/aramid/epoxy composite material. Each type consists of eight and ten layers in same configuration with two different kinds of angle orientations. The base materials used in this research were glass epoxy and aramyd/epoxy fiber composites in which the epoxy is used as matrix. Some mechanical tests and optical observation was carried out for analyzing its macro and micro mechanical characteristics for both types. From the result of mechanical test, it was found that the compressive strength, stiffness and impact characteristic of the second type was better than the first type, but its tensile strength was slightly lower then the first type. In impact test for both type, there was found an increasing in impact strength by decreasing the temperature from 27 °C to -10 °C, which at temperature was -10 °C the both of material was becoming brittle. Optically, it was found that the second type more rigid than first type by observing the shape and direction of its fracture."

"Sifat mampu basah komposit merupakan salah satu kunci utama dalam peningkatan sifat mekanis komposit. Penelitian ini dilakukan untuk mengetahui pengaruh variasi orientasi, kerapatan dan perlakuan permukaan pada serat terhadap sifat mampu basah komposit. Serat yang digunakan adalah fiberglass dan pengukuran sudut kontak dilakukan dengan metode image processing. Hasil pengaruh dari variasi didapatkan dari hubungan variasi terhadap sudut kontak dan waktu pembasahan. Berdasarkan penelitian yang telah dilakukan, orientasi serat 45°/45° menghasilkan sudut kontak yang lebih rendah, namun membutuhkan waktu pembasahan yang lebih lama dibandingkan dengan orientasi serat 0°/90°. Perbedaan sudut kontak mencapai 6 derajat lebih rendah dan waktu pembasahan 20 detik lebih lama pada orientasi serat 45°/45°. Sedangkan untuk pengaruh kerapatan, kerapatan serat 900 menghasilkan sudut kontak yang lebih rendah dan waktu pembasahan yang lebih cepat dibandingkan dengan kerapatan serat 1250. Perbedaan sudut kontak mencapai 5 derajat lebih rendah dan waktu pembasahan hanya 7 detik lebih cepat. Adanya perlakuan permukaan berupa perendaman dengan NaOH 5% mampu menurunkan sudut kontak hinga 25 derajat untuk resin epoksi dan 3 derajat untuk resin poliester tak jenuh serta mempercepat waktu pembasahan 10 detik. Dengan menggunakan resin poliester tak jenuh, sudut kontak yang dihasilkan lebih kecil dan waktu pembasahan yang lebih cepat dibandingkan dengan resin epoksi.

---

Wettability of composite is one of key to increase mechanical properties of composite. This research focused on the effect of orientation, density and surface treatment on fiber to the characteristic of composite?s wettability. The fiber used in this research is fiberglass and the method for contact angle measurement is image processing. The result for those variations can be obtained from contact angle and wetting time. According to result, fiber with orientation 45°/45° gives lower contact angle but longer wetting time than fiber with orientation 0°/90°. For orientation 45°/45°, the differences in contact angle reaches 6 degree lower and the wetting time is 20 second longer. In case of fiber density, the sheet with 900 of fiber density 900 has lower contact angle and faster wetting time than the sheet with 1250 of fiber density. The sheet with 900 of fiber density has results that 5 degree lower for contact angle and 7 second faster for wetting time. The surface treatment with NaOH 5% can decrease the contact angle until 25 degree for epoxy resin used and 3 degree for unsaturated polyester used, also accelerate the wetting time until 10 second. The use of unsaturated polyester results smaller contact angle and faster wetting time than using epoxy resin."

