"Fabricate through-hole porous anodic aluminum oxide (AAO) template were made by a two-step anodization method of an aluminum with purity 99,98% in 0,3 M oxalic acid at 45 V with 360 minutes of second anodization time. The effect of duration time on the second anodizing step, voltage and solution of the electrolyte on the porous oxide layer and influence of the pore opening on the structural as a template were studied in detail. Then, the prepared template was used as a template for fabricated of dense array of Cu by using electrochemical deposition process performed by direct current (DC). The composition of AAO was confirmed by x-ray diffraction (XRD) analyses and for the deposition of Cu were performed by energy dispersive x-ray spectroscopy (EDS). The structural features of nanowire were calculated by scanning electron microscopy (SEM) images and compared with the imaging of AAO template as parameter.

---

Fabrikasi templet Anodic aluminium Oxide (AAO) sebagai nanopori dilakukan dengan proses anodisasi dengan metode two-step anodization menggunakan alumunium dengan kemurnian 99,98 % pada larutan asam oksalat dengan konsentrasi 0,3 M pada voltase 45 V dan waktu anodisasi kedua sebesar 360 menit. Waktu anodisasi kedua dan voltase serta arus yang digunakan menjadi faktor utama dalam pembentukan ketebalan lapisan oksida dan diameter pori yang dihasilkan. Selain itu, pengaruh konsentrasi sangat berpengaruh dalam ketebalan templet AAO. Aplikasi templet AAO ini digunakan sebagai templet deposisi logam Cu, yaitu dengan cara elektrodeposisi dengan pada arus searah (DC). Digunakan pula X-ray diffraction (XRD) untuk melihat templet AAO dan komposisi Cu pada templet dikarakterisasi dengan energy dispersive x-ray spectroscopy. Untuk melihat morfologi nanopori pada cetakan AAO, dikarakterisasi dengan scanning electron microscopy (SEM)."

"Nanoporous anodic aluminum oxide (AAO) layers were successfully fabricated on aluminum foil through an anodizing process in oxalic acid and mixed electrolytes of sulfuric and oxalic acid. The effect of electrolyte resistivity on the morphology of nanoporous AAO, such as pore diameter and pore density, was investigated. The nanoporous AAO layers‘bmorphology was examined using field emission scanning electron microscopy (FE-SEM) and analyzed using image analysis software. The results showed that anodizing in mixed electrolytes (sulfuric and oxalic acid) produced a much smaller pore diameter and a much higher pore density at lower voltage compared to anodizing in a single oxalic acid. For the anodizing process in oxalic acid, the pore diameters ranged from 14 to 52 nm, and the pore density ranged from 34?106 pores in 500×500 nm2. The anodizing process in the mixed electrolytes resulted in pore diameters within the range of 7?14 nm, and the pore densities were within the range of 211?779 pores in 500×500 nm2. Overall, increasing the electrolyte resistivity within the same solution leads to decreased pore diameter."

