Wilujeng Laksmi
Sifat penyerapan gelombang mikro pada material La0,8Ca0,2-xAgxMnO3 (x= 0; 0,05; 0,10; 0,15) yang disintesis menggunakan metode sol-gel = Microwave absorption property of La0,8Ca0,2-xAgxMnO3 (x= 0; 0,05; 0,10; 0,15) material synthesized by sol gel method
"Telah dilakukan penelitian mengenai sifat penyerapan gelombang mikro material La0.8Ca0.2-xAgxMnO3 x= 0;0,05;0.1;0,15 yang termasuk golongan material perovskit manganat. Material disintesis menggunakan metode sol gel, kemudian dilakukan kalsinasi pada suhu 550?C, dan sintering di suhu 900?C. Karakterisasi XRD menunjukkan bahwa sampel berada dalam fasa tunggal. Dilakukan uji SEM yang menunjukkan morfologi sampel serta EDX yang menampilkan kemurnian sampel.
Pengujian menggunakan magnetometer kriogenik menunjukkan penurunan resistivitas bahan. Sampel telah dikonfirmasi ulang menggunakan uji ESR, untuk melihat konsenterasi elektron bebas pada sampel. Terakhir, sampel diuji menggunakan VNA untuk mengetahui Refleksi hilang, permittivitas dan permeabilitas bahan, dengan RL paling tinggi sebesar -4,965 dB.Kata kunci: Perovskit manganat, Sol Gel, Refleksi Hilang, Permitivitas, Permeabilitas.
The research about microwave absorption property of La0.8Ca0.2 xAgxMnO3 x 0 0.05 0.10 0.15 material is reported. The material synthesized by sol gel method, calcinated at 550 C and sintered at 900 C. According to XRD characterization, all samples were single phase. By SEM characterization the morphology of the samples are reported. EDX confirmed that all the samples have a good compositional purity.
Cryogenic magnetometer reported that Ag dopant caused the resistivity of materials generally decreased. ESR confirmed that Ag dopant also caused concentration of free electrons were increase. Finally VNA characterization reported the Reflection Loss, permittivity, and permeability, which the maximum RL is 4.965 dB."
Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2017
S67715
UI - Skripsi Membership  Universitas Indonesia Library
cover
Ryka Usnilawaty
Pengaruh Substitusi Fe di situs Mn terhadap Penyerapan Gelombang Mikro (Rentang Pita X) Pada Sistem Material La0.7Ba0.3Mn(1-x)FexO3 (x = 0; 0,1; 0,2; 0,25) disintesis dengan Metode Sol-Gel = Effect of Fe Substitution at the Mn-site on Microwave Absorption (X-Band) in La0.7Ba0.3Mn(1-x)FexO3 (x = 0, 0.1, 0.2, 0.25) Material System Synthesized by Sol-Gel Method
"Material penyerap gelombang mikro saat ini banyak dikembangkan untuk aplikasi di bidang pertahanan militer, komunikasi, dan elektronik. Fungsi material penyerap gelombang mikro ini dapat menjadi material anti radar yaitu pelindung/penghalang dari sistem radar. Kriteria material yang dapat digunakan sebagai penyerap gelombang mikro diantaranya memiliki karakteristik permeabilitas dan permitivitas. Material yang potensial digunakan dan banyak dikembangkan saat ini adalah material perovskit oksida sistem ABO3. Pengembangan material perovskit oksida yang dilakukan pada penelitian ini bertujuan untuk mendapatkan nilai penyerapan yang tinggi dan memperluas daerah penyerapan. Polikristalin La0,7Ba0,3Mn(1-x)FexO3 (x=0; 0,1; 0,2; 0,25) telah berhasil disintesis dengan metode sol-gel, dengan bahan dasar La2O3, Ba(NO3)2, Mn(NO3)2.4H2O, dan Fe2O3. Setelah sintesis sol-gel, sampel dipanaskan dengan suhu 180oC selama 2,5 jam. Kalsinasi dilakukan pada suhu 800oC selama 2 jam. Kemudian sampel dikompaksi dengan tekanan 10 ton, lalu sampel disintering pada suhu 900oC selama 2 jam. Hasil refinement pola difraksi sinar-x menunjukkan bahwa material La0,7Ba0,3Mn(1-x)FexO3 (x=0; 0,1; 0,2; 0,25) memiliki struktur kristal rhombohedral, dengan ukuran kristalit 53,92nm; 37,73nm; 29,7nm; dan 26,3nm. Penambahan Fe di situs Mn pada material lantanum barium manganit oksida mampu memperbanyak daerah penyerapan gelombang mikro. Komposisi yang memiliki kinerja terbaik pada penyerapan gelombang mikro adalah La0,7Ba0,3Mn0,75Fe0,25O3. Hasil pengujian serapan gelombang mikro pada rentang 7-13 GHz terdapat dua frekuensi puncak serapan pada 10 GHz sebesar -6,26 dB dan 12 GHz sebesar -4,6 dB.