"Komposit serat kaca yang diperkuat dengan bahan polimer Glasss Fibre Reinforced Polymer GFRP memiliki kekurangan yaitu kurang tahan terhadap api. Penggunaan clay dapat meningkatkan sifat tahan api terhadap GFRP. Akan tetapi, diperlukan pencampuran yang baik agar clay dapat terdispersi dengan baik. Penelitian ini bertujuan untuk mengetahui pengaruh clay dan kondisi pencampuran terhadap sifat anti bakar, kuat impak, dan modulus lengkung komposit GFRP/clay. Polimer Unsaturated polyester UP , serat kaca, dan 3-Aminopropyltriethoxysilane masing-masing digunakan sebagai matriks, penguat, dan compatibilizer untuk membuat komposit. Unsaturated polyester-clay-silane dicampur menggunakan magnetic stirrer dengan variasi kecepatan dan waktu pencampuran. Komposit unsaturated polyester-serat kaca-clay-silane difabrikasi menggunakan metode vacuum bagging. Variasi clay yang digunakan adalah 1 wt. , 2wt. , dan 3 wt.. Variasi kecepatan rotasi dan waktu pencampuran masing-masing 100,150, 200 rpm dan 60, 90, dan 120 menit. Komposit UP ndash; serat kaca digunakan sebagai bahan pembanding.Hasil penelitian menunjukkan bahwa komposit dengan kandungan clay 1wt tidak terbakar dengan nilai laju bakar sebesar 0 mm/min. Tidak terdapat perubahan variabel yang signifikan pada kuat impak dengan mekanisme berbeda seperti shear dan difusi yang bekerja bersamaan saat mendispersikan clay. Nilai modulus lengkung optimum dimiliki oleh komposit dengan komposisi clay 1 wt _200 rpm_60 menit sebesar 10 0.4 GPa , yang mengalami kenaikan 20 dibandingkan dengan UP ndash; serat kaca.

---

Glass fibre reinforced polymer GFRP composites have a weakness in fire resistant property. The addition of clay can improve the fire resistant property of GFRP. However, a good mixing is needed to disperse the clay. This research aims to observe the effect of clay and mixing conditions on fire resistance, impact strength, and flexural modulus of GFRP clay composites. Unsaturated polyester UP , glass fiber and 3 Aminopropyltriethoxysilane respectively were used as a matrix, a reinforcement and a compatibilizer respectively to build the composites. Unsaturated polyester clay silane were mixed using a magnetic stirrer with a variation of rotation speed and mixing duration. The composites were fabricated using a vacuum bagging method. The composition of clay was varied from 1, 2, and 3 wt. The rotation speed and mixing time were varied at 100, 150, 200 rpm and 60, 90, and 120 minutes, respectively. UP glass fiber was used as a comparison material.

The results showed that composites with 1 wt clay content was not burned with the buring rate value of 0 mm min. There were no significant effects of variables on impact strength in between the boundaries that attributed to different mechanisms such as shear and diffusion that worked together to disperse the clay. The optimum flexural modulus was found in the 1 wt clay 200 rpm 60 minute composites with a value of 10 0.4 GPa in which 20 higher compared to the UP glass fibre composites."

"Komposit polimer epoksi berpenguat serat gelas (GFRP) merupakan salah satu material yang dewasa ini sangat populer, karena nilai ekonomis dan kehandalan nya. Aplikasi GFRP pada lingkungan bawah air, menyebabkan terjadinya proses wet curing yang dapat mempengaruhi sifat mekanik. Penelitian ini membahas faktor-faktor yang dapat mempengaruhi kinerja dari material GFRP dan daya rekat komposit tersebut dengan logam, faktor-faktor tersebut diantaranya seperti durasi curing, temperatur dan salinitas. Komposit GFRP dengan dua tipe hardener yaitu poliamin dan siklikamin dimanufaktur dengan menggunakan metode hand lay-up. Spesimen GFRP selanjutnya dengan variasi durasi curing 12, 24 dan 48 jam dimanufaktur pada lingkungan udara, air laut dan air distilat dengan temperatur dan salinitas yang berbeda. Kemudian dilakukan pengujian tarik, tekuk dan impak serta uji kekuatan bonding dan pengamatan SEM. Dari hasil penelitian yang dilakukan, diperoleh kesimpulan bahwa GFRP dengan hardener poliamin gagal membuat ikatan crosslink pada proses wet curing, sedangkan dengan hardener siklikamin crosslink berhasil terbentuk, nilai karakteristik sifat mekanik pada proses wet curing sedikit menurun dibandingkan dengan proses dry curing, seperti hasil uji tarik menurun sebesar 10% dan uji daya rekat sambungan logam dengan komposit turun sebesar 16%. Pada penelitian selanjutnya dapat dilakukan uji coba dilapangan.