"Proses anodisasi pada aluminium menghasilkan struktur fenomenal berupa oksida logam yang terkenal dengan istilah Anodic Aluminum Oxide (AAO). AAO sangat diperlukan untuk meningkatkan daya adhesi pada proses pelapisan selanjutnya baik pada aluminium dan paduannya maupun komposit aluminium. Hal tersebut terjadi akibat adanya ikatan saling kunci antara lapisan oksida hasil anodisasi (AAO) dengan pelapis berikutnya. Morfologi pori pada AAO dapat dengan mudah dimodifikasi melalui perubahan parameter anodisasi. Namun, sayangnya penelitian-penelitian sebelumnya belum menyediakan informasi apapun mengenai pengontrolan diameter pori. Sedangkan seperti yang kita ketahui bahwa perbedaan aplikasi yang diinginkan membutuhkan diameter pori yang berbeda pula. Oleh karena itu guna mendapatkan diameter pori dengan ukuran tertentu maka pemilihan parameter proses anodisasi yang tepat sangatlah penting. Untuk memenuhi kebutuhan tersebut, dalam penelitian ini akan dihasilkan persamaan empiris yang dapat memprediksi ukuran diameter dan densitas pori AAO yang terbentuk hasil anodisasi dengan berbagai parameter tertentu agar dapat digunakan dalam aplikasi yang sesuai. Tujuan utama penelitian ini adalah pengembangan persamaan empiris yang menggambarkan hubungan konsentrasi oksalat, tegangan dan waktu anodisasi terhadap diameter pori. Namun penelitian ini juga menganalisis mekanisme pembentukan, karakteristik, dan ketahanan korosi lapisan terintegrasi pada Al7075/SiC. Serta menganalisis pengaruh konsentrasi, temperatur, dan resistivitas larutan elektrolit, dan tegangan anodisasi terhadap diameter dan densitas pori AAO pada aluminium foil. Proses anodisasi Al7075/SiC dilakukan dalam larutan asam sulfat 16% H2SO4 dengan rapat arus 15, 20, 25 mA/cm2 pada 25, 0, -25oC selama 30 menit. Selanjutnya dilakukan proses sealing dalam larutan CeCl3.6H2O + H2O2 pada temperatur ruang dengan pH 9 selama 30 menit. Proses anodisasi pada aluminium foil dilakukan dalam larutan 3 M H2SO4 + 0,5 M; 0,7 M; dan 0,9 M H2C2O4, dan 0,3; 0,5; 0,7 M H2C2O4 selama 40-60 menit. Proses anodisasi dilakukan pada tegangan konstan 35, 40, dan 45 V untuk larutan asam oksalat dan 15 V untuk larutan campuran. Pengamatan dan evaluasi morfologi lapisan pori hasil anodisasi dilakukan menggunakan alat FE-SEM (Field Emission Scanning Electron Microscope), ketahanan korosi material diinvestigasi menggunakan pengujian polarisasi dan EIS, sedangkan analisa kualitatif terhadap morfologi pori (diameter dan densitas) pada AAO menggunakan perangkat lunak ImagePro. Pengembangan persamaan empiris menggunakan metode derajat terkecil dan permukaan respon. Proses terintegrasi yang diaplikasikan pada komposit Al7075/SiC pada temperatur anodisasi 0 oC menghasilkan terbentuknya deposit bulat kaya cerium dengan diameter 64 nm ( 3 nm) yang menutupi seluruh permukaan lapisan oksida dan rongga secara efektif. Proteksi terintegrasi anodisasi dan pelapisan cerium meningkatkan ketahanan korosi hingga 4 order perbesaran dibandingkan tanpa perlindungan akibat terjadinya ikatan saling kunci antara kedua lapisan tersebut. Peningkatan konsentrasi larutan elektrolit asam oksalat, temperatur, tegangan dan waktu celup anodisasi dalam larutan 0,3; 0,5; dan 0,7 M mengakibatkan peningkatan diameter pori permukaan pada AAO. Sedangkan, penambahan asam sulfat dalam asam oksalat menghasilkan pori dengan morfologi diameter pori yang jauh lebih halus dan densitas pori yang jauh lebih besar. Secara umum, densitas pori hanya tergantung pada diameter pori hasil anodisasi, dimana peningkatan diameter pori menghasilkan densitas pori yang semakin menurun. Persamaan empiris hubungan antara tiga faktor anodisasi (konsentrasi asam oksalat, tegangan, dan waktu anodisasi) dengan diameter pori hasil dari penelitian ini adalah : Dp = 0,140625 MVt + 0,33125 MV ? 523542 Mt + 35,64583 M ? 0,04006 Vt + 0,685764 V +1,792431 t ? 42,5053 (derajat terkecil) dan Dp = 33,3 ? 236,3 M ? 1,453 V + 0,3942 t + 7,60 MV (metode derajat satu)

---

Anodizing process in aluminum produces a phenomenal structure in form of metal oxide which is known as Anodic Aluminum Oxide (AAO). AAOis a very useful morfology to improve the adhesion properties for further coating in aluminum alloy and composite aluminum. This phenomenon is related to the presence of interlock bond between AAO and the next layer. The AAO morphology can be modified simply by varying anodizing parameters.