Microwave absorber materials are currently being developed for applications in the fields of military defense, telecommunications, and electronics. The microwave absorber material can be an anti radar material for radar shielding. Permeability and permittivity characteristics are the criteria for microwave absorbing materials. Perovskite oxide of the system material ABO3 is currently being developed as the potential microwave absorber material. The goal of this research’s development in perovskite oxide materials is to increase the absorption area and expand absorption area. Polycrystalline La0.7Ba0.3Mn(1- x)FexO3 (x=0, 0.1, 0.2, 0.25) has been successfully synthesized using the sol-gel method, with the basic ingredients high purity La2O3, Ba(NO3)2, Mn(NO3)2.4H2O, and Fe2O3. After the sol-gel process has completeted, the sample was heated at 180oC for 2.5 hours. Calcination was carried out at 800oC for 2 hours. Then the sample was compressed with a pressure of 10 tons, then the sample was sintered at a temperature of 900oC for 2 hours. The results of the refinement of the x-ray diffraction pattern show that the La0.7Ba0.3Mn(1- x)FexO3 (x=0, 0.1, 0.2, 0.25) material has a rhombohedral crystal structure, with a crystallite size of 53.92nm; 37.73nm; 29.7nm; and 26.3nm. The addition of Fe at the Mn site in the lanthanum barium manganite oxide material can increase the microwave absorption area. La0.7Ba0.3Mn0.75Fe0.25O3 is the composition with the best microwave absorption performance. The microwave absorbing properties in the frequency range 7- 13 GHz revealed two peak absorption frequencies at 10 GHz of -6.26 dB and 12 GHz of -4.6 dB."
Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2024
T-pdf
UI - Tesis Membership  Universitas Indonesia Library
cover
Indah Fauziyah
Pengaruh doping nikel terhadap sifat penyerap gelombang mikro pada senyawa La0,67Sr0,33Mn(1-x)NixO3 yang disintesis dengan metode sol-gel = The effect of nickel doping on microwave absorption properties of La0,67Sr0,33Mn(1-x)NixO3compound synthesized by sol-gel method
"Telah dilakukan penelitian mengenai pengaruh doping nikel terhadap sifat penyerap gelombang mikro pada senyawa La0,67Sr0,33Mn 1-x NixO3 yang disintesis dengan Metode Sol-gel. Karakterisasi XRD menunjukkan bahwa La0,67Sr0,33Mn 1-x NixO3 memiliki fasa tunggal dengan struktur kristal rhombohedral. Dari hasil SEM-EDX terlihat bahwa ukuran partikel cenderung mengecil dan tidak ada unsur lain impuritas pada material. Pengujian dengan menggunakan Cryogenic Magnetometer menunjukan nilai resistivitas terbesar yaitu 1.49 ?m untuk x = 0,3. Hasil karakterisasi VNA menunjukan doping Ni dapat meningkatkan kemampuan penyerapan gelombang mikro. Nilai Reflection Loss terbesar yaitu -11,492 dB untuk x = 0,3<.
