"ABSTRAKLatar Belakang: Dalam rongga mulut, komposit resin dapat menyerap sejumlah air yang dapat menyebabkan kelarutan. Penelitian ini bertujuan untuk menganalisis pengaruh perendaman dalam akuades terhadap penyerapan dan kelarutan komposit resin flowable nanofill dan flowable hybrid giomer. Metode: Jumlah spesimen 21 buah dari masing-masing komposit resin flowable nanofill Filtek Supreme Ultra Flowable Restorative dan flowable hybrid giomer Beautifil Flow Plus Giomer dibagi menjadi tiga kelompok perendaman yaitu 1 hari, 7 hari, dan 14 hari. Penyerapan dan kelarutan dihitung dengan menimbang berat spesimen sebelum dan setelah perendaman dalam akuades. Hasil: Terdapat perbedaan bermakna pada setiap kelompok perlakuan p.

---

ABSTRACTBackgorund In oral environment, resin composite can absorb amount of water which can lead to solubility. This study aims to analyze the effect of immersion in distilled water to sorption and solubility of flowable nanofill and flowable hybrid giomer resin composite. Methods Twenty two spesimens of each flowable nanofill Filtek Supreme Ultra Flowable Restorative and flowable hybrid giomer Beautifil Flow Plus Giomer were divided into three different immersion time, which were 1 day, 7 days, and 14 days. Sorption and solubility were calculated by weighing the spesimens before and after immersion in distillated water. Results There were significant differences between each groups p"

"ABSTRAKPenelitian ini bertujuan untuk menganalisis pengaruh perendaman dalam akuades terhadap kekasaran permukaan komposit resin flowable nanofill dan flowable hybrid giomer. Empat puluh dua spesimen dari komposit resin flowable nanofill Filtek Supreme Ultra Flowable Restorative n=21 dan flowable hybrid giomer Beautifil Flow Plus Giomer n=21 dibagi menjadi tiga kelompok perendaman: 1 hari,7 hari dan 14 hari. Nilai kekasaran permukaan sebelum dan sesudah perendaman diukur dengan surface roughness tester. Hasil menunjukkan bahwa terdapat perbedaan bermakna pada setiap kelompok perlakuan p0,05 . Disimpulkan perendaman 7 dan 14 hari dalam akuades dapat memengaruhi kekasaran permukaan komposit resin flowable nanofilled dan flowable hybrid giomer secara signifikan.

---

ABSTRACTThis study aims to analyze the effect of immersion in distilled water to surface roughness of flowable nanofill and flowable hybrid giomer resin composite. Fourty two specimens of flowable nanofill Filtek Supreme Ultra Flowable Restorative n 21 and flowable hybrid giomer Beautifil Flow Plus Giomer n 21 resin composite were divided into three different immersion time groups 1 day, 7 days and 14 days. The surface roughness was measured before and after immersion by surface roughness tester. The result showed that there were significant differences between each group p0.05 . It can be concluded that 7 and 14 days immersion in distilled water has significant effect on surface roughness of flowable nanofill and flowable hybrid giomer resin composite."

