"The book is intended to be a handbook, a general reference, and a textbook. It contains the background educational materials on parametric analyses, extensive data, and previously unpublished master high-temperature curves for wrought and cast aluminum alloys.ASM International has previously published extensive numeric factual data on the high-temperature tensile and creep properties of aluminum alloys in the book Properties of Aluminum Alloys: Tensile, Creep, and Fatigue Data at High and Low Temperatures. In addition to interest in the properties themselves, there is a great amount of interest in how these properties are analyzed to provide estimates of long-time service performance. The latter analysis makes use of parametric time-temperature relationships based upon rate-process theory, enabling the user to combine all time-temperature exposure curves into one master curve useful for extrapolation as well as interpolation. The purpose of this book to explain and illustrate such analytical tools, and to provide a broad range of illustrative examples based upon data from the previous publication, plus much previously unpublished data from Alcoa Laboratories.The theory of and procedures for the development of master parametric relationships for high-temperature creep and stress rupture data for aluminum alloys are based upon rate-process theory. The advantages and limitations of several such analyses will be discussed. Previously unpublished master curves will be provided for a number of aluminum alloys, including wrought alloys 1100, 2024, 3003, 3004, 5050, 5052, 5154, 5454, 5456, 5083,and 6061, plus several castings alloys, including 224.0, 249.0, C355.0, and 357.0."

"The purpose of this research was to find other material to be alloyed to aluminum which is cheap, not a dangerous compound, which can be carted as simple as possible and should be as far as possible found in Indonesia. Tin, zinc, and indium, are metals to be alloyed which were reported gave a better performance to aluminum sacrificial anode, although the latest mentioned is difficult to be found in Indonesia. The alloying was done by simple casting. The investigation started with alloying aluminum with 5% Zn , and tin added in varying weights from of 0.004, 0.006, 0.008, 0.01, 0.04, 0.1, to 0.2 percent. The second was also 5% Zn and Indium in varying weights as from 0.004, 0.005, 0.02, 0.05, 0.07, to 0.08 percent. Anode potential, cathodic protection potential, the capacity of anode, anode output, anode efficiency, the anode corrosion patron and induction time were points being investigated to know the anode performance, gained by immersed test in 3% sodium chloride solution. The efficiency of 77 % can be obtained from 5% Zn and 0,1 % Sn aluminum alloy and for comparison, 5% Zn and 0.05% indium aluminum alloy can reach an efficiency of 86 %. The Sn, Zn aluminum alloys, have an anode potential of -1.15 volt, cathodic protection potential -1,06 volt , capacity of 2558 A.h/kg, while the Indium, Zn aluminum alloy has -1.155 volt anode potential, capacity of 2543 Ah/kg , and anode out put of 4.76 ampere. During the immersion time Al-Zn-Sn alloys give more stable cathodic protection potential."

"Karena sifatnya yang menarik seperti ketahanan aus yang tinggi, koefisien ekspansi termal yang rendah, ketahanan korosi yang baik serta kemampuan cor yang baik, paduan aluminium - silikon hipereutektik telah menjadi suatu kandidat material untuk aplikasi - aplikasi yang membutuhkan sifat mekanis yang baik seperti piston.Walaupun demikian, paduan ini memiliki kekurangan yaitu paduan akan semakin bertambah brittle seiring dengan bertambahnya kandungan silicon dikarenakan oleh adanya silikon primer yang kasar. Terdapat berbagai cara untuk meminimalkan ukuran dari fasa silikon salah satunya adalah modifikasi dengan penambahan modifier.Pada penelitian ini, material AC8A didesain pada kondisi hipereutektik. Modifier fosfor ditambahkan dengan komposisi 0,0025 wt%, 0,0027 wt %, 0,0038 wt %, 0,0046 wt % dan 0,0061 wt % P. Untuk mengetahui sifat mekanis material, dilakukan pengujian kekuatan tarik, kekerasan serta keausan. Pengujian struktur mikro, SEM dan EDAX dilakukan untuk mengetahu perubahan struktur mikro serta fasa - fasa yang terbentuk dalam paduan.Hasil penelitian menunjukkan bahwa penambahan fosfor pada material AC8A hipereutektik akan mengubah morfologi dan ukuran silikon primer dari yang berbentuk poligonal dan kasar menjadi berbentuk blocky dan halus. Silikon eutektik juga mengalami perubahan karena pertumbuhannya yang berasal dari ujung silikon primer dan dipengaruhi oleh morfologi dan ukuran silikon prime. Silikon eutektik berubah dari jarum - jarum halus yang panjang menjadi batangan pendek dan seperti titik dengan panjang rata - rata yang lebih pendek.Hasil pengujian kekerasan menunjukkan, dengan bertambahnya kadar fosfor (0,0025 wt%, 0,0027 wt %, 0,0038 wt %, 0,0046 wt % dan 0,0061 wt %), kekerasan akan meningkat dari 38 HRB menjadi 39 HRB,40 HRB, 41 HRB dan 42 HRB. Peningkatan juga terjadi pada nilai ketahanan aus material. Sedangkan nilai kekuatan tarik tidak menunjukkan kecenderungan tertentu dikarenakan terdapatnya porositas pada sampel.