A research on the effect of nickel doping on microwave absorption properties of La0,67Sr0,33Mn1 xNixO3 had been reported. The samples were synthesized by the sol gel method. The XRD characterization shows that La0,67Sr0,33Mn 1 x NixO3 had a single phase with a rhombohedral crystal structure. SEM EDX results show that there is no other element besides main elements and particle size decrease after doping Ni. Cryogenic Magnetometer showed that the resistivity increase after incoporation of Ni, the largest resistivity is 1,49 for x 0,3. The VNA characterization showed that after doping Ni The microwave absorption properties had been significantly improved. The largest Reflection Loss value is 11.49 dB for x 0,3<."
Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2017
S67345
UI - Skripsi Membership  Universitas Indonesia Library
cover
Utami Widyaiswari
Studi sifat kelistrikan dan kemagnetan serta efek magnetoresistan material La0,67Sr0,33Mn1-xnixO3 yang disintesis dengan metode sol gel = Study of electrical properties magnetic properties and magnetoresistance effect of La0 67Sr0 33Mn1 xnixO3 material synthesized by sol gel method / Utami Widyaiswari
"Telah dilakukan penelitian sifat listrik, sifat magnet, dan efek magnetoresistan bahan perovskite manganites La0,67Sr0,33Mn1-XNixO3. Sampel dibuat dengan metode sol gel. Hasil karakterisasi XRD menunjukkan bahwa sampel sudah memiliki fase tunggal dengan struktur rhombohedral dan space group R-3c. Pemberian doping Ni tidak mengubah struktur kristal namun menurunkan nilai parameter kisi kristal. Karakterisasi SEM-EDX menunjukkan bahwa unsur Ni sudah masuk ke dalam sampel dan adanya perubahan morfologi sampel ketika doping Ni divariasikan.
Data resistivitas sebagai fungsi temperatur menunjukkan bahwa doping Ni meningkatkan besar resistivitas bahan dan menggeser temperatur transisi metal-isolator ke temperatur yang lebih rendah. Efek magnetoresistan yang diberikan menunjukkan adanya peningkatan persen magnetoresistan saat doping Ni dinaikkan. Sedangkan kurva histerisis yang dihasilkan menunjukkan bahwa pemberian doping Ni menurunkan sifat kemagnetan bahan yang ditunjukkan oleh penurunan magnetisasi bahan.
The electrical properties, magnetic properties, and magnetoresistance effect of perovskite manganites La0,67Sr0,33Mn1-XNixO3 material have been studied. Samples were synthesized by using sol gel method. The result of XRD characterization showed that samples were single phase with Rhombohedral structure and R-3c space group. Ni doped did not change crystal structure but decreased lattice parameter. SEM-EDX characterization showed that Ni was included in the samples as a doping and the morphology of samples changed with various Ni doped.
Resistivity as temperature function showed that Ni doped increased the resistivity and decreased the metal-insulator transition temperature. Magnetoresistance effect of samples relatively enhanced with increased of Ni doping. While the hysteresis curve from VSM characterization showed that Ni doped decreased magnetic properties of samples."
Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2016
T46340
UI - Tesis Membership  Universitas Indonesia Library
cover
Santi Dewi Rosanti
Pengaruh doping Ag terhadap magnetoresistan bahan pada material (La1-xAgx)0,8Ca0,2MnO3 disintesis dengan metode sol gel = Pengaruh doping Ag terhadap magnetoresistan bahan pada material (La1-xAgx)0,8Ca0,2MnO3 disintesis dengan metode sol gel / Santi Dewi Rosanti
"Telah dilakukan sintesis bahan perovskite manganites La1-xAgx 0,8Ca0,2MnO3 yang disubtitusi dengan Ag pada site La dengan x = 0; 0,03; 0,07; 0,1; 0,2; 0,3; 04 dan 0,5. Pembuatan sampel dilakukan dengan metode sol-gel pada temperatur sintering 900 C. Prekursor yang digunakan adalah La2O3, AgNO3, Ca NO3 2.6H2O dan Mn NO3 2.4H2O. Hasil karakterisasi XRD untuk x < 0,1 menunjukkan fasa tunggal dengan struktur kristal orthorombik dan space group pnma. Pada x = 0,2; 0,3 dan 0,4 terdapat puncak Ag dan x = 0,5 terdapat puncak Ag, Ca dan nitrat. Pengujian nilai efek magnetoresistan di fokuskan pada x < 0,1. Ukuran rata-rata grain dari hasil karakterisasi SEM pada sampel yaitu dalam skala nanometer.