"Latar Belakang: Sifat mekanis material restorasi resin komposit sangat dipengaruhi komposisi material tersebut. Sifat mekanis tersebut juga dapat mengalami degradasi oleh cairan pada rongga mulut, termasuk makanan dan minuman seperti buah. Oleh sebab itu, pada penelitian ini dilakukan pengujian sifat mekanis kekuatan fleksural dari dua jenis resin komposit microhybrid setelah perendaman akuades dan larutan asam sitrat dengan konsentrasi buah sitrus yang umum dikonsumsi, yaitu jeruk mandarin dan jeruk lemon.Tujuan: Penelitian ini bertujuan untuk mengetahui perbedaan nilai kekuatan fleksural dua resin komposit microhybrid yaitu komposit tanpa Bis-GMA dan memiliki pre-polymerized filler (G-aenial PosteriorTM), serta komposit dengan Bis-GMA dan tanpa pre-polymerized filler (Filtek Z250TM), setelah penyimpanan kering dan perendaman akuades serta dua konsentrasi asam sitrat.Metode: Empat puluh spesimen microhybrid G-aenial PosteriorTM dan empat puluh spesimen Filtek Z250TM berbentuk balok berukuran 25 x 2 x 2 mm dibagi menjadi empat kelompok perlakuan, 1 hari penyimpanan kering, 30 hari perendaman akuades, 30 hari perendaman asam sitrat 0,06 mol/L (konsentrasi jeruk mandarin), dan 30 hari perendaman asam sitrat 0,30 mol/L (konsentrasi jeruk lemon). Spesimen di polimerisasi menggunakan LED curing unit irradiansi 700 mW/cm2 (LED Max Hilux) selama 20 detik. Spesimen diuji dengan Universal Testing Machine AGS-X (Shimadzu, Japan) 50 kgF dan 0,5 mm/menit untuk mendapatkan nilai kekuatan fleksural. Data dianalisis dengan uji statistik One-Way ANOVA dan Post-Hoc Tamhane.Hasil: Hasil uji statistik menunjukkan penurunan bermakna nilai kekuatan fleksural bahan G-aenial PosteriorTM dari nilai 86,32 ± 3,54 MPa pada 1 hari kering menjadi 70,14 ± 4,37 MPa setelah perendaman akuades, 71,58 ± 4,09 MPa setelah perendaman asam sitrat 0,06 mol/L, dan 71,01 ± 3,2 MPa setelah perendaman asam sitrat 0,30 mol/L, serta penurunan bermakna nilai kekuatan fleksural bahan Filtek Z250TM dari nilai 138,72 ± 6,26 MPa pada 1 hari kering menjadi 93,58 ± 7,69 MPa setelah perendaman akuades, 96,39 ± 3,15 MPa setelah perendaman asam sitrat 0,06 mol/L, dan 96,14 ± 5,39 setelah perendaman asam sitrat 0,30 mol/L. Antara kedua bahan microhybrid terdapat perbedaan nilai kekuatan fleksural bermakna pada masing-masing kelompok perlakuan, dengan nilai yang lebih besar bermakna pada Filtek Z250TM, namun Filtek Z250TM mengalami penurunan nilai kekuatan yang lebih besar dibandingkan G-aenial PosteriorTM. Pada masing-masing bahan microhybrid, tidak terdapat perbedaan nilai kekuatan fleksural yang signifikan antara kelompok perlakuan perendaman akuades, asam sitrat 0,06 mol/L dan asam sitrat 0,30 mol/LKesimpulan: Disimpulkan bahwa perendaman dalam akuades dan asam sitrat dapat mempengaruhi signifikan kekuatan fleksural kedua bahan komposit microhybrid.

---

Background: The mechanical properties of a resin composite restoration are affected by its composition. These mechanical properties can also be degraded by liquids in the oral environment, including food and drinks such as fruits. Therefore in this study, the mechanical property flexural strength of two different microhybrid composites are tested after immersion in distilled water, and citric acid solutions with concentrations of commonly consumed citrus fruits: mandarin orange and lemon.Objective: This study aims to observe the differences in flexural strength between two microhybrid composite resins after dry storage, and immersion in distilled water and citric acid. The first composite is without Bis-GMA and contains pre-polymerized fillers (G-aenial PosteriorTM), while the other one has Bis-GMA and doesn't contain pre-polymerized fillers (Filtek Z250TM).Methods: Forty G-aenial PosteriorTM and forty Filtek Z250TM 3-point bend test bar specimens are divided into four groups, 1 day dry storage, 30 days immersion in distilled water, 30 days immersion in 0.06 mol/L citric acid (mandarin orange concentration) and 30 days immersion in 0.30 mol/L citric acid (lemon concentration). The specimens are polymerized for 20 seconds using a 700 mW/cm2 irradiance LED curing unit (LED Max Hilux). Afterwards, the flexural strength of the specimens are measured with a Shimadzu, Japan AGS-X Universal Testing Machine (50 kgF, 0,5 mm/minute). Data was analyzed using a One-Way ANOVA statistical test and Tamhane Post Hoc.Result: Statistical analysis shows a significant reduction in the flexural strength of G-aenial PosteriorTM from a value of 86.32 ± 3.54 MPa after 1 dry storage, to 70.14 ± 4.37 MPa after immersion in distilled water, 71.58 ± 4.09 MPa after immersion in 0.06 mol/L citric acid, and 71.01 ± 3.2 MPa after immersion in 0.30 mol/L citric acid. Filtek Z250TM composite also showed a significant reduction in flexural strength from a value of 138.72 ± 6.26 MPa after 1 dry storage, to 93.58 ± 7.69 MPa after immersion in distilled water, 96.39 ± 3.15 MPa after immersion in 0.06 mol/L citric acid, and 96.14 ± 5.39 MPa after immersion in 0.30 mol/L citric acid. A significant difference of flexural strength is shown between the two microhybrid materials, in each of the treatment groups, with a significantly higher value for Filtek Z250TM, however Filtek Z250TM had a larger reduction in strength compared to G-aenial PosteriorTM. In each of the microhybrid composite types, there isn't a significant difference of flexural strength between the distilled water, 0.06 mol/L citric acid, and 0.30 mol/L citric acid immersion groups.Conclusion: It is concluded that immersion in water and citric acid has a significant effect on the flexural strength of the microhybrid composites."