Therefore, selecting appropriate parameters plays an important role in order to obtain the desired pore size. Unfortunately, the preliminary studies did not provide any information on controlling the pore size and density (through increasing/decreasing the concentration of sulfuric acids, voltage, and duration of anodizing to determine pore diameter and density).

For that purpose, in this research some empirical models were built to predict the pore size produced by anodizing process in various parameters. The grand design if this research aims to develop empirical equations which predict the relationship between oxalic acid concentration, anodizing voltage and time to the pore diameter. However, this research also aims to analyze the formation mechanism and of the integrated layer on Al7075/SiC, as well as the enhancement of corrosion resistance resulted from the integrated layer. Moreover, the influence of various anodizing parameters, i.e. resistivity, concentration, temperature, and type of electrolyte on pore characteristics of AAOis also conducted in this study.

Anodizing process of Al7075/SiC was conducted in 16% H2SO4 solution in current densities 15, 20, 25 mA/cm2 at25, 0, -25oC for 30 minutes. Subsequently, cerium sealing process was carried out in CeCl3.6H2O+H2O2 at room temperature and pH 9 for 30 minutes. Anodizing of aluminum foil were carried out in 0,3; 0,5; 0,7M H2C2O4 solution and a mixture solution of 0.5M, 0.7M, and 0.9M H2C2O4 and 3M H2SO4 for 40-60 minutes. Anodizing processes were performed under potentiostatic conditions with constant potentials of 35, 40, and 45V for oxalic solution and 15 V for a mixture solution.

Morphology of AAO layer observations were performed using field emission scanning electron microscopy (FE-SEM) FEI Inspect F50, while the corrosion resistance of materials were investigated by means of polarization and EIS, and qualitative analysis of pore characteristics (pore diameters and densities) accomplised by ImagePro software.

The development of empirical equations using least square and response surface methods Integrated protection by conducting anodization at 0oC prior to cerium sealing in Al7075/SiC leads tothe formation of cerium spherical deposit in the diameter of 64 nm ( 3nm) which effectively covered most of the surface of oxide film as well as cavity. Moreover, this integrated protection enhanced four orders magnification of corrosion resistance than that of bare composite due to interlock bonding between the layers.

The increasing of electrolyte concentration and temperature, as well as voltage and duration of anodizing in 0.3; 0.5; dan 0.7 M oxalic acid leads to the increasing of pore diameter in AAO surface. While, the addition of sulfuric acid in oxalic acid provides much smaller pore diameters and higher pore densities at lower voltages than single electrolyte of oxalic acid. In general, pore density is only dependent on pore diameter, which decreases with the increases of pore diameter. The empirical equations built in this research are : Dp = 0,140625 MVt + 0,33125 MV ? 523542 Mt + 35,64583 M ? 0,04006 Vt + 0,685764 V +1,792431 t ? 42,5053 (least square) and Dp = 33,3 ? 236,3 M ? 1,453 V + 0,3942 t + 7,60 MV (first order model) "

"Aluminium merupakan salah satu logam yang banyak digunakan serta dikembangkan untuk berbagai aplikasi. Pada penelitian kali ini dilakukan modifikasi terhadap permukaan almunium meggunakan metode two step anodization sehingga pada permukaan almunium terbentuk almuniun oksida.Pembentukan anodic alumunium oxide AAO digunakan elektrolit asam oksalat 0.3 M dan elektrolit campuran asam oksalat dengan asam sulfat. Dilakukan variasi konsentrasi asam sulfat 0.1 M, 0.3 M dan 0.5 M yang ditambahkan kedalam asam oksalat untuk mendapatkan kondisi optimum. Kondisi optimum dalam pembentukan AAO dengan menggunakan elektrolit campuran asam oksalat 0.3 M dengan asam sulfat 0.1 M dengan diameter pori 76.32 nm dan jarak antar pori 33.56 nm. Variasi voltase dilakukan untuk mengetahui pengaruh voltase dalam pembentukan pori. Penggunaan voltase 45 V pada asam oksalat memperoleh diameter pori 97.37 nm dan jarak antar pori 30.97 nm, sedangkan pada elektrolit campuran asam oksalat 0,3 M dengan asam sulfat 0,1 M di peroleh diameter pori 76.32 nm dan jarak antar pori 33,55 nm hanya menggunakan voltase 25 V. Hal ini menunjukkan penambahan asam sulfat pada asam oksalat memberikan pengaruh terhadap voltase yang digunakan memberikan pengaruh dalam pembentukan templat anodic almunium oxide.