Hasil kemurnian sampel telah dikonfirmasi menggunakan karektersasi EDX, dimana tidak terdapat pengotor atau impuritas. Hasil karakterisasi VSM menunjukkan bahwa nilai koersivitas semakin meningkat dengan meningkatnya doping Ag, nilai tertinggi HC = 234 Oe dengan sifat soft magnetik. Nilai optimum MR = 61,5 pada x = 0,07, temperatur 50 K di bawah pengaruh medan magnet luar sebesar 2T.
The synthesis of perovskite manganites La1 xAgx 0.8Ca0,2MnO3 was substituted with Ag on La site with x 0 0.03 0.07 0.1 0.2 0.3 04 and 0.5. Sample preparation was done by sol gel method at sintering temperature 900 C. The precursors are La2O3, AgNO3, Ca NO3 2.6H2O and Mn NO3 2.4H2O. The XRD characterization results for x 0.1 showed a single phase with orthorombic crystal structure and pnma space group. There is Ag peak at x 0.2 0.3 and 0.4 and at x 0.5 there are Ag and Ca peaks. The magnetoresistance effect value test was focused on x 0.1. The average size of grain from SEM characterization results in the sample is in the nanometer scale.
The results of the purity of the sample have comfirmed using EDX characterization. VSM characterization results showed that coercivity value increases with increasing Ag doping, the highest value of Hc 234 Oe with soft magnetic properties. The optimum value of MR 61,5 at x 0.07, temperature 50 K under the influence of the external magnetic field of 2T."
Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2018
T49120
UI - Tesis Membership  Universitas Indonesia Library
cover
Rina Kamila
Pengaruh doping silver (Ag) terhadap sifat listrik dan efek magnetoresistansi material La0,8-xAgxCaO,2MnO3 (x = 0; 0,05; 0,1; 0,15) dengan metode sol-gel = The effect of silver ag doping on electrical property and magnetoresistance La0,8-xAgxCaO,2MnO3 (x = 0; 0,05; 0,1; 0,15) material by sol gel method
"Telah dilakukan penelitian pengaruh doping Ag terhadap sifat listrik dan efek magnetoresistansi material La0,8-xAgxCa0,2MnO3 x = 0; 0,05; 0,1; 0,15. Material disintesis dengan metode sol-gel dan disintering pada temperatur 900 oC selama 24 jam. Material lanthanum manganit telah banyak diteliti karena memiliki sifat-sifat yang menarik, baik dalam segi struktural, sifat listrik, serta sifat magnet nya.
Struktur material dikarakterisasi menggunakan Difraksi Sinar-X XRD dan menunjukkan bahwa pada doping x = 0 dan 0,05, material memiliki fase tunggal single phase yaitu fase manganite, sedangkan pada doping x = 0,1 dan 0,15, material terdiri dari fasa campuran, yaitu fasa manganite dan Ag. Scanning Electron Microscopy SEM digunakan untuk observasi morfologi serta menunjukkan kehomogenan material. Dengan doping Ag, ukuran grain boundary dari material membesar.
Hasil karakterisasi dari Electron Dispersive Spectroscopy EDS mengkonfirmasi keberadaan unsur Ag pada material. Karakterisasi menggunakan Cryogenic Magnetometer dilakukan untuk menguji sifat listrik dari material seiring dengan peningkatan doping Ag. Seiring dengan peningkatan konsentrasi doping Ag, resistivitas material mengecil serta temperatur transisi metal-isolator TMI bergeser kearah temperatur ruang. Efek magnetoresistansi menurun saat doping x = 0,05 dan meningkat kembali saat x = 0,1 dan 0,15.
