"Kerapatan keadilan vibrasi lokal bahan a-Si, a-C, a-Si:H, dan a-C:H telah dihitung dengan menggunakan metode kekisi bethe gugus dan model potensial born. Potensial born mengikutsertakan dua tetapan kakas tetangga terdekat, yaitu tetapan kakas meruji dan tatapan kakas sudut. Hasil perhitungan memperlihatkan puncak-puncak yang terdapat pada spektrum raman bahan silikon amorf (a-Si) di pita lintang optik (480 cm) dan karbon amorf (a-C) di pita lintang optik (1080 cm). Hasil ini juga memperlihatkan bahwa kerapatan keadaan lokal dipengaruhi oleh keberadaan atom H di gugus. "

"Densitas keadaan elektron a-Si_1-xC_x, and a-Si_1-xH_y telah dihitung untuk seluruh konsentrasi karbon dan beberapa konsentrasi hidrogen (0≤y≤0.5). Struktur atom dimodelkan dengan struktur acak kontinu yang menghubungkan atom Si, C dan H. Keadaan elektron diperoleh dengan menyelesaikan Hamiltonian tight binding kisi Bethe dengan pendekatan medan efektif. Metode Gomez-Santos dan Verges digunakan untuk memperoleh perata-rataan DOS yang memperhitungkan ketidakteraturan diagonal dan off diagonal serta ketidakteraturan parameter SRO (short range order). Model struktur yang digunakan berdasarkan konfigurasi tetrahedral dari atom Si dan C serta konfigurasi trigonal dari atom C. Kehadiran hidrogen menyebabkan pergeseran ujung atas pita valensi ke energi yang lebih rendah sehingga mengakibatkan pelebaran gap pada a-Si_1-xH_y, a-C_1-yH_y(C-sp³) dan a-C_1-yH_y (C-sp²). Pergeseran ujung atas pita valensi ke energi yang lebih rendah juga terjadi dengan kenaikan konsentrasi karbon pada a-Si_1-x, Cx(C-sp³). Pergeseran ujung atas pita valensi yang berbeda terjadi pada a-Si_1-x Cx (C-sp²) yang bergeser ke energi yang lebih tinggi. Selain itu ujung bawah pita konduksi juga bergeser ke energi yang lebih tinggi. Kenaikan lebar gap yang lebih tinggi terjadi untuk konfigurasi karbon berikatan tetrahedral sp³ dibandingkan konfigurasi karbon berikatan trigonal sp2. Kehadiran hydrogen dan karbon secara bersamaan pada aSi_1-xC_x:H_y(C-sp³) dan a-Si C_1-xC_x (C-sp²) meningkatkan lebar gap. Peningkatan fraksi karbon dalam bentuk grafit meningkatkan lebar gap a-Si_1-x C_x (C-sp² dan C-sp³) sampai konsentrasi karbon x=0.6. "

"Untuk mengetahui pengaruh agen ikat silang terhadap sifat kuat tarik dan titik leleh polietilen densitas tinggi (HDPE-High Density Polyethylene) dibuat sampel XPE (Crosslinked Polyethylene) dengan variasi prosentase berat (0,50 sampai 1,50 bwt) agen ikat silang DCP (Dicumyl Peroxyde). Selanjutnya dilakukan pengukuran dan pengujian seperti fraksi rantai ikat silang.. FTIR, densitas, XRD. titik leleh, temperatur dekomposisi dan sifat kuat tarik.Hasil pengamatan menunjukkan bahwa DCP merangsang meningkatkan terbentuknya rental ikat silang dalem HDPE, tetapi mulai 1.50% DCP cenderung menuju keadaan jenuh. XPE dengan kendungan DCP kurang dari 1,50' terbentuk fasa kristalin ( bidang kristal (010) ) namun secara bulk XPE lebih berfasa amorfphous. Hal ini ditandai dengan penurunan nilai derajat kristalinitas dan densitas. Fenomena ini menyebabkan titik leleh dan dekomposisi meningkat, modulus Young menurun, elongasi meningkat dan UPS meningkat walau relatif kecil.Sehingga XPE merupakan polietilen yang bersifat kuat tarik lebih baik dan lebih stabil pada pemakaian temperatur operasi tinggi."