"Latar Belakang : Studi ini mengevaluasi sifat mekanik kekuatan tekan dan sifat fisik morfologi permukaan Resin Komposit Bulk-fill Packable dengan Flowable. Kedua material ini memiliki kemampuan berpenetrasi cahaya hingga kedalaman 4 mm namun dengan viskositas yang berbeda. Keduanya memiliki kandungan monomer dan konsentrasi filler yang berbeda dimana hal tersebut mempengaruhi sifat mekanik dan fisiknya. Tujuan : Mengetahui perbandingan kekuatan tekan Resin Komposit Bulk-fill Packable dengan Flowable, serta hubungannya dengan morfologi permukaan. Metode : 12 spesimen Resin Komposit Bulk-fill Packable dan Flowable disiapkan untuk uji kekuatan tekan lalu dianalisis dengan uji Independent T-test. Kemudian spesimen Resin Komposit Bulk-fill Packable dan Flowable disiapkan untuk analisis morfologi permukaan menggunakan SEM. Hasil Penelitian : Tidak terdapat perbedaan bermakna nilai kekuatan tekan antara Resin Komposit Bulk-fill Packable dan Flowable dengan nilai kekuatan tekan RK Bulk-fill Packable lebih tinggi dibandingkan dengan Flowable. Resin Komposit Bulk-fill Packable memiliki permukaan eksternal yang lebih tidak beraturan, ukuran partikel yang beragam, dan lebih banyak porus. Kesimpulan : Resin Komposit Bulk-fill Packable menunjukkan nilai kekuatan tekan yang sama dengan Resin Komposit Bulk-fill Flowable. Material RK Bulk-fill Packable memiliki morfologi permukaan yang tidak beraturan, lebih banyak porus, dan ukuran partikel yang lebih beragam dibandingkan dengan RK Bulk-fill Flowable.

---

Background : This study evaluates the compressive strength and surface morphology of the Resin Composite Bulk-fill Packable and Flowable. Both of these materials have the ability to penetrate light to a depth of 4 mm but with different viscosities. Each Resin Composite Bulk-fill have different monomer content and filler concentrations which affect their mechanical and physical properties.

Objective : Knowing the comparison of the compressive strength of Resin Composite Bulk-fill Packable with Flowable, and its relationship with surface morphology. Methods : 12 specimens of Resin Composite Bulk-fill Packable and Flowable were prepared for compressive strength test and then analyzed by Independent T-test. Then specimens of Resin Composite Bulk-fill Packable and Flowable were prepared for surface morphology analysis using SEM.

Results : There was no significant difference in the compressive strength values between Resin Composite Bulk-fill Packable and Flowable with the compressive strength of Resin Composite Bulk-fill Packable being higher than Flowable. Resin Composite Bulk-fill Packable have a more irregular external surface, a variety of particle sizes, and are more porous.

Conclusion : Resin Composite Bulk-fill Packable shows the same compressive strength value as Resin Composite Bulk-fill Flowable. The Resin Composite Bulk-fill Packable material has an irregular surface morphology, more voids, and more diverse particle size compared to Resin Composite Bulk-fill Flowable."