---

Because of the interesting properties such as high wear resistance, low thermal expansion coefficient, high resistance to corrosion and castability, hypereutectic Al-Si alloys have become a candidate material for potential applications including piston. Nevertheless, it has a disadvantage which is it becomes more brittle as the ratio of silicon is added because of the presence of coarse primary silicon. There are a lot of ways to minimize silicon phases, one of them is modification using modifier.

In this research, aluminium alloy desaigned as AC8A was desaigned in hypereutectic condition. Phosphorus modifier was added to the melt with composition 0,0025 wt%, 0,0027 wt %, 0,0038 wt %, 0,0046 wt % dan 0,0061 wt % P. Tensile strength, hardness and wear were tested in order to know mechanical properties of material. Microstructure testing, SEM and EDAX were conducted to observe microstructure changing and phases formed in alloy.

Results of this research show that phosphorus addition in hypereutectic AC8A alloy changes the morphology and size of primary silicon from coarse polygonal to fine blocky structure. Eutectic silicon is also changed because it grows from the tip of angles on the primary silicon and is influenced by the morphology and size of primary silicon. The eutectic silicon changes from long fine needle-like shape to short bars and dots with less average length.

Hardness testing shows that by increasing phosphorus addition (0 wt %, 0,003 wt%, 0,004 wt% , 0,005 wt% dan 0,006 wt%) to the melt, hardness of the material increases from 38 HRB to 39 HRB, 40 HRB, 41 HRB, and 42 HRB. Furthermore, the value of wear resistance also increases. Nevertheless, tensile strength doesn't show any tendency because of porosity."

"Pada umumnya modifier stronsium ditambahkan pada paduan Al-Si hipoeutektik dengan kadar Si < 12 %. Penambahan modifier stronsium pada paduan Al-Si hipoeutektik terbukti efektif meningkatkan sifat-sifat mekanis paduan. Sedangkan penambahan modifier stronsium pada paduan aluminium hipereutektik belum banyak dilakukan. Penelitian ini bertujuan untuk mengetahui pengaruh penambahan modifier stronsium terhadap sifat mekanis paduan Al-Si hipereutektik (Si>12,7%). Sifat mekanis yang ingin diketahui setelah penambahan modifier stronsium adalah kekerasan, kekuatan tarik dan keausan. Dalam penelitian ini digunakan material AC8A dengan standar kadar Si sebesar 11-13%. Ditambahkan kristal silikon murni ke dalam material AC8A untuk mendapatkan kondisi hipereutektik (Si>12.7%). Perbedaan penambahan kadar stronsium dalam paduan AC8A hipereutektik merupakan variabel dalam penelitian ini, sedangkan kondisi-kondisi proses lainnya dibuat sama. Stronsium yang ditambahkan adalah sebesar 0% wt, 0.126% wt, 0.208% wt, 0.284% wt dan 0.299% wt.Hasil penelitian menunjukkan bahwa dengan penambahan modifier stronsium pada paduan AC8A hipereutektik akan mengubah bentuk silicon eutektik dari acircular menjadi fibrous dan fasa intermetalik yang terbentuk menjadi lebih tersebar. Selain itu silikon primer akan ditekan pertumbuhannya sehingga berukuran lebih kecil dan lebih tersebar merata. Hasil pengujian kekerasan dan keausan menunjukkan adanya kekerasan dan ketahanan aus yang cenderung meningkat dengan peningkatan kadar stronsium yang ditambahkan. Kekerasan cenderung meningkat secara berturut-turut dari 41 HRB menjadi 44 HRB, 45 HRB, 43 HRB dan 48 HRB. Ketahanan aus meningkat dengan laju aus yang cenderung semakin menurun secara berturut-turut dari 3.27 x 10^-5 mm3/mm menjadi 2.01 x 10^-5 mm3/mm, 1.82 x 10^-5 mm3/mm, 2.27 x 10^-5 mm3/mm, dan 1.28 x 10^-5 mm3/mm. Kekuatan tarik yang didapatkan berturut-turut dari 173 Mpa menjadi 187 Mpa, 168 Mpa, 172 Mpa dan 185 Mpa. Nilai elongasi cenderung mengalami penurunan yaitu dari 0.125 menjadi 0.123, 0.118, 0.124 dan 0.114.

