"Semakin meningkatnya kebutuhan aspal sebagai bahan pembangunan jalan, perlu adanya upaya penghematan penggunan aspal. Dalam penelitian ini dipertimbangkan penggunaan serat serabut kelapa sebagai bahan tambah pada aspal pen 60/70 yang di modifikasi. Serat serabut yang di gunakan adalah bahan sisa yang tidak terpakai, sehingga di harapkan dalam penelitian ini dapat menggurangi penggunaan aspal dan dapat memanfaatkan limbah serabut kelapa. Proses untuk menentukan kombinasi campuran antara aspal dan serat serabut kelapa, uji kekuatan laston AC-WC dalam penelitian ini meliputi: uji karakteristik agregat, uji karakteristik aspal, uji marshall, uji stabilitas sisa dan uji modulust resilient dengan alat Umatta. Pengujian UMATTA terhadap dua jenis campuran yang diteliti pada temperatur 25°C 300C, 450C dan 600C menunjukkan bahwa nilai modulus resilient menurun dengan peningkatan temperatur. Pada suhu pengujian 300C campuran menggunakan aspal berserabut menghasilkan nilai Modulus Resilien (1743,15 MPa) yang lebih tinggi dibanding campuran menggunakan aspal Pen 60/70 (826,24MPa). Nilai modulust resilien aspal berserabut memiliki nilai 2,11 kali lebih tinggi di bandingkan aspal Pen 60/70.

---

The increasing need for asphalt as a road construction material, It is necessary to encourage the efficiency use of asphalt. This study we considering the use of coconut fiber as an additive to penetration bitumen 60/70 which has been modificated. Coir fiber used an unused material. In this study process to determine the combination of a mixture of asphalt and coir fiber with Laston AC-WC strength test include: test characteristics of aggregates, asphalt characteristics test, marshall test, residue stabilities resilient modulust test withUmatta tool. Umatta testing the two types mix in thoroughly at temperatures of 25°C, 30° C, 45° C and 60 °C showed that the resilient modulust value decreases with increasing temperature. At a temperature of 30 °C testing asphalt mixtures using stringy produce resilient modulust value (1743,15MPa) is higher compared using a mixture of penetration bitumen 60/70 (826,24 MPa). Resilient modulust asphalt filamentous value has a value of 2,11 times higher compared to 60/70 penetration bitumen."

"Pada proses pengadukan beton, akan menghasilkan limbah beton yang mengering pada tempat adukan dan air sisa dari adukan beton. Dari hasil limbah adukan beton tersebut, timbullah ide penelitian untuk memanfaatkan kembali limbah tersebut sebagai campuran paving block. Paving block tersebut dicampur bahan tambahan berupa serat ijuk. Parameter yang diuji adalah kuat tekan, kuat lentur dan penyerapan. Dari hasil penelitian, paving block tersebut memiliki kuat tekan serta kuat lentur yang rendah dan penyerapan yang tinggi. Dengan menambahkan serat ijuk ke dalam campuran, kuat tekan dan kuat lentur paving block tersebut dapat meningkat.

---

In the process of concrete mixing, concrete sludge waste will be produced from dry concrete and remaining water in place of concrete mixing. There is an idea to recycle concrete sludge waste as the material for paving block. That paving block will be added with palm fiber. The parameters that will be tested are compressive strength, flexural strength and absorption. As the results of research, the paving block has low compressive strength and flexural strength. But its absorption is high. By adding palm fiber into the mix, compressive strength and flexural strength of paving block can be increased."

"Perkerasan lentur merupakan jenis perkerasan yang banyak dipakai di Indonesia. Salah satu kerusakan yang sering terjadi pada perkerasan lentur ialah kerusakan alur roda. Jenis deformasi ini berupa perubahan bentuk permukaan jalan akibat beban roda kendaraan yang melintasi permukaan perkerasan jalan tersebut. Penelitian ini bertujuan untuk mencari alternatif campuran beton aspal yang dapat mengurangi terjadinya deformasi tersebut. Limbah sabut kelapa ditambahkan pada aspal sehingga menjadi aspal berserat. Bahan tambah ini berupa serat halus berukuran 0,5mm-1,25mm dicampur dengan Aspal pen 60/70 dengan persentase 0%; 0,75% dan 1,5% terhadap berat aspal. Aspal berserat ini kemudian dicampur dengan aggregat menjadi campuran beton aspal AC-WC kemudian dilakukan pengujian dengan Wheel Tracking Machine pada suhu 30˚C, 45˚C dan 60˚C. Hasil dari penelitian ini menyimpulkan bahwa penambahan limbah sabut kelapa lebih tahan terhadap pengaruh suhu dibandingkan dengan campuran aspal beton tanpa serat. Hasil pengujian Marshall dan Wheel Tracking Machine memperlihatkan terjadinya peningkatan stabilitas dan ketahanan terhadap nilai deformasi pada persentase limbah sabut kelapa 0.75%.