"Latar Belakang : Resin komposit menjadi salah satu jenis material restorasi yang banyak digunakan karena memiliki keunggulan dalam sifat fisik, mekanik, dan estetika. Salah satu resin komposit yang beredar di Indonesia adalah Resin Komposit Palfique Supra-Nano Universal Flow yang dikembangkan partikel filler-nya dan diklaim memiliki sifat fisik yang baik antara lain water sorption dan solubility. Penggunaan resin komposit seiring waktu akan terpapar oleh lingkungan rongga mulut akibat adanya saliva yang pH-nya bisa berubah seiring konsumsi makanan dan minuman sehingga mempengaruhi water sorption dan solubility-nya. Hingga saat ini, belum terdapat penelitian mengenai pengaruh perendaman pada berbagai pH saliva buatan terhadap water sorption dan solubility Resin Komposit Palfique Supra-nano Universal Flow. Tujuan : Menganalisis pengaruh perendaman Resin Komposit Supra-Nano Palfique Universal Flow tipe Super Low dan Medium pada berbagai pH saliva buatan terhadap water sorption dan solubility. Metode : Empat puluh delapan spesimen Resin Komposit Supra-Nano Palfique Universal Flow tipe Super Low dan Medium dengan dimensi 15 x 1 mm dibagi menjadi delapan kelompok uji berdasarkan tipe dan perendaman, yaitu pada perendaman di dalam akuades, saliva buatan pH 3, 5,5, dan 7 masing-masing selama 7 hari. Perhitungan dari nilai water sorption dan solubility dilakukan sesuai ISO 4049 : 2019. Analisis data menggunakan uji One way ANOVA dan Kruskall Wallis. Hasil : Nilai water sorption dan solubility pada kedua tipe Resin Komposit Palfique Supra-nano Universal Flow semakin tinggi pada perendaman pH yang semakin rendah. Perendaman di dalam akuades dan saliva buatan pH 3 mengalami kenaikan secara signifikan (p<0,05), dan tidak signifikan pada perendaman di dalam saliva buatan pH 3 dengan pH 5,5 dan pH 7 (p<0,05). Nilai solubility pada perendaman di dalam saliva buatan pH 3 dengan pH 5,5 mengalami kenaikan secara signifikan (p<0,05), sedangkan pada saliva buatan pH 5,5 dengan 7 tidak signifikan (p>0,05). Tipe Super Low memiliki nilai water sorption dan solubility yang lebih tinggi dibandingkan tipe Medium pada semua perendaman namun tidak signifikan (p>0,05). Kesimpulan : Terjadi peningkatan nilai water sorption dan solubility Resin Komposit Palfique Supra-nano Universal Flow setelah perendaman di dalam saliva buatan pH 3 dibandingkan pH 5,5, 7, dan akuades.

---

Background : Composite resin is one type of restoration material that is widely used because it has advantages in physical, mechanical, and aesthetic properties. One of the composite resins distributed in Indonesia is Palfique Supra-nano Universal Flow Composite Resin which developed its filler particles and claimed to have good physical and mechanical properties, one of which is the physical properties of water sorption and solubility. The use of composite resins over time will be exposed to the oral environment due to the presence of saliva which pH of saliva can change with the consumption of food and drinks, that affecting the water sorption and solubility of the Composite Resin. Until now, there’s not yet research the effect of immersion at various pH artificial saliva on water sorption and solubility of Palfique Supra-nano Universal Flow Composite Resin. Objective : To analyze the effect of immersion type Super Low and Medium Palfique Supra-Nano Universal Flow Composite Resin at various pH artificial saliva on water sorption and solubilty. Methods : Forty-eight type Super Low and Medium Palfique Supra-Nano Universal Flow Composite Resin specimens with dimensions of 15 x 1 mm were divided into eight test groups based on type and immersion ; distilled water, artificial saliva pH 3, 5,5, and 7 for 7 days. Calculations of water sorption and solubility values will be made according to ISO 4049: 2019. Data analysis used One way ANOVA and Kruskall Wallis test. Results : The value of water sorption and solubility for both types (Super Low and Medium) is higher in immersion at lower pH. Immersion in distilled water and artificial saliva pH 3 in both types increased significantly (p<0.05), and in artificial saliva pH 3 with pH 5.5 and pH 7 was not significant (p<0.05). The solubility value in pH 3 immersion with pH 5.5 increased significantly (p<0.05), while at pH 5.5 and 7 it was not significant (p>0.05). The Super Low type has higher water sorption and solubility values than the Medium type in all immersions but not significant (p>0.05). Conclusion : There is an increase on water sorption and solubility of Palfique Supra-nano Universal Flow Composite Resin after immersion at artificial pH 3 compared to pH 5,5, 7, and distilled water."