"Malaria masih menjadi masalah kesehatan masyarakat dan merupakan penyakit endemis di daerah tropis termasuk Indonesia. Semakin banyaknya strain Plasmodium yang resisten terhadap obat antimalaria membutuhkan penemuan obat baru yang lebih poten untuk mengatasi permasalahan ini. Delonix regia mengandung zat kimia alkaloid dan terpenoid yang memiliki potensi sebagai antiplasmodium. Tujuan penelitian ini adalah untuk membuktikan bahwa ekstrak kulit buah dan daun Delonix regia mampu menurunkan densitas Plasmodium berghei. Kelompok perlakuan mendapatkan ekstrak kulit buah dan daun yang diberikan dengan tiga dosis, yaitu 2,8 mg/20g mencit, 8,4 mg/20g mencit, dan 14 mg/20g mencit selama tiga hari berturut-turut dimulai tujuh hari setelah inokulasi parasit pada Mencit Swiss-webster. Pemeriksaan parasitemia dilakukan pada hari ke-0 sebelum perlakuan dan hari ke-3 setelah perlakuan dengan cara dibuat sediaan apusan darah tipis yang diwarnai dengan Giemsa. Hasil analisis statistik menunjukkan pada dosis ekstrak kulit buah Delonix regia dosis 2,8 mg/20g mencit dan dosis 8,4 mg/20g mencit menunjukkan perbedaan jumlah parasit yang signifikan terhadap jumlah parasit kelompok kontrol negatif, sedangkan pada ekstrak kulit buah Delonix regia dosis 14 mg/20g mencit menunjukkan bahwa tidak ada perbedaan yang signifikan terhadap kelompok kontrol negatif. Hasil analisis statistik pada ekstrak daun Delonix regia dosis 2,8 mg/20g mencit, 8,4 mg/20g mencit dan 14 mg/20g mencit menunjukkan tidak ada perbedaan yang signifikan terhadap kelompok kontrol negatif. Berdasarkan hasil penelitian tersebut dapat disimpulkan bahwa pemberian ekstrak kulit buah Delonix regia dosis 2,8 mg/20g mencit paling baik dalam menurunkan densitas Plasmodium berghei.

---

Malaria remains a public health problem and endemic in tropical country, including Indonesia. Increasing number of strains of drug-resistant Plasmodium malaria needs to find a new, more potent drugs to overcome this problem. Delonix regia contains alkaloid and terpenoid chemicals that have potential as antiplasmodium. The purpose of this study is to prove that the rind and leaf extracts of Delonix regia can reduce the density of Plasmodium berghei in Swiss-webster mice. The treatment group get rind and leaf extracts given in three doses, ie 2,8 mg/20g mice, 8,4 mg/20g mice, and 14 mg/20g mice for three consecutive days starting seven days after inoculation of parasites. Parasitemia examination performed on H0 before and day 3 after treatment made by blood smear preparations stained with Giemsa thin.

The results of the statistical analysis showed a dose Delonix regia rind extract dose 2,8 mg/20g mice and 8,4 mg/20g mice showed a significant difference in the number of parasites on the number of parasites negative control group, while in the rind extracts Delonix regia dose 14 mg/20g mice showed no significant difference to the negative control group. The results of statistical analysis on Delonix regia leaf extracts dose 2,8 mg/20g mice, 8,4 mg/20g mice and 14 mg/20g mice no significant difference to the negative control group. Based on these results it can be concluded that administration of Delonix regia rind extract at a dose of 2,8 mg/20g mice body weight is the best dose which can reduce the density of Plasmodium."