The research about effect of dopant Ag on electrical and magnetoresistance properties of La0,8 xAgxCa0,2MnO3 x 0 0,05 0,1 0,15 has been done. The materials were synthesized via sol gel method, sintered at temperature 900oC for 24 hours. Lanthanum manganite material has been widely investigated because its interesting properties, such as physical, electrical, and magnetic properties.
The structural of the materials were characterized using X Ray Diffraction XRD, show in doping x 0 and 0,05, material has single phase manganite phase, whereas in doping x 0,1 and 0,15, material consists of mixed phases, manganite and Ag phases. Scanning Electron Microscopy SEM was used to observe morphology of the materials and showed homogeneity of the materials. By doping Ag, grain boundary size of the material increase.
Electron Dispersive Spectroscopy EDS result confirmed existence of Ag in the material and the materials having desired composition. Characterization using Cryogenic Magnetometer was used to examined electrical property of the materials with increasing of Ag doping. As the Ag doping concentration increases, resistivity of the material decreases and the metal isolator transition temperature TMI shifts towards room temperature. Magnetoresistance effect decreases when doping x 0,05 and increase again when doping x 0,1 and 0,15."
Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2018
S-Pdf
UI - Skripsi Membership  Universitas Indonesia Library
cover
Nabila Aisyah Sahara
Studi sifat kelistrikan dan efek magnetoresistansi La0,8 (Ca1-xAgx)0,2MnO3 (x = 0; 0,05; 0,15; 0,2) yang disintesis dengan metode sol gel = Study of electrical properties and magnetoresistance effect of of La0,8 (Ca1-xAgx) 0,2mno3 (x = 0; 0,05; 0,15; 0,2) materials syntesized by sol gel method
"Pengaruh doping Ag terhadap sifat listrik dan magnetoresistansi material La0,8 Ca1-xAgx 0,2MnO3 x = 0; 0,05; 0,15; 0,2 telah diinvestigasi. Material La0,8Ca0,2MnO3 merupakan salah satu member dari material perovskite manganite yang mempunyai struktur umum ABO3. Material yang dihasilkan dikarakterisasi menggunakan XRD, SEM, dan Cryogenic Magnetometer. Hasil karakterisasi XRD didapatkan material memiliki fasa tunggal, dengan menggunakan metode pencocokan rietvield diketahui pendopingan Ag sebesar 0 le; x le; 0,05 memilki struktur orthorombik, namun ketika doping Ag sebesar x ge; 0,15 material mengalami transformasi struktur menjadi rhomohedral. Karakterisasi SEM menunjukkan perubahan ukuran rata-rata grain ketika doping silver meningkat. Dari hasil EDX terlihat unsur Ag telah berhasil tersubstitusi kedalam matriks La0,8Ca0,2MnO3 dengan nilai komposisi dari unsur-unsur yang ada didalamnya mendekati nilai komposisi perhitungan. Hasil karakterisasi cryogenic magnetometer menunjukkan pendopingan silver ke dalam ion Ca pada material La0,8Ca0,2MnO3 dapat menurunkan resistivitas bahan dan menaikkan nilai temperatur transisi metal ke isolator TMI , namun pada x = 0,2 resistivitas bahan kembali meningkat yang diikuti penurunan nilai TMI. Persen magnetoresistansi MR menunjukkan peningkatan ketika bahan La0,8Ca0,2MnO3 didoping oleh 5 dan 15 silver pada ion Ca-nya, namun ketika didoping silver sebesar 0,2 persen MR kembali menurun, yang mana MR terbesar yang didapatkan pada penelitian ini adalah 6 dengan komposisi doping x = 0,15.
