"Summary: This book presents a complete overview of the powerful but often misused technique of Electrochemical Impedance Spectroscopy (EIS). The book presents a systematic and complete overview of EIS. The book carefully describes EIS and its application in studies of electrocatalytic reactions and other electrochemical processes of practical interest. This book is directed towards graduate students and researchers in Electrochemistry. Concepts are illustrated through detailed graphics and numerous examples. The book also includes practice problems. Additional materials and solutions are available online"

"ABSTRACTUkuran butir merupakan salah satu faktor penting untuk mengamati sifat mekanis suatu material polikristalin terutama pada kekerasan serta ketahanan korosi. Penelitian terdahulu melakukan beberapa pengaturan parameter uji lapis listrik nikel, yang salah satunya dilakukan dengan penambahan aditif untuk mendapatkan lapisan nikel nanokristalin. Tujuan penelitian ini ialah untuk mengamati pengaruh penambahan sakarin pada proses lapis listrik nikel terhadap perubahan ukuran butir deposit dan ketahanan korosi lapisan nikel. Proses lapis listrik dilakukan dengan menggunakan larutan Watt bath pada temperatur 50-55oC dimana baja SPCC digunakan sebagai substrat yang ingin dilindungi. Pada penelitian ini sakarin ditambahankan pada larutan Watt bath dengan variasi konsentrasi sebanyak 0g/L, 1g/L, 3g/L dan 5g/L. Hasil pelapisan listrik dikarakterisasi melalui beberapa pengujian, yaitu pengamatan makro dengan menggunakan Optical Microscope, Secondary Electron Microscope SEM digunakan untuk mengamati perubahan struktur deposit, X-Ray Diffraction XRD digunakan untuk menghitung ukuran butir, thickness meter untuk mengukur ketebalan lapisan dan perilaku korosi diamati melalui pengujian Linear Polarization dan Electrocemical Impedance Spectroscopy EIS. Hasil pengujian menunjukan adanya perubahan struktur deposit setelah penambahan sakarin. Tanpa penambahan sakarin butir deposit memiliki struktur menyerupai piramidal dan polihedral kristal. Sementara setelah penambahan sakarin, butir deposit memiliki struktur globular yang berkoloni. Ukuran butir terhalus yaitu berukuran 17.39nm didapat dengan penambahan 5g/L sakarin. Ketebalan lapisan nikel yang terbentuk mengalami penurunan seiring penambahan sakarin. Hasil pengujian EIS diketahui pada sampel dengan butir terkecil yaitu 17.39nm memiliki nilai tahanan transfer muatan Rct dan tahanan lapisan pasif Rf tertinggi yaitu sebesar 3267? dan 83.4? yang diindikasi memiliki ketahanan korosiyang baik. Hal ini diverifikasi melalui hasil pengujian linear polarization dimana diketahui pada penambahan 5g/L memiliki nilai laju korosi terendah yaitu 0.024mm/year.

---

ABSTRACTThe Grain size is one of the factors that affects mechanical properties and corrosion resistance of polycrystalline material. In metallic coating process there are several ways to obtain nanocrystalline deposit and one them is by using additives. The previous studies have suggested that the addition of saccharin during the nickel electroplating process will produce nanocrystalline grains that can increase corrosion resistance. This study used watts bath solution for nickel electroplating with the current density used is 6 A dm2 for 20 minutes and by adding saccharine as much as 0g L, 1g L, 3g L and 5gr L. The grains deposit were observed by using the X Ray Diffraction XRD method while the corrosion mechanism was observed and measured by using Electrochemical Impedance Spectroscopy EIS and Linear polarization methods. The test results indicate a change in the structure of the deposit after the addition of saccharin. Without the addition of saccharine the deposit grains have a pyramidal like structure and a polyhedral crystalline, while after the addition of saccharin, the deposit grains have a colonized globular structure. The finest grain size of 17.39nm is obtained by the addition of 5g L saccharin. The thickness of the formed nickel coating decreases with the addition of saccharin. The result of EIS test is known in the sample with the smallest grain of 17.39nm has the highest charge transfer resistance Rct and passive resistance Rf value of 3267 and 83.4 which is indicated have good corrosion resistance. This is verified by the results of the linear polarization test which is known at the addition of 5g L has the lowest corrosion rate value of 0.024mm year."