---

Glass Fiber Reinforced Polymer (GFRP) is very popular among other material due to its economic value and reliability. As an application to subsea pipeline, the main challenge of GFRP is the process of wet curing which is required by epoxy composite to form a strong bonding of cross link in subsea environment and consequently can effect mechanical properties.

This study evaluated the factors that might affect the performance of epoxy composite material and its bonding to metal, i.e. curing duration, temperature, and salinity. GFRP composite with two different types of hardener which are polyamine and cyclic amine were manufactured by hand lay-up method. Then, the specimens were manufactured in atmospheric, sea water, and distillation water with different variables such as 12, 24, and 48 hours curing time; temperature; and salinity. Then, the specimens were tested for their tensile, flexural, impact, and bonding strength. The last, observation of fracture appearance was done by SEM.

Result of the study, concluded that GFRP with polyamine hardener was failed to create cross link on wet curing process while the one with cyclic amine hardener successfully created cross link. However, the mechanical characteristic was a bit lower, such as the tensile strength decreased to 10% and the adhesion strength of the bonding decreased to 16%. For the future, this study can be investigated by field testing."

"Material komposit adalah kombinasi dua atau lebih komponen berbeda yang membentuk material dengan sifat baru. Penyusun material komposit terdiri dari bahan penguat dan matriks. Vacuum infusion ialah proses pembuatan komposit dimana resin dihisap pompa vakum untuk membasahi serat pada cetakan. Terdapat permasalahan terkait geltime resin pada vacuum infusion yang membuat munculnya white spot pada material komposit. Hal ini menyebabkan waktu infusi resin harus diperhatikan. Pada penelitian ini, jumlah dan lapisan serat divariasikan. Didapatkan data waktu infusi resin pada luas serat woven roving 15x20 cm dari dua hingga enam lapis dalam detik : 55, 59, 66, 71, 78; 15x25 cm dari dua hingga enam lapis dalam detik : 119, 142, 168, 198, 235; 15x35 cm dari dua hingga enam lapis dalam detik : 181, 203, 235, 263, 303. Pada pengolahan data, didapatkan hasil panjang dimensi serat maksimum yang dapat dialiri resin, dengan hasil pada jumlah 2 lapisan: Luas 0,4825 m2, Panjang 3,21 m; 3 lapisan: Luas 0,4524 m2, Panjang 3,01 m; 4 lapisan: Luas 0,4506 m2, Panjang 3,00 m; 5 lapisan: Luas 0,4402 m2, Panjang 2,93 m; 6 lapisan: Luas 0,4391 m2, Panjang: 2,92 m. Selain itu, didapatkan jumlah lapisan serat maksimum yang dapat dialiri resin untuk luas 15x20 cm, 15x25 cm, dan 15x35 cm masing-masing 147, 145, dan 123 lapis. Untuk mencegah permasalahan geltime resin, serat woven roving yang dibuat menjadi komposit tidak boleh melewati luas, panjang, dan jumlah lapisan serat maksimum hasil penelitian ini. Pada penelitian ini diketahui resin lebih cepat mengalir pada serat woven roving dibanding serat chopped strand mat.