---

Flexible pavement is a type of pavement that is widely used in Indonesia. One of damage that often occurs in flexible pavement damage is the wheel groove. Type of deformation is a change in shape of the road surface due to wheel loads of vehicles across the surface of the pavement. This study aimed to explore alternative asphalt concrete mixtures that can reduce the occurrence of such deformation. Coconut coir waste is added to the asphalt so that it becomes fibrous asphalt. The added material in the form of fine fibers measuring 0.5 mm – 1.25mm mixed with asphalt pen 60/70 with a percentage of 0 % , 0.75 % and 1.5 % of the weight of asphalt. Fibrous asphalt is then mixed with aggregate into asphalt concrete mix AC - WC then testing the Wheel Tracking Machine at a temperature of 30˚C , 45˚C and 60˚C. The results of this study concluded that the addition of coconut coir waste is more resistant to the effects of temperature compared to asphalt concrete mixtures without fiber. The results of testing the Marshall Test and Wheel Tracking Machine reflects the increasing stability and resistance to deformation values ​​on the percentage of waste coconut husks 0.75 %. "

"Limbah sisa adukan beton dan limbah kaca seringkali menjadi sampah dan berpotensi merusak lingkungan karena sifatnya yang sulit terurai. Padahal kedua bahan tersebut mempunyai potensi untuk dimanfaatkan, salah satunya sebagai pengganti agregat dan semen pada paving block. Tujuan penelitian ini adalah mengetahui seberapa besar pengaruh penambahan limbah adukan beton dan serbuk kaca terhadap sifat-sifat mekanik paving block. Pembuatan paving block dibuat dari limbah adukan beton, semenPC type I, dan serbuk kaca yang berasal dari sisa botol heinkein dan anker bir. Benda uji penelitian dibuat dengan perbandingan komposisi semen dan agregat 1:4,5 dengan 4 perlakuan subtitusi serbuk kaca yaitu 0%, 10%, 20%, dan 30% dari berat semen. Pengujian kuat tekan dan kuat lentur dilakukan pada hari ke-7,14,28 sedangkan pengujian penyerapan air dilakukan pada hari ke-14, 28, 49 dan 56.Dari hasil pengujian, didapatkan bahwa penambahan serbuk kaca 10% dari berat semen mempunyai komposisi terbaik untuk menghasilkan kekuatan yang optimum. Dimana kuat tekan paving block pada umur 28 hari mencapai 13,625 Mpa dan mengalami peningkatan sebesar 25,86% dari paving block tanpa mengunakan campuran serbuk kaca.

---

Residual concrete sludge waste and glass waste is often a waste and potentially damaging to the environment because it is difficult to unravel. Yet, both materials have the potential to be used, as a substitute for aggregate and cement on paving block for example. The purpose of this study was to determine how much impact from the addition of waste concrete and glass powder on the mechanical properties of paving block. Paving blocks were made ​​of concrete waste, Portland Cement type I, and glass powder taken from the rest of heinkein and Anker beer bottles. Research specimens were made ​​with cement and aggregate composition ratio of 1:4,5 and different amount of substitution using glass powder. Glass powder ratios are as follow: 0%, 10%, 20%, and 30% of cement weight. Compressive and flexural strength testing were performed on day 7, 14, 28 while the water absorption test were performed on day 14, 28, 49 and 56.

From the test results, it was found that the specimen with the addition of glass powder by 10% of cement weight has the best composition resulted in producing optimum power. Compressive strength of paving blocks at day 28 reached 13.625 MPa, produced an increase by 25,86% compared to the paving block without using mixture of glass powder."

"Reclaimed Asphalt Pavement (RAP) berasal dari hasil pengerukan jalan dalam kondisi perbaikan dimana RAP tersebut masih mengandung komponen aspal dan agregat dengan tujuan dapat digunakan kembali. Penelitian ini menghasilkan campuran beraspal dengan variasi kadar RAP 35%, 45%, 51.55% dan variasi kadar aspal 5%, 6%, 7% dengan total jumlah sampel 27 buah serta menganalisa pengaruh dari metode pencampuran dengan suhu hangat ( WMA) pada campuran beraspal yang dibuat untuk Laston lapis antara (AC-BC). Sampel akan dilakukan uji Marshall untuk mendapatkan nilai-nilai stabilitas, kelelehan, MQ, VIM, VMA dan VFA yang kemudian dikaitkan dengan spesifikasi Bina Marga untuk melihat campuran beraspal terbaik pada variasi kadar yang telah ditentukan serta dapat menentukan kadar aspal optimum dan kadar RAP optimumnya. Uji Factorial Design juga dilakukan untuk mengetahui signifikansi kadar RAP, kadar aspal dan interaksi keduanya terhadap nilai-nilai yang didapatkan dalam uji Marshall. Hasil penelitian didapatkan campuran terbaik pada kadar RAP 35% dengan kadar aspal 6% serta kadar aspal optimum 6.3%, signifikansi kadar RAP tidak berpengaruh terhadap seluruh nilai-nilai yang didapatkan dari uji Marshall sementara untuk kadar aspal berpengaruh signifikan terhadap nilai VMA, VIM dan VFA.