---

Aluminum is one of the most widely used metals and developed for various applications. In this research, modification of aluminum surface using two step anodization method and aluminum oxide has formed on aluminum surface. The forming of anodic aluminum oxide AAO is used electrolyte oxalic acid 0.3 M and electrolyte mixture of oxalic acid and sulfuric acid. A variation of 0.1 M, 0.3 M and 0.5 M sulfuric acid concentrations was added to the oxalic acid to obtain the optimum condition. The optimum conditions in the forming of AAO by using 0.3 M electrolyte oxalic acid and 0.1 M sulfuric acid with pore diameter 76.32 nm and pore distance 33.56 nm. Variations of voltage are performed to determine the effect of voltage in the pore forming. Using 45 V voltage on oxalic acid obtained pore diameter 97.37 nm and pore distance 30.97 nm, whereas in the mixing of electrolyte oxalic acid 0,3 M and sulfuric acid 0,1 M obtained pore diameter 76.32 nm and pore distance 33.55 nm. This shows that the addition of sulfuric acid to oxalic acid has a significant effect on the voltage used."

"Fabrikasi templet Anodic aluminium Oxide AAO sebagai nanoporous dilakukan dengan proses anodisasi dengan metode two-step anodization menggunakan alumunium dengan kemurnian 99,98 dengan variasi larutan elektrolit yaitu, larutan asam oksalat dan asam sulfat dengan variasi konsentrasi 0,3 M untuk asam oksalat dan 0,1 M, 0,3 M dan 0,5 M untuk asam sulfat, serta waktu anodisasi kedua sebesar 360 menit. Waktu anodisasi, larutan dan konsentrasi elektrolit, serta arus yang digunakan menjadi faktor utama dalam pembentukan ketebalan lapisan oksida dan diameter pori yang dihasilkan. Selain itu, voltase sangat berpengaruh dalam pembentukan jumlah pori pada templet AAO. Untuk melihat stuktur pori yang terbentuk, templet AAO dikarakterisasi dengan Scanning Electron Microscopy SEM . Diperoleh kondisi optimum dari penggunaan asam sulfat konsentrasi 0,3 M pada voltase 25 V menghasilkan diameter pori sebesar 57,72 nm serta jarak antar pori 30,52 nm. Untuk penggunaan asam oksalat 0,3 M pada voltase 45 V menghasilkan pori 97,37 nm dan jarak antar pori 31,97 nm.

---

Fabrication of Anodic Aluminium Oxide AAO template as nanoporous were studied by a two step anodization process using aluminum with 99.98 purity in 0,3 M oxalic acid and a variation of 0,1 M, 0,3 M and 0,5 M sulfuric acid solution with 360 minutes of second anodization time. Time for anodizing process, electrolyte solution and concentration, and current become the main factors in the formation of the oxide layer thickness and the pore diameter. Then, the effect of a voltage affects the number of pores on the AAO template. The structural features of nanoporous were examined by Scanning Electron Microscopy SEM The optimum condition was obtained from the use of 0.3 M sulfuric acid at 25 V with pore diameter 57,72 nm and pore distance 30,52 nm. For the use of 0.3 M oxalic acid at 45 V with pore diameter 97,37 nm and pore distance 31,97 nm."