---

In general, stronsium modifier is added to hypoeutectic Al-Si alloys with Si content < 12%. Addition of stronsium modifier in hypoeutectic Al-Si alloys effectivelly improve mechanical properties of alloys. Whereas, addition of stronsium modifier in hypereutectic Al-Si alloys is done rarely. This research has purpose to know effect of stronsium modifier addition on mechanical properties of hypereutectic Al-Si alloys. The mechanical properties that will be observed in this research are hardness, tensile strength and wear resistant. This research use AC8A material with 11-13% standard of Si content. Silicon crystal is added to AC8A material for obtaining hypereutectic condition (Si >12.7%). The difference of amount stronsium addition is as variable on this research. The other condition casting process, such as : strontium modifier addition temperature, cast temperature, solidification time and casting time are the same. The amount of strontium modifier which added is 0,126% wt, 0.208% wt, 0.284% wt and 0.299% wt.

The result of research show that with addition of strontium modifier to hypereutectic AC8A alloy will change eutectic silicon morphology from acircular to fibrous and intermetallic phase that be formed become more uniformly dispersed. Another, the growth of primary silicon will be suppressed until finer in size and more uniformly dispersed. The results both of hardness and wear testing show presence of disposed increasing in hardness and wear resistant with rising of Sr content that be added. The hardness disposed increase, in succession, from 41 HRB to 44 HRB, 45 HRB, 43 HRB and 48 HRB. Wear resistant disposed increase with disposed decreasing of wear rate, in succession, from 3.27 x 10-5 mm3/mm to 2.01 x 10^-5 mm3/mm, 1.82 x 10^-5 mm3/mm, 2.27 x 10^-5 mm3/mm, and 1.28 x 10^-5 mm3/mm. Tensile strength that be obtained, in succession, from 173 Mpa to 187 Mpa, 168 Mpa, 172 Mpa and 185 Mpa. The value of elongation disposed decrease from 0.125 to 0.123, 0.118, 0.124 and 0.114."

"Metode pengecoran dengan tekanan rendah (Low Pressure Die Casting) adalah proses yang digunakan untuk menghasilkan komponen logam dengan kualitas yang tinggi dan presisi yang akurat. Penelitian ini bertujuan untuk menganalisis pengaruh tekanan terhadap hasil produk pengecoran dengan metode Low Pressure Die Casting menggunakan casting simulator Z-cast. Dalam penelitian ini, dilakukan serangkaian eksperimen dengan memvariasikan tekanan yang diterapkan pada proses pengecoran yaitu; 20Kpa, 40Kpa, 60Kpa, 80Kpa, 100Kpa. Produk yang dihasilkan kemudian dievaluasi berdasarkan hasil simulasi menggunakan Z-cast. Hasil penelitian menunjukkan bahwa tekanan pengecoran memiliki pengaruh terhadap hasil produk. Peningkatan tekanan menyebabkan Flow time yang menjadi lebih singkat, velocity yang semakin meningkat, solidification time yang meningkat, dan juga keberadaan shrinkage. Temuan ini memberikan pemahaman yang lebih baik tentang pengaruh tekanan pada proses Low Pressure Die Casting dan dapat digunakan sebagai panduan dalam mengoptimalkan parameter produksi. Dengan memilih tekanan yang tepat, produsen dapat menghasilkan komponen logam dengan kualitas yang lebih baik dan efisiensi produksi yang lebih tinggi.

---

Low Pressure Die Casting is a process used to produce high-quality metal components with precise accuracy. This study aims to analyze the influence of pressure on the casting results using the Low Pressure Die Casting method with the Z-cast casting simulator. A series of experiments were conducted varying the applied pressures during casting: 20 kPa, 40 kPa, 60 kPa, 80 kPa, 100 kPa. The produced products were then evaluated based on simulation results using Z-cast. The research findings indicate that casting pressure significantly affects the product outcomes. Increasing pressure results in shorter flow times, increased velocities, prolonged solidification times, and the presence of shrinkage. These findings provide a better understanding of the pressure effects in the Low Pressure Die Casting process and can be used as a guide to optimize production parameters. By selecting the appropriate pressure, manufacturers can produce metal components with higher quality and higher production efficiency."