The effect of Ag doping on electrical properties and magnetoresistance of La0,8 Ca1 xAgx 0,2MnO3 x 0 0,05 0,15 0,2 materials has been investigated. La0,8Ca0,2MnO3 material is one member of the perovskite manganite material that has a general structure ABO3. Samples that have been synthesized, XRD measurement were taken. After that, the samples are compressed using dice, in which has a diameter 12 mm. So in here, the shape of the samples will be pellet. The pellet samples characterized using SEM EDX and Cryogenic Magnetometer. XRD characterization results obtained, all the samples has a single phase, by using rietvield refinement technique it is known that the substitution of Ag with large doping x ge 0,15 occurs the transformation of structure to rhombohedral. SEM characterization indicates a grain size change when the level of doping Ag increases. The EDX results indicate that the silver elementhas successfully entered into La0,8Ca0,2MnO3 matrix with the composition value of the elements contained therein close to the composition value from the calculation. Cryogenic Magnetometer results show that substitution of Ag into the material La0,8Ca0,2MnO3 , it can decrease the resistivity of the material and increase the value of TMI of the material, but when doping silver was 0,2, The resistivity of material returns increases and TMI value decreases. The Percentage of magnetoresistance MR shown an increase when the La0,8Ca0,2MnO3 material was doped by 5 and 15 silver, but when silver doped 0,2 , percentage of MR decreased again, the largest MR obtained in this study was 6 with doping Ag was 0,15. "
Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2018
S-Pdf
UI - Skripsi Membership  Universitas Indonesia Library
cover
S. Indra Putra
Studi Pembuatan, Karakterisasi XRD dan ESR pada Sampel Manganat LaMg
"Telah dilakukan sintesis dan karakterisasi Resonansi Spin Elektron pada paduan LaMgxMn1-xO3 (x=0; 0,35; 0,5). Sintesis bahan LaMgxMn1-xO3 menggunakan metode pencampuran mekanik dari oksida-oksida penyusun La2O3, MgO dan MnO2. Campuran ini digerus menggunakan High Energy Milling dengan variasi waktu 5, 8 dan 10 jam dan dilakukan proses pemanasan pada suhu 1300 oC selama 6 jam. Bahan ini kemudian digerus kembali dengan variasi waktu 5, 8 dan 10 jam serta dilakukan proses pemanasan ulang pada suhu 1100 oC selama 24 jam. Pengukuran XRD telah dilakukan pada temperatur ruang dengan interval pengukuran sudut 2θ sebesar 200?1000.
Hasil pengukuran XRD menunjukkan bahwa senyawa LaMgxMn1-xO3 dapat dihasilkan melalui pemanasan sampai 1300oC setelah dilakukan penggerusan menggunakan High Energy Milling. Hasil senyawa LaMgxMn1-xO3 (x=0; 0,35; 0,5) yang lebih homogen dapat dihasilkan melalui penggerusan kembali dan pemanasan sampai 1100oC selama 24 jam. Dengan menggunakan persamaan Scherer, semakin lama waktu penggerusan maka ukuran butir senyawa LaMgxMn1-xO3 akan semakin membesar. Sebaliknya, semakin tinggi konsentrasi pendopingan Mg maka ukuran butir LaMgxMn1-xO3 akan semakin mengecil. Pengukuran ESR pun telah dilakukan pada temperatur ruang dengan lebar sapuan 500 mT dan pada frekuensi 9,47 GHz.
Hasil pengukuran ESR menunjukkan bahwa LaMgxMn1-xO3 bersifat paramagnetik dan sifat keparamagnetan LaMgxMn1-xO3 ini secara dominan dipengaruhi oleh ion Mn yang berasal dari bahan dasar MnO2. Karakteristik nilai g dan ∆Hpp senyawa LaMgxMn1-xO3 cenderung tetap dan tidak dipengaruhi oleh penambahan waktu penggerusan. Sedangkan penambahan konsentrasi pendopingan Mg pada LaMgxMn1-xO3 menyebabkan nilai g dan ∆Hpp bertambah sampai pada nilai x tertentu (0,35
Synthesis and characterization of Electron Spin Resonance on the LaMgxMn1-xO3 (x=0; 0,35; 0,5) compound have been performed. Synthesis of the LaMgxMn1-xO3 material used mechanical alloying method from compiling oxides of La2O3, MgO and MnO2. This mixture was milled during 5, 8 and 10 hours using High Energy Milling and sintered at 1300oC for 6 hour. Then this material was milled again with variation of milling time 5, 8 and 10 hours and reheated at 1100oC for 24 hours. XRD measurement have been done at room temperature with interval of 2θ 200?1000.