"Penumbuhan lapisan porous anodik aluminium oksida (PAAO) di atas substrat aluminium tubular merupakan suatu tantangan karena struktur pori tumbuh kurang teratur, kurang homogen, dan lapisannya rentan mengalami retakan. Penelitian ini bertujuan untuk meningkatkan ketahanan terhadap retakan lapisan PAAO yang ditumbuhkan di atas substrat aluminium tubular dengan penambahan etilen glikol (EG) dan pemanasan. Lapisan PAAO diperoleh melalui anodisasi aluminium dalam larutan 0,3 M asam sulfat dan oksalat pada suhu 10°C selama 4 jam. EG ditambahkan dengan variasi konsentrasi 0, 5, 10 dan15 vol%. Morfologi lapisan PAAO dikarakterisasi dengan FESEM dan struktur kristalnya dianalisis dengan XRD. Jumlah retakan berkurang dari 4,04x10-4/ µm2 menjadi 2,24x10-5/ µm2 retakan dan 2,47x10-4/µm2 menjadi 6,73x10-5/µm2 retakan dalam asam sulfat dan asam oksalat dengan penambahan 0-15 vol% EG. Rentang diameter pori sebelum dilepas dari substrat adalah 10-14 nm dan setelah dilepas dari substrat dan dietsa kimia menjadi 14-24 nm. EG berperan dalam menjaga stabilitas suhu selama anodisasi, mengurangi kerapatan arus dan meningkatkan viskositas larutan sehingga mampu mengurangi populasi dan lebar retakan. Pemanasan lapisan PAAO dari 1000-1250 oC menyebabkan perubahan fasa dari fasa amorf menjadi fasa kristal g, d, dan ὰ Al2O3.

---

The growth of the porous anodic aluminum oxide (PAAO) layer on a tubular aluminum substrate is challenging because the pore structure grows less orderly, less homogeneous, and layers are prone to cracking. This study aims to improve resistance to cracking of PAAO layers grown on tubular aluminum substrates by adding ethylene glycol (EG) and heating. The PAAO layer was obtained by anodizing aluminum in a 0.3 M sulfuric and oxalic acid at 10 °C for 4 hours. The EG was added at various concentrations of 0, 5, 10, and 15 vol%. The morphology of PAAO layers was characterized by FESEM and the crystal structure was analyzed by XRD. The population of cracks decreased from 4.04x10-4/µm2 to 2.24x10-5/µm2 and 2.47x10-4/µm2 to 6.73x10-5/µm2 cracks in sulfuric and oxalic acid by addition EG 0-15 vol%. The pore diameter range before being removed from the substrate was 10-14 nm and after being removed from the substrate and chemically etched it was 14-24 nm. EG plays a role in maintaining temperature stability during anodization, reducing current, and increasing viscosity of solution to reduce population and width of the crack. Heating PAAO layer from 1000-1250 oC causes the phase change from amorphous to crystalline g-, d-, and ὰ-Al2O3."

"Anodizing adalah salah satu teknik yang digunakan untuk meningkatkan ketahanan korosi logam aluminium. Sayangnya, teknik ini memiliki beberapa kelemahan yang dapat menghambat pembentukan film oksida anodik dalam logam tersebut. Untuk mengatasi masalah ini, banyak senyawa organik telah ditambahkan ke larutan elektrolit yang digunakan dalam proses anodisasi ini. Penambahan senyawa organik ini bertujuan untuk meningkatkan laju pertumbuhan dan karakteristik film oksida anodik yang terbentuk nantinya.Dalam penelitian ini, pengaruh penambahan Ethylene Glycol (EG) ke sifat-sifat film oksida anodik dalam lingkungan korosif dan laju pertumbuhan film oksida anodik diselidiki, yaitu dengan merekam kurva tegangan-waktu dari proses anodisasi, mengamati penampilan permukaan, mengamati bentuk morfologis film, mengukur ketebalan film, mengukur kekerasan film, dan menguji ketahanan film dalam lingkungan korosif. Proses anodisasi dilakukan pada arus konstan, yaitu 300 A / m2 dalam larutan 2M H2SO4 dengan suhu di bawah 10°C. Proses anodisasi dilakukan dalam tiga waktu yang berbeda, yaitu 30 menit, 45 menit, dan 60 menit. EG ditambahkan ke larutan elektrolit dengan konsentrasi 0, 10, 20, hingga 30%.Hasil penelitian ini menunjukkan bahwa penambahan EG meningkatkan laju reaksi elektrokimia pada permukaan logam aluminium yang dibuktikan dengan peningkatan kemiringan pada kurva tegangan-waktu, yaitu dari 0,1 V / menit menjadi 0,6 V / menit sebagai EG konsentrasi meningkat dalam larutan. Lamanya waktu yang digunakan dalam proses anodisasi dan jumlah komposisi EG dalam larutan elektrolit mempengaruhi tingkat ketebalan film dan juga kekerasan film yang terbentuk. Karakterisasi awal sampel menunjukkan bahwa sampel yang dianodisasi dalam 45 menit memberikan hasil yang lebih baik dibandingkan yang lain. Uji ketahanan korosi yang dilakukan pada sampel anodisasi dalam waktu 45 menit menunjukkan bahwa semakin besar komposisi EG dalam larutan elektrolit membuat film oksida anodik yang terbentuk menjadi semakin lemah terhadap serangan korosi.