"Paduan aluminium seperti 2024 aluminium alloy banyak digunakan pada industri pesawat sebagai bahan penguat struktur dan lapisan sayap pesawat. Tetapi paduan aluminium tersebut rentan terhadap korosi pada aging state tertentu, sehingga aluminium perlu diplating. Nikel merupakan salah satu logam yang sering digunakan sebagai material pelapis karena memiliki sifat ketahanan korosi yang baik, kekerasan dan juga dapat meningkatkan tampilan dari logam yang dilapisi. Dalam penelitian ini, dilakukan proses pelapisan Nikel pada lempeng Aluminium melalui metode electroplating dengan variasi rapat arus sebesar 3 mA/cm2, 10 mA/cm2, dan 25 mA/cm2. Karakterisasi XRD dan SEM dilakukan untuk melihat struktur kristal dan mikrostruktur lapisan nikel. Uji kekerasan dilakukan dengan metode Vickers. Uji sifat korosi dilakukan dengan metode LSV (Linear Sweep Voltamettry). Pola difraksi sinar-X menunjukkan peningkatan intensitas bidang (111) dan bidang (002) seiring meningkatnya rapat arus, sedangkan intensitas bidang (022) mengalami penurunan. Pengolahan data LSV menunjukkan sampel dengan arus 25 mA cm-2 memiliki daya tahan korosi yang paling baik yaitu sebesar 0,157 mm/tahun, tetapi memiliki tingkat kekerasan yang paling rendah sebesar 416,6 VH. Perubahan rapat arus ditemukan dapat mempengaruhi struktur kristal, morfologi permukaan dan sifat elektrokimia lapisan nikel yang terdeposisi.

---

Aluminium alloys such as 2024 aluminium alloys are widely used in aircraft industry as structural sthrength and skin for wings. However, those alloys are susceptible to corrosion at certain aging state, hence plating is necessary. Nickel is one of metal that widely used as coating material due to their high corrosion resistance property, hardness and enhancing the metal’s surfaces. In the current study, Nickel was successfully deposited on the Aluminium surface by electroplating method with various current density which are 3 mA/cm2, 10 mA/cm2, and 25 mA/cm2. XRD and SEM was performed to see the crystal structure and microstructure of the plated nickel coating. Hardness test was performed using Vikers method. The corrosion property was tested by LSV (Linear Sweep Voltamettry) method. The XRD patterns show increasing intentisy of (111) and (002) plane along the increase of current density, while the (022) intensity decreasing. The LSV shows that the sample with 25 mA cm-2 current density has the highest corrosion resistance with value of 0.157 mm/year, but it has the lowest hardness value at 416.6 VH. It was found that the variation of current density can affect crystal structure, surface morphology and electrochemical property of the deposited nickel coating."

"Characterization of pellet mixture of oxyde uranium and oxyde zirconium that is sintering process product. Characterization of nixture pellet UO2 and ZrO2 result of sintering process has been done as a mean to knows hardness character , microstructure, grain size and pellet density...."

"[ABSTRAKLapangan XXX merupakan lapangan minyak di cekungan Natuna Baratdengan reservoir utama berupa reservoir batu pasir. Ketebalan reservoir padalapangan ini sangat bervariasi sehingga hasil inversi hanya dapat memetakanketebalan reservoir yang mendekati ketebalan tuning.Berdasarkan uji sensitifitas, parameter AI di setiap sumur tidak dapatmembedakan hidrokarbon, sehingga parameter akustik saja tidak dapat diaplikasikandalam karakterisasi reservoir lapangan ini. Namun ketika parameter densitas terpisahdengan parameter kecepatan P, sebaran hidrokarbon dapat dibedakan dengan baik.Kecepatan S tidak tersedia di semua sumur padahal data ini sangat diperlukanuntuk melakukan pengolahan data dengan metode inversi simultan. Oleh karena ituakan dilakukan beberapa estimasi untuk mendapatkan data kecepatan S antara laindengan metode castagna, metode gassmann, metode parsial, metode Xu-White danmetode Lee. Data kecepatan S yang dipakai adalah kecepatan S terbaik yangdiperoleh dari metode Xu White dikarenakan hasil log poisson?s rationya palingmendekati tren kurva saturasi air. Selain itu aspek rasio batuan yangmempertimbangkan nilai porositas dan volume clay, serta kontrol kualitas Vp modeldari metode Xu-White memiliki rasio error minimum jika dibandingkan dengan nilaiVp dari data log.Metode inversi simultan dengan data pre-stack atau partial stackmemungkinkan dilakukannya prediksi parameter Impedansi P, Impedansi S, dandensitas dari data seismik. Selain itu meode inversi simultan dapat dipergunakanmulti wavelet dalam pengolahan datanya. Hasil penampang inversi yang diperolehmenunjukkan bahwa inverse densitas dapat menjelaskan letak sebaran batuanreservoir dan fluida berdasarkan cut off sensitifitas yakni nilai dibawah 2,26 gr/cc.