"Dross aluminium yang dihasilkan oleh industri peleburan aluminium dapat menyebabkan polusi udara dan pencemaran lingkungan, untuk itu pemanfaatan ulang dross aluminium sebagai pengganti sebagian pasir pada struktur beton diharapkan bisa mengurangi masalah lingkungan yang ditimbulkan dan bisa menjadi sumber bahan baku alternatif pengganti pasir. Dampak fraksi filler dross aluminium 0%, 5% dan 8% terhadap kekuatan tekan dikarakterisasi dengan compressive strength test pada umur beton 1, 3, 7 dan 28 hari. Ketahanan korosi struktur beton dipelajari dengan potentiodyanamic polarization dan electrochemical impedance spectroscopy. Kandungan ion klorida dianalisis menggunakan X-ray fluorescence spectrometry per ketebalan 10 mm dan perubahan struktur setelah siklus dry-immerse beton di lingkungan klorida selama 30, 60 dan 90 hari dievaluasi dengan scanning electron microscope. Hasil investigasi sifat mekanik beton menampilkan kekuatan tekan cenderung menurun dengan naiknya fraksi dross aluminium. Hasil uji elektrokimia menampilkan ketahanan korosi cenderung meningkat dengan naiknya fraksi dross aluminium, selain itu hasil polarisasi potensiodinamik juga menampilkan perpanjangan rentang pasivasi baja tulangan. Hasil karakterisasi X-ray fluorescence spectrometry menunjukkan peningkatan ion klorida terhadap waktu paparan dan kenaikan fraksi dross aluminium. Pengamatan struktur mikro membuktikan bahwa peningkatan konsentrasi ion klorida dipengaruhi oleh pola retak dan munculnya rongga udara dalam struktur beton. Kesimpulan menunjukkan bahwa modifikasi konsentrasi dross aluminium memiliki pengaruh yang sangat signifikan terhadap struktur beton, kekuatan tekan dan ketahanan korosi.

---

Aluminum dross was produced by the aluminum smelting industry can induce air pollution and environmental defilement, therefore reused of aluminum dross as a partial replacement of sand in a concrete structure is intended to diminish the environmental problems and it can be an option source of raw material to replace sand. The impact of aluminum filler fraction of 0%, 5% and 8% on compressive strength was analyzed by compressive strength tests on concrete age of 1, 3, 7 and 28 days. Corrosion resistance of concrete structures was studied by potentiodyanamic polarization and electrochemical impedance spectroscopy. The chloride ion content was analyzed using X-ray fluorescence spectrometry every 10 mm thickness and structure evolution after concrete dry-immerse in the chloride environment for 30, 60 and 90 days were evaluated by scanning electron microscope. The results of the mechanical properties examination indicated compressive strength tend to alleviate with the increase the aluminum dross fraction. Electrochemical test results display that corrosion resistance tends to increase with increasing aluminum dross fraction, furthermore, potentiodynamic polarization results also indicate an extended range of reinforced bar passivation. The results of X-ray fluorescence spectrometry characterization showed a chloride ions enhancement towards the exposure time and aluminum dross fraction escalation. Micro structure verification prove that the concentration of chloride ions escalation is influenced by crack patterns and the appearance of air cavities in concrete structures. The consequences illustrate the strong influence of aluminum dross on concrete structure, compressive strength and corrosion resistance of concentrate modification."

"Studi perilaku elektrokimia dari anoda korban paduan aluminium Al-xZn dan Al-xZn-yIn diteliti pada larutan NaCl 3,5% dengan menggunakan metode electrochemical impedance spectroscpoy (EIS). Hasil penelitian menunjukan bahwa anoda Al-5Zn memiliki diameter kurva semicircle paling kecil diantara anoda paduan Al-xZn yang lain. Begitupula dengan adanya kehadiran indium pada anoda paduan Al-xZn membuat diameter kurva semicircle yang diperoleh menjadi semakin kecil. Berdasarkan hasil pencocokan kurva Nyquist dengan model sirkuit ekuivalen, didapatkan hasil bahwa nilai Rct paling kecil diantara anoda Al-xZn dimiliki oleh Al-5Zn, yaitu Rct = 9008 Ω. Kehadiran indium pada anoda Al-5Zn-0.02In juga membuat nilai tahanan transfer muatan yang diperoleh menjadi semakin kecil, dimana nilai Rct = 2400 Ω. Hasil ini menunjukan bahwa penambahan unsur Zn dan adanya kehadiran In dalam anoda paduan aluminium akan membuat nilai tahanan transfer muatan (Rct) menjadi semakin berkurang, sehingga laju korosi atau laju disolusi dari Al menjadi semakin meningkat.