"Tujuan :Penelitian bertujuan untuk mengetahui pengaruh aplikasi gel acidulatedphosphate fluoride terhadap perubahan warna material restoratif resin komposit bulk-fillflowable yang direndam dalam larutan kopi. Metode penelitian: Dua puluh spesimenresin komposit bulk-fill flowable berbentuk silinder berdiameter 6 mm dengan tebal 2 mmdisiapkan kemudian dibagi menjadi 2 kelompok, dengan salah satu kelompok menerimaaplikasi gel APF dan kelompok lainnya tidak. Setelah diberikan aplikasi gel, spesimenkemudian direndam di dalam larutan kopi (37oC) selama 7 hari. Pengukuran warnadilakukan dengan colorimeter pada saat sebelum perlakuan, setelah aplikasi gel APF dansetelah perendaman di dalam larutan kopi, kemudian dihitung nilai perubahan warnanyasesusai sistem CIE Lab. Analisis data menggunakan uji statistik Independent T-Testuntuk menilai perbedaan perubahan warna antara kelompok dengan dan tanpa aplikasigel APF. Hasil: Hasil menujukkan kelompok yang menerima gel APF mengalamiperubahan warna yang lebih besar (p>0.05) daripada kelompok tanpa gel APF.Kesimpulan : Dari hasil penelitian, disimpulkan bahwa aplikasi gel APF memilikipengaruh terhadap perubahan warna pada resin komposit bulk-fill flowable

---

Objective: The aim of this study was to determine the effect of application of

acidulated phosphate fluoride gel on the color change of bulk-fill flowable composite

resin restorative material immersed in coffee. Methods: Twenty specimens of bulk-fill

flowable composite resin in the form of cylinders 6 mm in diameter and 2 mm in thickness

were prepared and then divided into 2 groups, with one group receiving APF gel

application and the other group not. After being given the gel application, the specimens

were then immersed in a coffee solution (37oC) for 7 days. Color measurement was

carried out with a colorimeter before treatment, after application of APF gel and after

immersion in coffee solution, then the value of the color change was calculated according

to the CIE Lab system. Data was analyzed using the independent T-Test statistical test to

assess differences in color change between groups with and without APF gel application.

Results: The results showed that the group that received the APF gel had a greater color

change (p> 0.05) than the group without APF gel application. Conclusion: From the

results of the study, it was concluded that the application of APF gel had an effect on the

color change of the flowable bulk-fill composite resin."

"Penelitian ini bertujuan untuk mengetahui pengaruh lama perendaman dalam saliva buatan terhadap perubahan pH-nya dan kekasaran permukaan resin komposit Giomer Bulk-Fill. Jumlah spesimen 63 buah dibagi dalam sembilan kelompok perlakuan yaitu perendaman dalam saliva buatan pH 7; 5,5; dan 4,5 selama masing-masing 1 jam, 24 jam, dan 72 jam pada suhu 370C. Perubahan pH saliva buatan diukur menggunakan pH meter dan pengujian kekasaran permukaan spesimen menggunakan surface roughness tester. Hasil menunjukkan bahwa terdapat perbedaan yang bermakna pada setiap kelompok perlakuan.

---

This study aimed to determine the effect of immersion time on artificial saliva pH changes and surface roughness of Giomer Bulk Fill composite resin. Sixty three specimens were divided into nine groups with immersion in artificial saliva pH 7, 5.5, and 4.5 for 1 hour, 24 hours, and 72 hours at 370C respectively. The changes in artificial saliva pH were measured using a pH meter and the surface roughness measured using surface roughness tester. The results showed that there were significant differences between each groups."

"Latar belakang: Gel acidulated phosphate fluoride merupakan salah satu material preventif yang umum digunakan dan berpotensi untuk berkontak dengan material restoratif, salah satunya adalah material restoratif resin komposit yang cukup baru yaitu resin komposit bulk-fill flowable.Tujuan: Penelitian ini bertujuan untuk melihat pengaruh aplikasi gel acidulated phosphate fluoride (APF) terhadap perubahan warna resin komposit bulk-fill flowable. Metode: Sample resin komposit bulkfill-flowable berbentuk silinder berdiameter 6 mm dengan tebal 2 mm. Digunakan dua puluh spesimen dibagi menjadi dua kelompok dengan perlakuan aplikasi gel APF pada salah satu kelompok. Setelah diberikan aplikasi gel, spesimen kemudian direndam dengan larutan anggur merah selama 7 hari untuk melihat perubahan warnanya. Pengukuran warna dilakukan sebanyak 3 kali, setelah pembuatan sampel, setelah aplikasi gel APF dan setelah perendaman dengan larutan anggur merah. Analisis data menggunakan SPSS uji Independent T-Test.Hasil: Hasil penelitian dan uji analisis menunjukan terjadi perubahan warna lebih besar pada kelompok dengan aplikasi gel APF (p>0.05) dibandingkan kelompok yang tidak menerima aplikasi gel APF.Kesimpulan: Dapat disimpulkan bahwa aplikasi gel APF tidak memiliki pengaruh signifikan terhadap perubahan warna pada resin komposit bulk-fill flowable setelah direndam dalam larutan anggur merah