---

Reclaimed Asphalt Pavement (RAP) is derived from the results of dredging the road in repair conditions where the RAP still contains asphalt and aggregate components for the purpose of being reused. This study produced paved mixtures with variations in RAP levels of 35%, 45%, 51.55% with variations in asphalt content of 5%, 6%, 7% with a total 27 samples and analyzed the effect of mixing methods with warm temperatures (WMA) on mixtures paved made for Laston layers between (AC-BC). The sample will be tested by Marshall to obtain the values ​​of stability, melt, MQ, VIM, VMA and VFA to see the best asphalt mixture at a predetermined level variattion based on Bina marga specification and can determine optimum asphalt content and grade optimum RAP.

Factorial Design Test was also conducted to determine the significance of RAP levels, asphalt levels and their interactions with the values ​​obtained in the Marshall test. The results showed the best mixture of 35% RAP levels with 6% asphalt content and optimum asphalt content 6.3%, the significance of RAP levels did not affect all values ​​obtained from the Marshall test while the asphalt content had a significant effect on the values ​​of VMA, VIM and VFA."

"Skid resistance dihasilkan dari gesekan antara permukaan jalan dan ban kendaraan. Skid resistance ini juga memiliki hubungan antara gaya vertikal dan gaya horizontal dari geseran ban di permukaan perkerasan. Keselamatan berkendara dipengaruhi oleh skid resistance permukaan jalan, meningkatnya gesekan permukaan jalan dapat diperoleh dengan ketahanan slip yang tinggi. Dalam penelitian ini, Crumb Rubber dan Asbuton Retona Blend telah digunakan sebagai aditif untuk proses daur ulang aspal agregat atau Reclaimed Asphalt Pavement RAP pada campuran aspal panas. Persentase CR yang digunakan adalah 0 hingga 1,0. Pengujian Skid resistance menggunakan British Pendulum Tester telah dilakukan menggunakan variasi suhu 25°C, 30°C, 35°C, 40°C, 45°C, 50°C, di mana rentang tersebut adalah suhu yang paling umum terjadi di Indonesia. Nilai Skid Resistance pada pengujian menggunakan British Pendulum Tester dilaporkan sebagai British Pendulum Number BPN. Crumb Rubber mengubah komposisi gradasi agregat pada campuran aspal, hal ini telah meningkatkan kinerja campuran aspal pada nilai stabilitas Marshall jika dibandingkan dengan campuran aspal tanpa Crumb Rubber. Campuran aspal beserta agregat daur ulang dengan penambahan Crumb Rubber memiliki keuntungan pada suhu tinggi sehingga campuran tersebut berfungsi lebih efektif. Hasil pengujian Skid Resistance pada campuran RAP dengan Crumb Rubber memiliki trend meningkat terhadap suhu, sehingga dapat disimpukan bahwa CR mampu meningkatkan tahanan gelincir permukaan aspal.

---

Skid resistance is a results from friction between the road surface and the vehicle tire. This is the relationship between the vertical force and the horizontal force of the tire slide at the surface of the pavement. Driving safety is influenced by skid resistance of road surface, the increasing of road surface pavement friction can be obtained by high slip resistance.

In this study, Crumb Rubber and Asbuton Retona Blend were used as additives to the aggregate from asphalt recycling process or known as Reclaimed Asphalt Pavement RAP. The percentage of crumb rubber used are 0 and 1.0 Skid resistance testing using the British Pendulum Tester had carried out in temperature variations of 25°C, 30°C, 35°C, 40°C, 45°C, 50°C, since those temperatures are the most common pavement temperature in Indonesia. Skid Resistance values using the British Pendulum Tester are reported as British Pendulum Number BPN.

Crumb Rubber has changed the aggregate gradation composition on the asphalt mixture, this has changed the asphalt performance tends to be better on Marshall rsquo s stability compared to the asphalt without CR. The mixture of asphalt and RAP with the addition of Crumb Rubber tends to have an advantage at high temperatures so that the asphalt mixture has functioned more effectively.

The result of Skid Resistance test in RAP and CR mixtures indicates that it increases as the temperature rises, hence it can be concluded that CR capable to improve the slip resistance of asphalt pavement surface. "

"Kondisi perkerasan akan mengalami perubahan seiring berjalannya waktu. Perubahan yang terjadi mengakibatkan perubahan kecepatan rata-rata lalu-lintas yang dapat dicapai. Semakin baik kondisi perkerasan maka kecepatan yang bisa dicapai juga semakin tinggi. Tingkat kecepatan kendaraan juga turut mempengaruhi perkembangan lalu-lintas. Karya tulis ini membahas tentang konsep dan pendekatan yang diambil dalam memprediksi tingkat kerataan permukaan serta pengaruh kondisi perkerasan terhadap jumlah kendaraan yang melintas ruas jalan tersebut. Sebuah program aplikasi yang didasarkan pada konsep dan pendekatan tersebut akan dibuat. Program yang dibuat membantu mensimulasi dan akan memberikan output berupa perkiraan perkembangan kondisi yang akan terjadi dari parameter-parameter yang ditinjau."