Result of XRD measurement at room temperature indicates that LaMgxMn1-xO3 can be yielded by heating until 1300oC after milling the mixture using High Energy Milling. LaMgxMn1-xO3 phase will be more homogeny if the mixture was milled again and reheated at 1100oC. Using Scherer formula, increasing in milling time will increase the grain size of LaMgxMn1-xO3. On the contrary, increasing in doping concentration of Mg will reduce the grain size of LaMgxMn1-xO3. ESR measurement of LaMgxMn1-xO3 have been done at room temperature with sweep width 500 mT and frequency 9,47 GHz.
Result of ESR measurement indicate that LaMgxMn1-xO3 is paramagnetic and this paramagnetism dominantly influenced by ion Mn from its oxide: MnO2. Characteristic of g factor and ∆Hpp from LaMgxMn1-xO3 tends to constant and not influenced by milling time. While increasing in doping concentration of Mg will increase the value of g factor and ∆Hpp until certain value of x (0,35"
Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2008
T21552
UI - Tesis Open  Universitas Indonesia Library
cover
Rayhan Faiz Syahrizal
Pengaruh substitusi unsur tembaga terhadap sifat magnetik dan sifat penyerapan gelombang mikro material La0,667Ba0,333Mn1-xCuxO3 (x = 0,35; 0,40; 0,45; dan 0,50) = Effect of Copper Substitution On Magnetic Property and Microwave Absorbtion Property of Material La0,667Ba0,333Mn1-xCuxO3 (x = 0,35; 0,40; 0,45; and 0,50).
"Material perovskite manganat La0,667Ba0,333Mn1-xCuxO3 (x = 0,35; 0,40; 0,45; dan 0,50) disintesis menggunakan metode sol gel. Sampel disinterring dengan temperatur 1000oC selama 6 jam. Metode Rietveld refinement menunjukan struktur kristal berupa orthorombik dengan space group Pnma. Terjadi distorsi pada stuktur kristal yang ditandai dengan perubahan lattice parameter. Dilakukan karakterisasi Scanning Electron Microscope (SEM) dan Energy Dispersive Spectroscopy (EDS) untuk mengetahui morfologi sampel dan komposisi unsur kimia yang terkandung dalam material. Sifat magnet ditentukan menggunakan karakterisasi Vibrating Sample Magnetometer (VSM). Berdasarkan sifat kemagnetan untuk masing-masing material tidak ditemukan perubahan yang signifikan seluruhnya bersifat paramagnetik. Selain itu dilakukan pengujian penyerapan gelombang mikro menggunakan karakterisasi Vector Network Analyzer (VNA). Pada penelitian ini frekuensi gelombang mikro berada pada rentang 8-12 GHz yang sesuai dengan aplikasi frekuensi gelombang radar. Pada pengujian ini didapatkan nilai refleksi hilang material tertinggi pada -31,0253 dB pada frekuensi 10,02 GHz. Selain itu digunakan karakterisasi impedansi untuk mengetahui impedansi listrik di dalam material.
Perovskite manganate material La0,667Ba0,333Mn1-xCuxO3 (x = 0,35; 0,40; 0,45; and 0,50) were synthesized using sol gel method. The samples were sintered at 1000OC for 6 hours. Rietveld refinement shows that both samples are crystallized in orthorhombic structure with Pnma space group and distortion was found in the crystal structure with the changed of lattice parameter. Scanning Electron Microscope (SEM) method was used to measured samples morphology. Energy Dispersive Spectroscopy (EDS) method was used to measured chemistry composition of samples. Magnetic property was measured by Vibrating Sample Magnetometer (VSM). Vector Network Analyzer (VNA) was used to measure the ability of material to absorb the microwave. In this experiment the microwave frequency using 8-12 GHz with the specification of radar wave. In VNA characterization the reflection loss value of material could be measured. The highest reflection loss in material is -31,0253 dB on 10,02 GHz. The impedance characterization was used to measure the electric impedance of material.