---

Anodizing is one of the techniques used to increase aluminum metal corrosion resistance. Unfortunately, this technique has several disadvantages that can inhibit the formation of anodic oxide films in the metal. To overcome this problem, many organic compounds have been added to the electrolyte solution used in this anodizing process. The addition of organic compounds aims to increase the growth rate and characteristics of anodic oxide films formed later.

In this study, the effect of adding Ethylene Glycol (EG) to the properties of anodic oxide films in a corrosive environment and the rate of growth of anodic oxide films was investigated, namely by recording the voltage-time curve of the anodizing process, observing the surface appearance, observing the morphological shape of the film, measuring film thickness, measure film hardness, and test film resistance in corrosive environments. The anodizing process is carried out at a constant current, which is 300 A / m2 in a 2M H2SO4 solution with temperatures below 10°C. The anodizing process is carried out in three different times, namely 30 minutes, 45 minutes and 60 minutes. EG is added to the electrolyte solution at concentrations of 0, 10, 20, up to 30%.

The results of this study indicate that the addition of EG increases the rate of electrochemical reaction on the surface of the aluminum metal as evidenced by an increase in the slope of the voltage-time curve, ie from 0.1 V / min to 0.6 V / min as the EG concentration increases in solution. The length of time used in the anodizing process and the amount of EG composition in the electrolyte solution affect the level of film thickness and also the hardness of the film formed. Initial characterization of the sample shows that the anodized sample in 45 minutes gives better results than the others. Corrosion resistance tests conducted on anodized samples within 45 minutes showed that the greater the composition of EG in the electrolyte solution made the anodic oxide film formed became weaker against corrosion attack."

"ABSTRAKKaca konduktor memiliki fungsi strategis di berbagai aplikasi elektronik. Jenisyang menjanjikan adalah Fluorine-doped Tin Oxide (FTO). Dalam penelitian inidilakukan studi pengaruh waktu deposisi (5, 10, 20, 30, dan 40 menit) lapisan tipisFTO dengan metode spray pyrolysis menggunakan alat ultrasonic nebulizer yangtelah dimodifikasi terhadap nilai karakteristik lapisannya ditinjau dari sifat optis,kristalinitas, resistivitas, dan mikrostruktur. Variasi juga dilakukan denganmembandingkan prekursor Sn murni dan larutan yang telah didoping dengan Fsebanyak 2%wt untuk melihat pengaruh penambahan doping F pada larutanprekursor. Pengujian karakteristik lapisan dilakukan menggunakan XRD, SEM,UV-Vis spectroscopy, dan digital multimeter. Berdasarkan karakterisasi yangdilakukan diperoleh nilai terbaik untuk FTO yang dihasilkan adalah pada waktudeposisi 20 menit dengan nilai transmitansi 74%, energi band gap (Eg) 3,85 eV,dan sheet resistance (Rs) 7,99 Ω/sq.