---

ABSTRACTX field is an oil field in West Natuna Basin with sandstone reservoir asprimary target. There was varying reservoir thickness, so the inversion method thatcould only be applied to map reservoir thickness, which close to tuning thickness.Based on sensitivity analysis, Acoustic Impedance parameters couldn?tindicate hydrocarbon appearance for each well, so Acoustic Impedance cannot beapplied for reservoir characterization in this field. Density versus AcousticImpedance could map hydrocarbon appearance.Shear velocity weren?t available where those data was needed for runningsimultaneous inversion method. Predicting velocity shear would be carried out byusing several method such as Castagna, Gassmann, Parsial, Xu-White, and Lee. Thebest estimated velocity shear would be used for inversion, The best estimated shearvelocity from Xu-White method because Xu-White?s poisson ratio log presentssimilar trend with water saturation log (Sw). Moreover, Xu-White?s ratio aspect isalso considering porosity and clay volume value. Based on quality control result, Vpmodel of Xu-White had minimum error ratio compared to Vp from log.Simultaneous inversion with pre-stack and parsial stack data what can be usedfor predicting P-Impedance, S-Impedance, and density from seismic data. Otherwise,this method is also used not only for single wavelet but also multi wavelet. Theinversion result from this study can mapping out the hydrocarbon appearance forreservoir target based on cut off value from sensitivity test of less than 2,26 gr/cc.;X field is an oil field in West Natuna Basin with sandstone reservoir asprimary target. There was varying reservoir thickness, so the inversion method thatcould only be applied to map reservoir thickness, which close to tuning thickness.Based on sensitivity analysis, Acoustic Impedance parameters couldn?tindicate hydrocarbon appearance for each well, so Acoustic Impedance cannot beapplied for reservoir characterization in this field. Density versus AcousticImpedance could map hydrocarbon appearance.Shear velocity weren?t available where those data was needed for runningsimultaneous inversion method. Predicting velocity shear would be carried out byusing several method such as Castagna, Gassmann, Parsial, Xu-White, and Lee. Thebest estimated velocity shear would be used for inversion, The best estimated shearvelocity from Xu-White method because Xu-White?s poisson ratio log presentssimilar trend with water saturation log (Sw). Moreover, Xu-White?s ratio aspect isalso considering porosity and clay volume value. Based on quality control result, Vpmodel of Xu-White had minimum error ratio compared to Vp from log.Simultaneous inversion with pre-stack and parsial stack data what can be usedfor predicting P-Impedance, S-Impedance, and density from seismic data. Otherwise,this method is also used not only for single wavelet but also multi wavelet. Theinversion result from this study can mapping out the hydrocarbon appearance forreservoir target based on cut off value from sensitivity test of less than 2,26 gr/cc., X field is an oil field in West Natuna Basin with sandstone reservoir asprimary target. There was varying reservoir thickness, so the inversion method thatcould only be applied to map reservoir thickness, which close to tuning thickness.Based on sensitivity analysis, Acoustic Impedance parameters couldn’tindicate hydrocarbon appearance for each well, so Acoustic Impedance cannot beapplied for reservoir characterization in this field. Density versus AcousticImpedance could map hydrocarbon appearance.Shear velocity weren’t available where those data was needed for runningsimultaneous inversion method. Predicting velocity shear would be carried out byusing several method such as Castagna, Gassmann, Parsial, Xu-White, and Lee. Thebest estimated velocity shear would be used for inversion, The best estimated shearvelocity from Xu-White method because Xu-White’s poisson ratio log presentssimilar trend with water saturation log (Sw). Moreover, Xu-White’s ratio aspect isalso considering porosity and clay volume value. Based on quality control result, Vpmodel of Xu-White had minimum error ratio compared to Vp from log.Simultaneous inversion with pre-stack and parsial stack data what can be usedfor predicting P-Impedance, S-Impedance, and density from seismic data. Otherwise,this method is also used not only for single wavelet but also multi wavelet. Theinversion result from this study can mapping out the hydrocarbon appearance forreservoir target based on cut off value from sensitivity test of less than 2,26 gr/cc.]"