---

Composite material is two or more different components combination to form material with new properties. Composite material consists of reinforcement and matrix. Vacuum infusion is process to make composite in which resin sucked by vacuum pump to moisten fiber in mold. There is a problem in vacuum infusion related to geltime resin, makes white spots appear on composite. This make resin infusion time should be considered. In this research, area and reinforcement layers are variated. This research obtain resin infusion time data for woven roving 15x20 cm in two until six layers in seconds 55, 59, 66, 71, 78 15x25 cm in two until six layers in seconds 119, 142, 168, 198, 235 15x35 cm in two until six layers in seconds 181, 203, 235, 263, 303. Data processing obtained maximum fiber area and length that can flown by resin, with result at 2 layers, Area 0,4825 m2, Length 3,21 m 3 layers Area 0,4524 m2, Length 3,01 m 4 layers Area 0,4506 m2, Length 3,00 m 5 layers Area 0,4402 m2, Length 2,93 m 6 layers Area 0,4391 m2, Length 2,92 m. Maximum fiber total layers that can flown by resin obtain for 15x20 cm, 15x25 cm, and 15x35 cm such as 147, 143, and 125 layer. To overcome resin geltime problem, woven roving fiber that will made must not surpass area, length and total layers maximum in this research. In this research we known that resin is more quickly flow in woven roving fiber than chopped strand mat."

"Material komposit telah berkembang menjadi bahan serbaguna yang sangat diminati dalam berbagai aplikasi, terutama dalam bidang pertahanan dan militer. Glass Fiber Reinforced Polymer atau GFRP, adalah salah satu  jenis material komposit yang paling umum digunakan dalam bidang manufaktur bahan komposit. Material seperti GFRP menawarkan potensi besar dalam hal ini, memberikan perlindungan yang efektif dengan berat yang lebih ringan dibandingkan dengan bahan tradisional seperti baja. Fokus penelitian ini adalah penggunaan simulasi Finite Element Method untuk pengujian balistik untuk menilai kinerja material komposit serat kaca dan matriks epoksi terhadap peluru jenis I 38 Special Round Nose dengan kecepatan 274 m/s dan jenis II 9 mm Full Metal Jacketed dengan kecepatan 334 m/s, sesuai dengan standar National Institute of Justice. Berdasarkan hasil dari simulasi, 48 lapis serat fiberglass/epoksi dapat menyerap energi kinetik dari peluru Special RN sebesar 165,0 Joule dan meneruskan energi kinetik sebesar 7,8 Joule. 80 lapis serat fiberglass/epoksi dapat menyerap energi kinetik dari peluru 9mm FMJ sebesar 216,7 joule dan meneruskan energi kinetik sebesar 23,7 Joule. Kerusakan yang terjadi pada serat fiberglass/epoksi adalah brittle fracture. Perubahan bentuk peluru pada kedua simulasi adalah bagian depan peluru dan mengalami deformasi menjadi bentuk kerucut (conical).

---

Composite materials have evolved into versatile materials that are in high demand in various applications, especially in the defence and military fields. Glass Fiber Reinforced Polymer or GFRP, is one of the most commonly used types of composite materials in the field of composite materials manufacturing. Materials such as GFRP offer great potential in this regard, providing effective protection at a lighter weight compared to traditional materials such as steel. The focus of this research is the use of Finite Element Method simulations for ballistics tests to assess the performance of glass fibre and epoxy matrix composite materials against Type I 38 Special Round Nose bullets with a velocity of 274 m/s and Type II 9 mm Full Metal Jacketed bullets with a velocity of 334 m/s, in accordance with National Institute of Justice standards. The results of this simulation will produce a visual representation in three-dimensional form using Finite Element Analysis software. Based on the results of the simulation, 48 layers of fiberglass/epoxy can absorb the kinetic energy of a Special RN bullet amounting to 165.0 Joules and transmit kinetic energy of 7.8 Joules. 80 layers of fiberglass/epoxy can absorb the kinetic energy of a 9mm FMJ bullet amounting to 216.7 Joules and transmit kinetic energy of 23.7 Joules. The damage occurring to the fiberglass/epoxy is brittle fracture. The deformation observed in the bullets in both simulations shows that the front part of the bullets undergoes deformation into a conical shape."

