Analisis Sruktur dan Sifat Magnetik Manganit Perovskite Nd1-xSrxMnO3 (x = 0; 0,2; 0,4; 0,6; 0,8; 1) dengan Metode Sol-Gel = Structural Analysis and Magnetic Properties of Perovskite Manganite Nd1-xSrxMnO3 (x = 0; 0,2; 0,4; 0,6; 0,8; 1) Using the Sol-Gel Method

Febie Permata Sari; Djati Handoko, supervisor; Azwar Manaf, examiner; Budhy Kurniawan, examiner (Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2021)

 Abstrak

Telah dilakukan penelitian mengenai struktur kristal, morfologi dan sifat magnetic bahan Nd1-xSrxMnO3 (x = 0, 0.2, 0.4, 0.6, 0.8, 1) dengan metode sol-gel. Divariasikan substitusi Sr terhadap senyawa NdMnO3. Efek dari substitusi Sr terhadap NdMnO3 didapatkan dari perbedaan struktur kristal, morfologi, dan sifa magnetic setiap variasi komposisi Sr. Dengan karakterisasi struktur kristal menggunakan X-Ray Diffractometer (XRD) dan karakterisasi morfologi menggunakan Scanning Electron Microscope (SEM) serta karakterisasi sifat magnetik menggunakan Vibrating Sample Magnetometer (VSM). Hasil XRD menunjukkan bahwa komposisi Sr di NdMnO3 tidak mengubah struktur kristal dari perovskite tersebut, tetapi parameter kisi dari struktur kristal berubah tiap komposisi Sr nya. Bentuk dan ukuran grain partikel juga sangat berbeda tiap komposisi Sr nya, hal ini menunjukkan bahwa komposisi Sr di NdMnO3 memang dapat mengubah strukur kristal, morfologi, dan sifat magnetik manganit perovskite NdMnO3.

Research on the crystal structure, morphology and magnetic properties of Nd1- xSrxMnO3 (x = 0, 0.2, 0.4, 0.6, 0.8, 1) was carried out using the sol-gel method. The Sr substitution of NdMnO3 was varied. The effect of Sr substitution on NdMnO3 was obtained from differences in crystal structure, morphology, and magnetic properties for each variation in the composition of Sr. With characterization of crystal structure using X-Ray Diffractometer (XRD) and morphological characterization using Scanning Electron Microscope (SEM) and characterization of magnetic properties using a Vibrating Sample Magnetometer (VSM). XRD results showed that the Sr composition in NdMnO3 change the crystal structure of the perovskite and the lattice parameters of the crystal structure changed with each Sr. composition. The shape and grain size of the particles are also very different for each Sr. composition, this shows that the Sr composition in NdMnO3 can indeed change the crystal structure, morphology, and magnetic properties of the NdMnO3 perovskite manganite.

 

 File Digital: 1

Shelf
 S-Febie Permata Sari.pdf :: Unduh

LOGIN required

 Kata Kunci

 Metadata

Jenis Koleksi : UI - Skripsi Membership
No. Panggil : S-pdf
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Entri tambahan-Nama badan :
Program Studi :
Subjek :
Penerbitan : Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2021
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : computer
Tipe Carrier : online resource
Deskripsi Fisik : xi, 41 pages ; illustration ; 28 cm + appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
S-pdf 14-24-36085530 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 9999920541694
Cover
 Lihat juga