---

Background: Acidulated phosphate fluoride gel is one of the preventive materials commonly used in preventing caries in high-risk patients. Its applications have the potential to come into contact with restorative materials, one of which is a relatively new composite resin restorative material that is bulk-fill flowable composite resin.

Objective: This study aims to analyze the colour change of bulk-fill composite resin treated with acidulated phosphate fluoride gel in red wine immersion.

Research method: Twenty cylindrical specimens with 6 mm in diameter and 2 mm in thickness divided into two groups of ten, one of the group were treated with APF gel for 30 minutes, then all groups were immersed in red wine solutions for 7 days. The colour of the specimens was measured using colorimeter after cleaned using an ultrasonic cleaner. The colours of specimens were documented in CIE L*a*b* system. To determine the influence of APF, the colour differences of the two groups were compared using independent T-test analysis.

Result: The result statistically showed no significant colour change difference (p>0.05) between the two groups.

Conclusion: APF application had insignificant effect on the discolouration of bulk-fill flowable composite resin when immersed in red wine solution"

"Kebocoran mikro resin komposit proksimal seringkali terjadi pada dinding gingiva. Tujuan studi ini mengevaluasi efek komposit flowable sebagai lapisan antara untuk mengurangi kebocoran mikro pada dinding ginigva. Metode: 30 gigi premolar RA dipreparasi berbentuk boks, restorasi dilakukan pada kelompok 1 dengan resin komposit packable saja (kontrol). Kelompok 2 dengan RK flowable sebagai lapisan antara, setebal 1 mm dan komposit packable di atasnya. Kelompok 3, seperti kelompok 2 namun RK flowable sebagai lapisan antara setebal 2 mm. Setelah dilakukan siklus termal, kebocoran mikro diukur dari penetrasi zat warna metilen biru 1%. Analisis statistik dengan uji Kolmogorov-smirnov. Hasil: Kebocoran mikro pada kelompok 1 berbeda bermakna dengan kelompok 2 dan 3. Namun tidak terdapat perbedaan bermakna pada kelompok 2 dan 3 (p<0.05). Kesimpulan : Tingkat kebocoran mikro dinding gingiva paling sedikit pada restorasi RK proksimal dengan aplikasi RK flowable pengganti dentin setebal 1 mm namun, ketebalannya tidak memiliki pengaruh terhadap tingkat kebocoran mikro secara statistik.

---

Microleakage of composite restoration in proximal often occurs on gingival wall. The purpose of this study is to evaluate the influence of flowable composite as intermediate layer to reduce microleakage on gingival wall. Materials and Method: Thirty whole-extracted upper premolars were devided into 3 groups. Within a box-like cavities, the first group is restored with packable composite only. Group 2 were restored with flowable composite with 1 mm thickness then restored with incrementally packable composite. Group 3 were restored like group two with flowable composite thickness were 2mm. After thermocycling, the penetration of 1% methylene blue was investigated along the gingival wall. The data were analyzed with Kolmogorov-smirnov test. Results: There were significant difference between group 1 with group 2 and 3. No significant difference found between Group 2 and Group 3. Conclusion: Flowable composite as intermediate layer has influence in reducing the microleakage of gingival wall on proximal composite restoration. Nonetheless the thickness of flowable composite has no influence."