---

Electrochemical behaviour study of aluminium sacrificial anode Al-xZn and Al-xZn-yIn was investigated in 3.5 wt.% NaCl solution by using electrochemical impedance spectroscopy. The result of EIS tests showed that Al-5Zn alloy has a semicircle curve with the smallest diameter between the others sacrificial anode. Similarly, the presence of indium makes the diameter of semicircle curve that was obtained becomes smaller. Based on the results of nyquist curve fitting with equivalent circuits model, the result showed that the value of smallest Rct between Al-xZn sacrificial anode was owned by Al-5Zn, Rct = 9008 Ω. The presence of indium in Al-5Zn-0.02In sacrificial anode also makes the value of charge transfer resistance (Rct) that was obtained becomes smaller, where the value of Rct = 2400 Ω. These result indicate that the addition of zinc element and the presence of indium in aluminium sacrificial anode will make charge transfer resistance value decreases, so the corrosion rate or dissolution rate of aluminum became increases."

"Hibrida zeolit NaY - ZSM-5 telah berhasil dibuat di atas permukaan pelat kuarsa. Zeolit ZSM-5 dilapisi di atas permukaan pelat kuarsa dengan menggunakan metode spin coating menggunakan bubuk zeolit ZSM-5 yang sebelumnya disintesis dari koloid gel ZSM-5 dengan menggunakan metode sintesis double template dan metode hidrotermal. Dilanjutkan dengan pelapisan zeolit NaY menggunakan metode dip coating menggunakan bubuk zeolit NaY dari hasil sintesis menggunakan proses seeding. Hasil XRD menunjukkan bahwa zeolit yang dihasilkan merupakan zeolit ZSM-5 dan NaY. Diperkuat dengan hasil SEM dan EDS yang memperlihatkan rasio Si/Al pada ZSM-5 sebesar 41,3 dan pada NaY sebesar 2,08. Kemudian dilakukan modifikasi menggunakan ion Co2+ .Untuk melihat pengaruh gas amonia terhadap hibrida zeolit dihitung menggunakan metode EIS (Electrochemical Impedance Spectrometer) yang dengan rentang frekuensi 50 Hz ? 1 MHz. Didapatkan rentang deteksi amonia 0 ppm ? 1000 ppm. Serta dihitung hubungan antara konsentrasi dengan perubahan nilai impedansi pada frekuensi 2000 Hz dan diperoleh nilai r2 sebesar 0,9531. Sedangkan nilai r2 untuk komposit tanpa Co2+ pada 7000Hz didapatkan senilai 0,9991.

---

Zeolite hybrid NaY-ZSM-5 has been successfully made on quartz plate. ZSM-5 zeolite was synthesized using double template and hydrothermal technique and deposited using sipn coating method. The process was continued with depositing NaY zeolite that was synthesized with seeding technique using dip coating method. The XRD result show that the zeolite wich was synthesized was ZSM-5 and NaY zeolite. SEM and EDS characterization that have a good agree with XRD data show Si/Al ratio in ZSM-5 and NaY was 41.3 and 2.1, respectively. Modification was performed using Co2+ ion. The influence of ammonia gases on the zeolite hybrid was see using EIS (Electrochemical Impedance Spectrometer) method with frequency range 50 Hz ? 1 MHz. Correlation between concentration and impedance value was plotted at 2000Hz frequency and the obtained value was r2=0.9531. While value of r2 for composite without Co2+ at 7000Hz was 0,9991."

"Pengamatan terhadap perubahan perilaku korosi sumuran material Duplex SAF 2205 yang telah diberikan perlakuan panas dengan tujuan untuk meningkatkan nilai ketangguhan material tersebut telah dilakukan. Pengujian korosi sumuran dilakukan melalui metode Electrochemical Impedance Spectroscopy dan Polarisasi Potentiodynamic pada material yang telah mengalami perlakuan panas pada rentang temperatur 350-550°C dan waktu tahan 10-40 menit dimana sebagian sampel mengalami perlakuan serangan hidrogen.Berdasarkan pengamatan mikrostruktur, tidak ditemukan terbentuknya fasa sekunder pada sampel sehingga mikrostruktur sampel tidak berubah. Hasil pengujian mekanik menunjukkan proses perlakuan panas pada sampel awal akan meningkatkan kekuatan tarik hingga 10% dan kemampuan elongasi hingga 70%.Hasil pengujian korosi sumuran terlihat dengan meningkatkan temperatur perlakuan panas dan waktu tahan akan meningkatkan laju korosi, namun tidak terlalu signifikan, dimana juga terjadi perbedaan perilaku korosi sumuran pada sampel yang mengalami serangan hidrogen.