"
Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2019
S-Pdf
UI - Skripsi Membership  Universitas Indonesia Library
cover
Bambang Purwo Sri Sedono
Penngaruh Variasi Waktu Milling dan Temperatur Pemanasan terhadap Sifat Magnetik Dinamis Bahan CaMnO3
"Bahan manganat CaMnO3 adalah bahan yang mengalami transisi fase magnetik dari keadaan isolator (paramagnetik) menjadi konduktor (feromagnetik) atau sebaliknya. Preparasi bahan CaMnO3 dilakukan melalui proses reaksi zat padat yaitu dengan mencampurkan bahan dasarnya yang terdiri dari CaCO3 dan MnO2 sesuai dengan perhitungan stoikiometri. Proses pencampuran dilakukan dengan menggunakan ball mill dengan variasi waktu penggerusan 3, 6, 9 dan 12 jam. Setelah itu proses preparasi dilanjutkan dengan memberikan perlakuan panas dengan variasi suhu pemanasan 400°C, 600°C, 800°C dan 1000°C serta variasi lama pemanasan 3, 6 dan 9 jam.
Pengukuran ESR terhadap CaMnO3 telah dilakukan pada temperatur ruang dengan lebar sapuan 500 mT dan pada frekuensi 9,47 GHz. Hasil pengukuran ESR menunjukkan bahwa CaMnO3 bersifat paramagnetik yang secara dominan berasal dari bahan dasar MnO2. Pada temperatur pemanasan 800oC, penambahan waktu milling tidak memberikan pengaruh yang cukup signifikan terhadap faktor g Lande dan konsentrasi spin paramagnetik bahan belum memiliki satu pola yang konsisten. Sementara itu, pengaruh tersebut mulai terlihat pada temperatur pemanasan 1000oC dengan indikasi kenaikan nilai g dari 2.07 hingga 2.12 dan penurunan konsentrasi spin paramagnetik bahan. Pengaruh temperatur pemanasan pada waktu milling 12 jam dan waktu pemanasan 9 jam terlihat dengan adanya kenaikan nilai g dari 2.07 hingga 2.46 dan kenaikan konsentrasi spin paramagnetik bahan.
CaMnO3 is a manganate sample that undergoes magnetic phase transistion from paramagnetic insulator to ferromagnetic conductor or vice versa. Preparation of CaMnO3 was done by solid state reaction (mixing the raw materials of CaCO3 dan MnO2) based on the stoichiometric calculations. The mixing processes was done by using ball mill equipment and by varrying the milling time of 3, 6, 9 and 12 hours. The processes is then continued by giving heat treatment with the temperature variations of 400°C, 600°C, 800°C and 1000°C and also with the heating time variations of 3, 6 and 9 hours.
ESR measurements of CaMnO3 was done at room temperature with sweep width of 500 mT and frequency of 9.47 GHz. ESR results showed that at room temperature, CaMnO3 was paramagnetic that was dominantly originated from the raw material of MnO2. At a heating temperature of 800oC, an increasing of milling time did not give significant influences to the g Lande factor and also the concentration of paramagnetic spins of the sample did not show a tendency to a concistence. However, the influences was slightly observed at a heating temperature of 1000oC identified by the increasing of the g Lande factor from 2.07 to 2.12 and also by the decreasing of the concentration of paramagnetic spins of the sample. The influence of heating temperature at milling time of 12 hours and heating time of 9 hours is identified by an increasing of g Lande factor from 2.07 to 2.46 and also by the increasing of the concentration of paramagnetic spins of the sample."
Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2006
T20648
UI - Tesis Membership  Universitas Indonesia Library