"Penelitian ini betujuan untuk mengetahui pengaruh temperatur cetakan dan temperatur tuang terhadap hasil pengecoran piston pada material aluminium AC8A menggunakan metode gravity die casting dengan program simulasi Z-Cast. Penelitian ini menggunakan simulasi pengecoran. Simulasi ini menggunakan software Z-Cast Pro 3.0 dan desain pada penelitian ini menggunakan software Solid Works 2021 untuk menghasilkan gambar 3D. Penelitian ini menggunakan produk piston dengan variasi variabel temperatur cetakan dan temperatur tuang. Variasi variabel temperatur cetakan yang digunakan adalah 250°C, 300°C, dan 350°C. Variabel yang digunakan untuk variasi temperatur tuang adalah 660°C, 700°C, dan 750°C. Shrinkage karena adanya proses pembekuan atau solidifikasi yang tidak merata pada produk, disebabkan oleh penyusutan volume logam cair pada proses pembekuan serta tidak mendapatkan pasokan logam cair dari riser. Pada penelitian tidak menggunakan riser dengan keadaan optimal pada temperatur cetakan 250°C dan temperatur tuang 660°C, penggunaan riser berukuran 40 mm didapatkan hasil temperature cetakan 350°C dan temperatur tuang 750°C , ukuran riser 50 mm dengan keadaan optimal pada temperatur cetakan 250°C dan temperatur tuang 660°C. Upaya untuk mengurangi cacat dengan membesarkan ukuran riser, dengan ukuran riser 50 mm akan menghasilkan produk coran denga temperatur cetakan dan temperatur tuang yang rendah. Shrinkage pada riser 50 mm lebih sedikit dibandingkan ukuran 40 mm dan tidak menggunakan riser.

---

This research aims to determine the effect of mold temperature and pouring temperature on the results of piston casting on AC8A aluminum material using the gravity die casting method with Z-Cast simulation program. This research uses casting simulation. This simulation uses Z-Cast Pro 3.0 software and the design in this research uses Solid Works 2021 software to produce 3D images. This research uses piston product using variable variations in mold temperature and pouring temperature. The variable of mold temperature variations used are 250°C, 300°C, and 350°C. The variables used to vary the pouring temperature are 660°C, 700°C, and 750°C. Shrinkage is due to the uneven solidification process in the product, due to the shrinkage of the liquid metal volume during the solidification process and not getting a supply of liquid metal from the riser. In the research without using a riser with optimal conditions at a mold temperature of 250°C and a pouring temperature of 660°C, using a 40 mm riser resulted in a mold temperature of 350°C and a pouring temperature of 750°C, a riser size of 50 mm with optimal conditions at the mold temperature 250°C and pouring temperature 660°C. Efforts to reduce defects by increasing the riser size, with a riser size of 50 mm will produce cast products with low mold temperatures and casting temperatures. Shrinkage on a 50 mm riser is less than the 40 mm size and does not use a riser."

"Penghalus butir sering diaplikasikan pada pengecoran aluminium karena mampu meningkatkan kualitas dan mengurangi reject. Salah satu metode pengecoran yang sering digunakan untuk menghasilkan produk aluminium adalah low pressure die casting (LPDC). Namun, siklus LPDC yang mencapai 4 jam dikhawatirkan dapat menyebabkan fading pada penghalus butir. Penelitian ini dimaksudkan untuk mengetahui waktu fading yang terjadi pada penghalus butir Al-5Ti-1B yang ditambahkan pada paduan AC4B hasil LPDC. Fading dapat diamati melalui perubahan kekerasan, kekuatan tarik, struktur mikro serta tingkat kegagalan bocor paduan aluminium AC4B.Pada penelitian ini ditunjukan bahwa dengan semakin lamanya waktu tahan, maka kekerasan dan kekuatan tarik akan menurun, sedangkan keuletan dan lebar secondary dendrite arm spacing (SDAS) pada foto mikro akan meningkat. Penelitian ini juga menunjukan bahwa fading sudah terjadi antara jam ke 0 dan jam ke 1. Selain itu, pengamatan struktur mikro paduan AC4B dengan menggunakan Scanning Electron Microscopy (SEM) dan Energy Dispersive X-RaY Analysis (EDAX) menunjukan keberadaan titanium pada paduan sebagai indikasi dari adanya partikel penghalus butir.

---

Grain refiner is usually applied for aluminum casting to improve quality and reduce rejection. One of casting methods that commonly used to produce aluminum is low pressure die casting (LPDC). One cycle of production of LPDC with ~450 kg capacity may take up 4 hours. Therefore, using grain refiner in LPDC process might cause fading. Aim of this research is to understand the fading time of Al-5Ti-1B grain refiner during LPDC. Fading was observed through the changes of hardness, tensile strength and microstructure. Percentage of leakage in the trial of AC4B cylinder head production was also evaluated.

The results show that the longer the holding time, the lower hardness and the tensile strength of AC4B alloy. On the other hand, the longer the holding time, the higher the ductility & secondary dendrite arm spacing (SDAS). This indicates that fading had occurred before 1 hour. In addition; microstructure observation by using Scanning Electron Microscopy (SEM) and Energy Dispersive X-Ray Analysis (EDAX) shows the presence of titanium in the alloy which indicates that titanium may act as the nucleant for solidification process."

"A collective effort of 53 recognized experts on aluminum and aluminum alloys. This book is a joint venture by world-renowned authorities and the Aluminum Association Inc. and ASM International."