"Latar Belakang: Resin komposit Giomer Bulk-Fill merupakan resin komposit yang dapat ditumpat hingga ketebalan 4 mm dan dapat melepas ion fluor. Resin komposit ini juga menjadi buffer asam ketika tingkat pH saliva turun dan mengembalikan ke pH netral. Namun, kenaikan pH diikuti dengan penurunan sifat fisik dari material. Belum diketahui apakah terdapat pengaruh terhadap kekerasan permukaan setelah material ini melepas fluor dan perubahan pH saliva.Tujuan: Untuk mengetahui pengaruh perbedaan pH saliva buatan dan lama perendaman terhadap kekerasan permukaan resin komposit Giomer Bulk-Fill.Metode: Penelitian eksperimental laboratorik menggunakan sembilan puluh spesimen resin komposit Giomer Bulk-Fill berdiameter 6 mm dan tinggi 3 mm dibagi menjadi 9 kelompok perendaman yaitu dengan saliva buatan pH 7 (kontrol); pH 5,5; pH 4,5 dengan lama perendaman 1 jam, 24 jam, dan 72 jam yang disimpan dalam inkubator dengan suhu 37°C. Uji kekerasan menggunakan Knoop Microhardness Tester (Shimadzu HMV-G21DT, Jepang).Hasil: Berdasarkan hasil uji statistik One-way ANOVA terdapat perbedaan bermakna (p<0,05) antara kelompok perendaman dalam saliva buatan pH 4,5 dengan kelompok perendaman dalam saliva buatan pH 5,5 dan kelompok perendaman dalam saliva buatan pH 4,5 dengan kelompok perendaman dalam saliva buatan pH 7 yang dilakukan perendaman selama 72 jam. Nilai kekerasan pada perendaman dengan saliva buatan pH 4,5 dan lama perendaman 1 jam, 24 jam, dan 72 jam beruturut-turut sebesar 35,9±2,40 KHN, 33,75±2,98 KHN, dan 32,7±2,71 KHN. Sementara itu, nilai kekerasan dengan saliva buatan pH 5,5 dan lama perendaman 1 jam, 24 jam, dan 72 jam beruturt-turut sebesar 38,92±2,96 KHN, 37,00±1,82 KHN, dan 38,6±3,42 KHN. Dengan larutan saliva buatan pH 7 dan lama perendaman 1 jam, 24 jam, dan 72 jam didapatkan nilai kekerasan berturut-turut adalah 37,01±2,21 KHN, 37,05±1,79 KHN dan 37,72±2,51 KHN.Kesimpulan: Lama perendaman dan tingkat keasaman dalam saliva buatan dapat menurunkan nilai kekerasan permukaan resin komposit Giomer Bulk-Fill.

---

Introduction: Composite resin Giomer Bulk-Fill is a material for restoration that can be placed in single increment with depth until 4 mm and release fluoride ion. This composite resin can be an acidic buffer when pH saliva drops and turns it back to pH neutral. However, the physical properties of the material are decreased. It is unknown if there any change of surface hardness of the material due to fluoride ion release and changes in pH saliva.

Objective: This study aimed to determine the effect of immersion time and different pH levels of artificial saliva on surface microhardness of composite resin Giomer Bulk-Fill.

Methods: Laboratory experimental research using ninety specimens of resin composite Giomer Bulk-Fill and divided into nine groups with immersion in artificial saliva pH 7 (control); 5,5; and 4,5 for 1, 24, and 72 hours at 37°C respectively and tested using Knoop Microhardness Tester (Shimadzu HMV-G21DT, Japan).

Result: The statistical test using One-way ANOVA showed that there were significant differences (p<0,05) between group of immersion in artificial saliva pH 4,5 compared to group of immersion in artificial saliva pH 5,5 and group of immersion in artificial saliva pH 5,5 compared to group of immersion in artificial saliva pH 7 for 72 hours of immersion. The result showed that the hardness number of the groups immersed in artificial saliva pH 4,5 for 1 hour, 24 hours, and 72 hours respectively are 35,9±2,40 KHN, 33,75±2,98 KHN, and 32,7±2,71 KHN. Meanwhile, the hardness number of the groups immersed in artificial saliva pH 5,5 for 1 hour, 24 hours, and 72 hours respectively 38,92±2,96 KHN, 37,00±1,82 KHN, and 38,6±3,42 KHN. The hardness number of the groups immersed in aritificial saliva of pH 7 for 1 hours, 24 hours, and 72 hours are 37,01±2,21 KHN, 37,05±1,79 KHN dan 37,72±2,51 KHN.

Conclusion: Different immersion times and pH levels decrease surface microhardness of Giomer Bulk-Fill composite resin."