---

Observation of pitting corosion behaviors in heat-treated Duplex SAF 2205, in order to improve material?s toughness has been investigated. Pitting Corrosion Investigation has been done by using Electrochemical Impedance Spectroscopy and Potentiodynamic Polarization to heat-treated samples with temperature range between 350-550°C and holding time 10-40 minutes, which half of samples underwent hydrogen charging.

Based on microstructure observation, there is no microstructural change because secondary phases were not formed. Mechanical behavior examination shows that tensile strength will increase up to 10% and elongation will increase up to 70% by heat-treating samples. Corrosion pitting examination showed that increasing temperature and holding time of heat treatment will increase corrosion rate insignificantly, where the differences of corrosion rate behaviors were found in hydrogen-charged samples."

"Pengujian electrochemical impedance spectroscopy (EIS) dilakukan untuk menganalisa perbandingan terhadap coating primer antara epoxy dan alkyd serta topcoat antara polyurethane dan acrylic. Penggunaan metode salt spray (sembur garam) dilakukan terhadap coating primer sebagai analisa kualitatif. Analisa FTIR (Fourier Transform Infrared) dilakukan untuk mengkarakterisasi terhadap gugus fungsi pelapis dan mendukung adhesi antara pelapis dengan substrat.Hasil penelitian ini menunjukkan bahwa sebagai pelapis primer coat, epoxy akan memiliki performa serta perlindungan yang lebih baik dibandingkan alkyd. Sedangkan pada pelapis topcoat, didapatkan polyurethane yang memiliki performa lebih baik dibandingkan acrylic.

---

Electrochemical impedance spectroscopy (EIS) studies have been carried out to compare coating primer between epoxy and alkyd also topcoat between polyurethane and acrylic. The use of the method of salt spray conducted on the qualytitative analysis. FTIR analysis determined the functional groups supporting the adhesion between the coating as well as with the substrate.The results showed that sample epoxy will have performance and better protection than alkyd as coating primer. While the topcoat, polyurethane has the best performance compared to acrylic."

"Ketahanan korosi SS 316L pada variasi konsentrasi lingkungan NaCl diinvestigasi dengan menggunakan pengujian Electrochemical Impedance Spectroscopy (EIS). Perlakuan panas dilakukan pada suhu 1100oC. Pengamatan struktur mikro menggunakan Optical Microscope. Larutan NaCl mensimulasikan kondisi air laut tempat pengaplikasian SS316L, variasi konsentrasi larutan NaCl yaitu ; 1%, 2%, 3,5%, 4%, dan 5%. Ion klorida pada NaCl dapat menyerang lapisan pasif pada permukaan SS. Penetrasi ion klorida ini yang bepengaruh terhadap ketahanan korosi pada SS316L. Hasilnya menunjukkan bahwa pada konsentrasi 3,5% NaCl memiliki ketahanan korosi yang paling rendah. Kelarutan oksigen dalam air paling optimum pada ion Cl 3-3,5%. Pengamatan perubahan struktur mikro menggunakan larutan 3,5% NaCl sebagai pembanding ketahanan korosi sebelum dan setelah dilakukannya perlakuan panas. Hasilnya menunjukkan ketahanan korosi sesudah diberikan perlakuan panas jauh lebih rendah. Struktur mikro saat sesudah mengalami sensitasi pada batas butirnya dan ketidaksamaan besar butir.

---

Corrosion resistance of Austenitic Stainless Steel 316L in variation of NaCl environment was investigated using Electochemical Impedance Spectroscopy test. Heat treatment was done at temperature 1100oC. The microstructure was studied by Optical Microscopy. NaCl solution demonstrated seawater environment, conctentrations varying from 1% to 5%. Ion chloride can penetration through passive film. The penetration of chloride affected corrosion resistance of SS316L.

The result showed that the corrosion resistance of concentration of 3,5% NaCl had the lowest corrosion resistance. Optimum oxygen dissolved occured in concentration 3 ? 3,5% NaCl. The studied of changed of microstructure used 3,5% NaCl solution to compared corrosion resistance of before and after heat treatment. The result demonstrated tha corrosion resistance after heat treatment was lower than the before one. The microstructure after heat treatment suffered sensitization and dissimilarity of grain on microstructure."