"Penambahan carbon black terhadap komposit epoksi/E-glass terbukti dapat menyerap gelombang elektromagnetik dengan lebih baik dibandingkan dengan komposit epoksi/E-glass, sehingga komposit epoksi/E-glass/carbon black dapat menjadi salah satu material penyerap gelombang elektromagnetik atau Radar Absorbent Material (RAM) untuk membuat teknologi siluman. Penelitian ini merupakan kelanjutan penelitian sebelumnya mengenai penyerapan gelombang elektromagnetik, yang bertujuan untuk mempelajari pengaruh carbon black terhadap sifat mekanik tarik dan tekuk pada komposit epoksi/E-glass/carbon black. Komposit dibuat dengan variasi carbon black (1 wt%, 3 wt%, dan 5 wt%) dan komposit epoksi/E-glass tanpa carbon black dan komposit ini difabrikasi menggunakan metode hand lay-up. Hasil pengujian menunjukkan nilai kuat tarik dan kuat tekuk tertinggi didapatkan pada komposisi carbon black 3 wt % dengan peningkatan sebesar 75,9 % untuk kuat tarik dan 9,73 % untuk kuat tekuk dibandingkan dengan kuat tarik dan kuat tekuk komposit epoksi/E-glass. Pengamatan permukaan patahan menggunakan Scanning Electron Microscope (SEM) menunjukkan ikatan antarmuka matriks dan serat tidak begitu kuat dengan moda kegagalan adalah fiber pull-out.

---

The addition of carbon black in the epoxy/E-glass composites has been proved to a better electromagnetic waves absorption than epoxy/E-glass composites. It indicates that epoxy/E-glass/carbon black composites is one of the Radar Absorbent Materials (RAM) for steath technology. This research is a continuation of the previous research about electromagnetic waves absorption on epoxy/E-glass/carbon black composites, with the research aim is to study the effect of carbon black on the tensile and flexural properties of epoxy/E-glass/carbon black composites. The composites were made with a variation of carbon black (1 wt%, 3 wt%, and 5 wt%) and epoxy/E-glass composites without carbon black. These composites were fabricated with a hand lay-up method.

The results showed that the maximum values of tensile and flexural strengths belong to the composites with the composition of carbon black 3 wt%, which were improved by 75.9 % for tensile strength and 9,73 % for flexural strength compared to tensile and flexural strengths of epoxy/E-glass composites. Scanning Electron Microscope (SEM) observation on the fracture surfaces showed that the matrix and fiber interface bonding was not very strong, which was indicated by fiber pull-out."

"Komposit sandwich merupakan komposit struktur yang diproduksi menjadi panel atau balok ringan yang memiliki sifat kekakuan dan kekuatan yang tinggi. Penelitian ini bertujuan untuk membandingkan sifat mekanik dan morfologi komposit sandwich kulit polyester berpenguat woven roving E glass dan inti honeycomb polypropylene yang difabrikasikan dengan teknik VARI dan adhesif cold-press. Pengujian mekanik yang dilakukan pada penelitian ini adalah uji lentur, uji tarik, dan uji tekan. Pengamatan morfologi pada sebelum dan sesudah pengujian dilakukan dengan menggunakan kamera. Hasil penelitian ini menunjukkan bahwa fabrikasi adhesif cold-press memiliki nilai kekuatan lentur, tarik, dan tekan yang lebih unggul dibandingkan dengan metode VARI yaitu masing-masing sebesar (24,93 ± 0,21) MPa, (0,52 ± 0,02) MPa, dan (1,95 ± 0,05) MPa. Setelah uji lentur, tarik, dan tekan, sampel mengalami kerusakan pada bagian inti.

---

Sandwich composites are structural composites that are manufactured into lightweight panels or beams with high stiffness and strength properties. This study aimed to compare the mechanical properties and morphological of polyester skin sandwich reinforced with woven roving E-glass reinforced polyester as skins and a polypropylene honeycomb core fabricated by the VARI and cold-press adhesive techniques. The mechanical tests which were flexural, tensile, and compressive tests were conducted. Morphological observations before and after testing were carried out using a camera. The results of this study indicated that the cold-press adhesive fabrication had superior flexural, tensile, and compressive strength values compared to the ones of VARI method, namely (24,93 ± 0,21) MPa, (0,52 ± 0,02) MPa, and (1,95 ± 0,05) MPa respectively. After bending, tensile, and compressive tests, all samples were failed in the core."