---

ABSTRACTConductive glass has strategic functions in various electronic applications. Oneof the lead is Fluorine-doped Tin Oxide (FTO). In this research, the effects ofdeposition time (5,10,20,30, and 40 minutes) for fabrication of FTO thin film uponspray pyrolysis process using modified ultrasonic nebulizer on its characteristicin terms of optical, crystalinity, resistivity and microstructure properties has beenstudied. Variation was also performed by comparing the pure Sn precursor andthe solution that has been doped with F 2%wt to see the doping effect toproperties of thin film. The thin film characterization were carried out using XRD,SEM, UV-Vis spectroscopy, and digital mutlimeter. Based on the results obtainedfor the best FTO was generated at the time of deposition is 20 minutes. Providing74% transmittance, band gap energy (Eg) 3.85 eV and sheet resistance (Rs) 7.99Ω/sq."

"Saat ini nanoteknologi berkembang dengan sangat pesat karena menghasilkan sifat yang menarik dan berbeda dengan teknologi yang dihasilkan dalam ukuran makroskopis. Produk-produk nanoteknologi berbasis nanostructure materials telah banyak dikaji dan dikembangkan, beberapa diantaranya adalah carbon nanotube, quantum dots, dan nano porous membrane. Sintesis nanostructure materials tersebut dapat dilakukan dengan template nano porous aluminum oxide hasil proses anodisasi. Sifat dan struktur nanoporous aluminum oxide tersebut sangat dipengaruhi oleh beberapa variabel proses anodisasi seperti waktu anodisasi, jenis dan konsentrasi larutan elektrolit, tegangan dan rapat arus, dan juga temperatur.Pembuatan nano porous aluminum oxide dari aluminium foil untuk aplikasi nanostructure materials telah dilakukan dengan metoda anodisasi. Proses anodisasi dilakukan dengan kenaikan temperatur 10 °C, 20 °C, dan 30 °C dalam campuran larutan asam sulfat 3 M dan asam oksalat 0,5 M, pada kondisi tegangan 15 volt, dan waktu anodisasi 30 menit. Pengamatan diameter pori dilakukan dengan alat FESEM sedangkan pengukuran ketebalan dilakukan dengan alat SEM. Hasil pengamatan menunjukkan bahwa pada kondisi temperatur 10 °C dan 20 °C tidak terbentuk lapisan nano porous alumina sedangkan pada temperatur 30 °C terbentuk nano porous dengan keteraturan near-ordered dengan diameter ratarata 25 nm. Pengujian ketebalan oksida menunjukkan bahwa semakin tinggi temperatur menyebabkan kenaikan ketebalan rata-rata oksida. Ketebalan lapisan oksida mengalami kenaikan berturut-turut 351 nm, 652 nm, dan 770 nm pada temperatur 10 °C, 20 °C, dan 30 °C.

---

Recently, nanotechnology grows fast because it develops interesting features and different from technology produced on macroscopic scale. Nanotechnology products like nanostructure materials have been studied and developed. Some of them are carbon nanotube, quantum dots, and nano porous membrane. Fabrication of nanostructure materials can be done by template of nano porous aluminum oxide from anodizing process. Properties and structure of the nano porous aluminum oxide was influenced by several variables from anodizing process like time, type and concentration of solution, voltage and current density, and temperature.

Fabrication of nano porous aluminum oxide from aluminum foil for nanostructure materials application have been done from anodizing process in this research. Anodizing process was done on different temperature 10 °C, 20 °C, and 30 °C in mixing solution of sulfuric acid 3 M and oxalic acid 0.5 M, voltage 15 volt, anodizing time 30 minute. Observation of pores diameter was done by FESEM and measurement of oxide thickness was done by SEM. The result shows that there is no formation of porous alumina on temperature 10 °C and 20 °C. In other hand, there is formation of near-ordered nano porous aluminum oxide on temperature 30 °C with 25 nm average diameters. Measurement of thickness show that oxide thickness increases when temperature is raised. Oxide film thickness increases 351 nm, 652 nm, and 770 nm on temperature 10 °C, 20 °C, and 30 °C, respectively."